`(original) A method for brazing an article comprising of:
`
`(1) providing an article formed from a ferrous material;
`
`(2),
`
`applying a brazing material to said article formed from an alloy
`
`consisting essentially of from about 52.25 wt% to about 57.0 wt%
`
`silver,
`from about 38.95 wt% to about 43.0 wt% copper,
`from
`about 0.5 wt% to about 5.5 wt% manganese, and up to about 2.5
`
`wt% nickel; and (3) heating said article and said brazing
`
`material at a temperature in the range of from about 900°C to
`
`about 1050°C for a time sufficient to melt said brazing material.
`
`8.
`
`(original) The method of claim 7, wherein said heating step
`
`comprises heating said article and said brazing material at a
`
`temperature in the range of from about 950°C to about 1050°C.
`
`9.
`
`(original) The method of claim 7, wherein said brazing
`
`material applying step comprises applying a brazing material
`
`consisting essentially of 56 wt% silver, 42 wt% copper, and 2.0
`
`wt% manganese.
`
`10.
`
`(original) The method of claim 7, wherein said brazing
`
`material applying step comprises applying a brazing material
`
`consisting essentially of 0.5 to 5.5 wt% manganese with the
`
`Page 3 of 5
`
`
`
`
`
`Prel. Amdt. dated July 19, 2005
`
`Attorney Docket No.: EH—lO4SZB(00-749-3)
`
`remaining composition proportional to the 56 wt% silver, 42 wt%
`
`copper, and 2.0 wt% nickel alloy.
`
`11.
`
`(original) The method according to claim 7, wherein said
`
`brazing material being applied has a nickel content in the range
`
`of from about 1.5 wt% to about 2.5 wt%.
`
`12.
`
`(original) The method according to claim 7, wherein said
`
`brazing material being applied has a manganese content in the
`
`range of from about 1.0 wt% to about 5.5 wt%.
`
`13.
`
`(original) The method according to claim 7, wherein said
`
`article providing step comprises providing an article formed
`
`from steel.
`
`14.
`
`(original) The method according to claim 7, wherein said
`
`article providing step comprises providing an article formed
`
`from stainless steel.
`
`Page 4 of 5
`
`
Accessing this document will incur an additional charge of $.
After purchase, you can access this document again without charge.
Accept $ Charge
This document could not be displayed.
We could not find this document within its docket. Please go back to the docket page and check the link. If that does not work, go back to the docket and refresh it to pull the newest information.
Your account does not support viewing this document.
You need a Paid Account to view this document. Click here to change your account type.
Your account does not support viewing this document.
Set your membership
status to view this document.
With a Docket Alarm membership, you'll
get a whole lot more, including:
- Up-to-date information for this case.
- Email alerts whenever there is an update.
- Full text search for other cases.
- Get email alerts whenever a new case matches your search.
One Moment Please
The filing “” is large (MB) and is being downloaded.
Please refresh this page in a few minutes to see if the filing has been downloaded. The filing will also be emailed to you when the download completes.
Your document is on its way!
If you do not receive the document in five minutes, contact support at support@docketalarm.com.
Sealed Document
We are unable to display this document, it may be under a court ordered seal.
If you have proper credentials to access the file, you may proceed directly to the court's system using your government issued username and password.
Access Government Site