`Samsung Electronics Co., Ltd. v. Demaray LLC
`Samsung Electronic's Exhibit 1056
`Exhibit 1056, Page 1
`
`
`
`U.S. Patent
`
`
`
`Jun. 25, 2002
`
`
`
`
`Sheet 1 of 5
`
`
`
`US 6,409,965 B1
`
`
`
`Fig.
`
`
`
`
`
`1 =e
`
`
`
`RATIO 97% |
`
`
`eepessgpar||
`
`
`po)ASSPP ~
`
`
`
`
`
`DEPOSITIONRATE(A/s)
`
`
`
`oRKEcoes¢| DENY
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`LIFETIME OF TARGET (kWh)
`
`
`
`Ex. 1056, Page 2
`
`Ex. 1056, Page 2
`
`
`
`
`
`— am)
`
`oo
`
`
`
`MAGNETICPERMEABILITY
`
`
`
`0 «40~©6020 80-100
`
` f OFRATEEARTHALLOYPOWDER
`
`U.S. Patent
`
`
`
`
`Jun. 25, 2002
`
`
`
`
`
`Sheet 2 of 5
`
`
`US 6,409,965 B1
`
`
`
`Fig. 2
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`CONTENT OF RATE EARTH METALS
`IN RATE EARTH ALLOY POWDER (IN WEIGHT ‘b)
`
`
`
`
`
`
`
`
`Ex. 1056, Page 3
`
`Ex. 1056, Page 3
`
`
`
`U.S. Patent
`
`
`
`
`Jun. 25, 2002
`
`
`
`
`
`Sheet 3 of 5
`
`
`US 6,409,965 B1
`
`
`
` S
`=
`
`
`
`
`
`-
`
`2
`
`
`=
`a
`
`=<
`
`
`Oo
`
`2
`
`
`a
`Es
`
`
`Li
`
`
`
`=
`
`
`
`
`a2
`
`
`
`
`
`2
`©
`=
`w
`z
`
`
`
`
`
`
`vONTENT OF RATE EARTH ALLOY POWDER
`
`
`
`
`
`
`
`
`
`
`IN ALLOY POWDER (IN WEIGHT %)
`
`
`
`
`=
`
`a=
`
`
`=
`a-
`
`2
`iS
`
`g
`
`
`=
`
`p=
`
`a
`a
`2
`
`
`
`©
`
`ic
`
`
`—
`©
`
`
`=
`
`
`
`
`
`
`
`
`CONTENT OF RATE EARTH ALLOY POWDER
`
`
`
`
`HAVING THE MAGNETIC PERMEABILITY
`
`
`
`
`
`
`OF 1.5 IN ALLOY POWDER (IN WEIGHT ‘%)
`
`
`
`Ex. 1056, Page 4
`
`Ex. 1056, Page 4
`
`
`
`U.S. Patent
`
`
`
`
`Jun. 25, 2002
`
`
`
`
`
`Sheet 4 of 5
`
`
`US 6,409,965 B1
`
`
`
`
`
`
`
`Ex. 1056, Page 5
`
`Ex. 1056, Page 5
`
`
`
`U.S. Patent
`
`
`
`
`Jun. 25, 2002
`
`
`
`
`
`Sheet 5 of 5
`
`
`US 6,409,965 B1
`
`
`
`
`
`
`
`
`
`Fig. 6A
`
`
`
`
`
`
`
`
`
`
`
`
`
`Fig. 6D
`
`WA"
`
`Ex. 1056, Page 6
`
`Ex. 1056, Page 6
`
`
`
`
`
`US 6,409,965 B1
`
`
`
`10
`
`15
`
`20
`
`25
`
`30
`
`35
`
`40
`
`
`
`
`
`55
`
`60
`
`65
`
`
`1
`SPUTTERING TARGET AND ITS
`
`
`
`MANUFACTURING METHOD
`
`
`BACKGROUND OF THE INVENTION
`
`
`1. Field of the Invention
`
`
`
`
`
`
`
`
`
`
`
`This invention relates to a sputtering target and its manu-
`
`
`
`
`
`
`
`
`facturing method especially suitable for application to an
`
`
`
`
`
`
`alloy target used for sputtering in a manufacturing process of
`
`
`
`
`a magneto-optical recording medium.
`
`
`
`
`
`2. Description of the Related Art
`
`
`
`
`
`
`
`
`
`For years, price strategies have been importantin thefield
`
`
`
`
`
`
`
`of AV recording mediumssuch as mini discs (MDs) intended
`
`
`
`
`
`
`
`
`
`for general customers, and reduction of prices has been
`
`
`
`
`
`
`
`
`demanded continuously. To meet
`the demand for price
`
`
`
`
`
`reduction of mediums, reduction of manufacturing costs of
`
`
`
`
`
`
`
`
`mediums has been required. Regarding cost reduction of
`
`
`
`
`
`
`
`mediums,thicknessof targets used for fabrication of record-
`
`
`
`
`
`ing materials of mediumsis an important factor.
`
`
`
`
`
`
`is,
`That
`for manufacturing a medium, magnetron
`
`
`
`
`
`
`
`sputtering, among others, is used for stacking its recording
`
`
`
`
`
`
`
`material. For deposition of the recording medium by mag-
`
`
`
`
`
`
`
`netron sputtering, a target containing the recording material
`
`
`
`
`
`
`
`
`is used. Such a target includes as its major componenta rare
`
`
`
`
`
`
`
`earth element which is a rare element and expensive.
`
`
`
`
`
`
`
`
`Conventionally, however, only 30% to 50% of the target was
`
`
`
`
`
`
`
`
`sputtered and contributed to deposition of the film, and the
`
`
`
`
`
`
`
`remainder of the target was abandoned. Therefore,
`it has
`
`
`
`
`
`
`
`
`been demanded to increase the ratio of a target actually
`
`
`
`
`
`
`sputtered and contributing deposition of a film by increasing
`
`
`
`
`the thickness of the target.
`
`
`
`
`
`
`However, targets conventionally used for manufacturing
`
`
`
`
`
`
`mediums had magnetic permeability around 5. Therefore,
`
`
`
`
`
`
`
`the maximum thickness of a target enabling stable discharge
`
`
`
`
`
`
`
`of plasma and sputtering was about 8 mm.
`
`
`
`
`
`
`Under the circumstances, various researches and devel-
`
`
`
`
`
`
`
`opments have been made toward fabrication of targets
`
`
`
`
`
`having a thickness of 8 mm or more, and various proposals
`
`
`were presented.
`
`
`
`
`
`
`
`
`For example, there was proposes a technique for manu-
`
`
`
`
`
`
`
`facturing a target made by hot-pressing alloy powder
`
`
`
`
`
`
`
`obtained by mechanical crushing and having a magnetic
`
`
`
`
`
`
`permeability not exceeding 3 (Japanese Patent Laid-Open
`
`
`
`
`
`
`Publication No. hei-10-251847 (Literature 1)). Literature 1
`
`
`
`
`
`teaches a method for manufacturing a magneto-optical
`
`
`
`
`
`
`
`recording alloy target made by hot-pressing alloy powder
`
`
`
`
`
`
`
`made by mechanical crushing and having a magnetic per-
`
`
`
`
`
`
`meability not exceeding 3, and a method for manufacturing
`
`
`
`
`
`
`
`a magneto-optical recording alloy target made by mechani-
`
`
`
`
`
`
`
`
`
`cally crushing used targets into alloy powder and mixingit
`
`
`
`
`
`
`
`
`with new alloy powder and having a magnetic permeability
`
`
`not exceeding 3.
`
`
`
`
`
`
`
`Literature 1 also teaches that a target having a low
`
`
`
`
`
`
`magnetic permeability, low containment of oxygen, single-
`
`
`
`
`
`
`
`
`sintered structure of a rare earth metal and a transition metal,
`
`
`
`
`
`
`
`
`
`and a thickness not
`less than 8 mm can be made by
`
`
`
`
`
`
`
`
`dissolving a source material and used targets, then making a
`
`
`
`
`
`
`
`
`quickly cooled alloy, and mechanically crushing the quickly
`
`
`
`
`
`cooled alloy into alloy powder.
`
`
`
`
`
`
`However,
`the Inventor conducted various experiments
`
`
`
`
`
`
`
`
`concerning alloy powder as taught by Literature 1, and
`
`
`
`
`
`
`
`
`found that the alloy powder described in Literature con-
`
`
`
`
`
`
`
`tained an unacceptably large amount of metal impurities for
`
`
`practical use.
`
`
`
`
`
`
`
`
`For example, there was proposed a technique for manu-
`
`
`
`
`
`
`
`facturing a target made by hot-pressing alloy powder
`
`
`2
`
`
`
`
`
`
`obtained by mechanical crushing and having a magnetic
`
`
`
`
`
`
`permeability not exceeding 3 (Japanese Patent Laid-Open
`
`
`
`
`
`
`Publication No. hei-10-251847 (Literature 1)). Literature 1
`
`
`
`
`
`teaches a method for manufacturing a magneto-optical
`
`
`
`
`
`
`
`recording alloy target made by hot-pressing alloy powder
`
`
`
`
`
`
`
`made by mechanical crushing and having a magnetic per-
`
`
`
`
`
`
`
`meability not exceeding 3, and a method for manufacturing
`
`
`
`
`
`
`
`a magneto-optical recording alloy target made by mechani-
`
`
`
`
`
`
`
`
`
`cally crushing used targets into alloy powder and mixingit
`
`
`
`
`
`
`
`
`with new alloy powder and having a magnetic permeability
`
`
`not exceeding 3.
`
`
`
`
`
`
`
`The magneto-optical recording alloy target having a mag-
`
`
`
`
`
`
`
`netic permeability not larger than 3, which is disclosed in
`
`
`
`
`
`
`
`
`Literature 1, also involves the problem that a sufficient leak
`
`
`
`
`
`
`
`magnetic flux cannot be obtained in any magnetron sputter-
`
`
`
`
`
`
`
`ing apparatus, and sputtering of this target is impossible.
`
`
`
`
`
`
`
`
`That is, although the Inventor made a target having the
`
`
`
`
`
`
`
`magnetic permeability of 2.1 and the thickness of 10 mm
`
`
`
`
`
`
`
`
`
`from alloy powder as taught by Literature 1, and tried
`
`
`
`
`
`
`
`
`
`sputtering by setting this target in place of a sputtering
`
`
`
`
`
`
`apparatus, it could not sputter this target.
`
`
`
`
`
`
`teach a
`Furthermore, although Literature 1 does not
`
`
`
`
`
`
`magneto-optical recording alloy target having a magnetic
`
`
`
`
`
`
`
`
`permeability not larger than 2.3, according to the Inventor’s
`
`
`
`
`
`
`knowledge, a 10 mm thick target having a magnetic perme-
`
`
`
`
`
`
`
`
`
`ability around 2.3 as taught by Literature 1 cannot be
`
`sputtered.
`OBJECTS AND SUMMARY OF THE
`
`
`
`INVENTION
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`It is therefore an object of the invention to provide a
`
`
`
`
`
`
`
`sputtering target and its manufacturing method enabling
`
`
`
`
`
`
`
`
`effective use of expensive rare earth metals, not adversely
`
`
`
`
`
`
`affecting the environment, contributing to reduction of the
`
`
`
`
`
`
`
`manufacturing cost, and ensuring a target with a magnetic
`
`
`
`
`
`permeability low enough for sputtering.
`The Inventor made researches toward solution of the
`
`
`
`
`
`
`
`
`
`
`
`
`above-indicated problems involved in the conventional tech-
`
`
`
`
`
`niques. A summary thereof is shown below.
`
`
`
`
`
`According to the Inventor’s knowledge, in orderto effec-
`
`
`
`
`
`
`
`
`tive use an expensiverare earth metal for fabricating a target
`
`
`
`
`
`
`
`
`
`whose thickness is not less than 10 mm,it is desirable to
`
`
`
`
`
`
`
`produce recycled alloy powder by using used targets, and
`
`
`
`
`
`
`
`
`fabricate new targets by using the recycled alloy powder. So,
`
`
`
`
`
`
`the Inventor conducted various experiments regarding rare
`
`
`
`
`
`
`
`earth alloy power containing recycled alloy powder.
`
`
`
`
`
`
`
`
`The Inventor first made reviews about theoretic density
`
`
`
`
`
`
`
`ratios of targets fabricated. According to the Inventor’s
`
`
`
`
`
`
`
`
`knowledge, rare earth alloy powderis very readily oxidized,
`
`
`
`
`
`
`
`
`and if a target substantially made of rare earth alloy powder
`
`
`
`
`
`
`
`
`has a low theoretic density ratio, oxidationofthetargetitself
`
`
`
`
`
`
`
`
`progresses. Therefore, any medium made by usingthistarget
`
`
`
`
`
`
`
`cannot have a satisfactory property. Relation between depo-
`
`
`
`
`
`
`
`
`
`sition rate in a sputtering process and target
`lifetime is
`
`
`
`
`
`
`
`
`
`shown in FIG. 1,
`taking two different cases where the
`
`
`
`
`
`
`
`
`theoretic density ratio of the target is 95% and 97%, respec-
`
`tively.
`
`
`
`
`
`
`
`
`It is apparent from FIG. 1 that, when the theoretic density
`
`
`
`
`
`
`
`
`
`
`ratio is high, ie. 97%, fluctuation in deposition rate of
`
`
`
`
`
`
`
`sputtering is small. In other words,if thickness of the target
`
`
`
`
`
`
`
`
`
`is constant, the target lifetime is longer, and the manufac-
`
`
`
`
`
`
`
`turing cost of mediums can be reduced whenthe theoretic
`
`
`
`density ratio is high.
`
`
`
`
`
`
`Therefore, it is preferable for a target to have a theoretic
`
`
`
`
`
`
`
`
`
`density ratio not lower than 95%, and more preferably not
`
`
`
`
`Ex. 1056, Page 7
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`Ex. 1056, Page 7
`
`
`
`
`
`US 6,409,965 B1
`
`
`3
`
`
`
`
`
`
`
`lower than 97%. Discussion is continued below, selecting
`
`
`
`
`
`
`
`
`
`
`the case of the theoretic density ratio not lower than 97%.
`
`
`
`
`
`
`
`For the purpose of determining composition of rare earth
`
`
`
`
`
`
`
`alloy powder, the Inventor conducted an experiment about
`
`
`
`
`
`
`
`dependency of magnetic permeability of rare earth alloy
`
`
`
`
`
`
`
`
`powder upon quantity of rare earth metals contained in rare
`
`
`
`
`
`
`
`
`earth alloy powder. A result of the experiment is shown in
`FIG. 2.
`
`
`
`
`
`
`
`
`
`It apparent from FIG. 2 that magnetic permeability of rare
`
`
`
`
`
`
`
`earth alloy powderis 5 or higher whenit contains about 20
`
`
`
`
`
`
`
`weight % of rare earth metals, but decreases to 2 or lower
`
`
`
`
`
`
`whenthe content of earth metals therein is 35 weight % or
`
`
`
`
`
`
`higher. Therefore, in order to maintain a magnetic perme-
`
`
`
`
`
`
`
`
`
`the
`ability not higher than 2 in rare earth alloy powder,
`
`
`
`
`
`
`
`
`
`content of rare earth metal in the rare earth alloy powderis
`
`
`
`
`
`
`
`
`preferably not lower than 35 weight %, and more preferably
`
`
`
`
`
`not lower than 40 weight %.
`
`
`
`
`
`
`
`The Inventor also conducted an experiment about mag-
`
`
`
`
`
`
`
`
`20
`netic permeability and theoretic density ratio of targets upon
`
`
`
`
`
`
`
`
`rare earth alloy powder contained in alloy powder, using
`
`
`
`
`
`
`
`
`targets prepared by using rare earth alloy powder. A result of
`
`
`
`
`
`
`
`the experiment is shown in FIG. 3. In FIG. 3, values of
`
`
`
`
`
`
`
`magnetic permeability of targets are plotted with I whereas
`
`
`
`
`
`
`
`values of theoretic density ratio are plotted with o.
`
`
`
`
`
`
`
`
`It is apparent from FIG. 3 that permeability of targets is
`
`
`
`
`
`
`
`
`larger than 2 when the content of rare earth alloy powder in
`
`
`
`
`
`
`
`
`alloy powderis less than 65 weight %, and becomes2 or less
`
`
`
`
`
`
`
`
`
`
`when the content of the rare earth alloy powder in alloy
`
`
`
`
`
`
`
`
`powderis not less than 65 weight %, or preferably not less
`
`
`
`
`
`
`
`than 70 weight %, taking errors into account.
`
`
`
`
`
`
`
`
`Thus, content of rare earth alloy powderin alloy powder
`
`
`
`
`
`
`
`
`
`as the source material of a target should be not less than 65
`
`
`
`
`
`
`
`
`weight %, and more preferably not less than 70 weight %.
`35
`
`
`
`
`
`
`
`The Inventor also conducted an experiment about mag-
`
`
`
`
`
`
`
`
`netic permeability and theoretic density ratio of targets. FIG.
`
`
`
`
`
`
`
`4 shows dependency of magnetic permeability and theoretic
`
`
`
`
`
`
`
`
`
`
`density ratio of targets upon content of rare earth alloy
`
`
`
`
`
`
`
`powderin alloy powder, when magnetic permeability of the
`
`
`
`
`
`
`
`
`rare earth alloy powder is controlled not to exceed 2 (more
`
`
`
`
`
`
`
`
`specifically around 1.5).
`In FIG. 4, values of magnetic
`
`
`
`
`
`
`
`permeability of targets are plotted with II whereas values of
`
`
`
`
`
`
`theoretic density ratio are plotted with o.
`
`
`
`
`
`
`
`
`It is apparent from FIG. 4 that magnetic permeability of
`
`
`
`
`
`
`
`
`targets becomes larger than 2 when amount of rare earth
`
`
`
`
`
`
`
`
`alloy powder, having a magnetic permeability not larger than
`
`
`
`
`
`
`
`
`2, contained in alloy powder used as the source material of
`
`
`
`
`
`
`
`
`targets is less than 50 weight %, and becomes2 or less when
`
`
`
`50 weight % or more.
`
`
`
`
`
`
`
`
`Therefore, content of rare earth alloy powder having a
`
`
`
`
`
`
`
`magnetic permeability not higher than 2 in alloy powder
`
`
`
`
`
`
`
`used as the source material of targets is preferably controlled
`
`
`
`
`
`not to be lower than 50 weight %.
`
`
`
`
`
`
`
`Through those various experiments and researches, the
`
`
`
`
`
`
`
`
`Inventor has come to know that, in order to control magnetic
`
`
`
`
`
`
`
`permeability of a target not to exceed 2 while using recycled
`
`
`
`
`
`
`
`
`alloy powder, it is necessary to control the content of rare
`
`
`
`
`
`
`
`
`earth alloy powder including recycled alloy powder con-
`
`
`
`
`
`
`
`
`tained in alloy powder used as the source material of the
`
`
`
`
`target not to exceed 65 weight %.
`
`
`
`
`
`
`
`The invention has been made through those researches
`
`
`
`and accompanying experiments.
`
`
`
`
`
`
`
`
`According to the first aspect of the invention, there is
`
`
`
`
`
`
`provided a sputtering target made of alloy powder which
`
`
`
`
`
`
`
`contains at least 65 weight percentof at least one kind ofrare
`
`
`
`
`
`
`
`
`earth alloy powder made of at least one kind of rare earth
`
`10
`
`15
`
`25
`
`30
`
`40
`
`45
`
`50
`
`55
`
`60
`
`65
`
`
`
`
`
`
`
`
`
`4
`elementandat least two kinds of elements selected from the
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`group consisting of Fe, Co, Ni, Cr and Si, and contains at
`
`
`
`
`
`
`
`
`least one kind of recycled alloy powder prepared by using a
`
`
`
`
`
`
`target used at least once for sputtering.
`
`
`
`
`
`
`In the first aspect of the invention, magnetic permeability
`
`
`
`
`
`
`
`
`of the target is typically a value not larger than 2.
`
`
`
`
`
`
`
`
`In the first aspect of the invention, thickness of the target
`
`
`
`
`
`
`ensuring a sufficient
`leak magnetic flux intensity and
`
`
`
`
`
`
`enabling sputtering is typically not less than 8 mm and not
`
`
`
`
`
`
`
`more than 20 mm,or preferably not less than 10 mm and not
`more than 15 mm.
`
`
`
`
`
`
`
`
`
`
`
`According to the second aspect of the invention, there is
`
`
`
`
`
`provided a manufacturing method of a sputtering target
`
`
`
`
`
`
`
`which manufactures a target from alloy powder which
`
`
`
`
`
`
`
`
`containsat least 65 weight percentof at least one kind ofrare
`
`
`
`
`
`
`
`
`
`earth alloy powder made of at least one kind of rare earth
`elementandat least two kinds of elements selected from the
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`group consisting of Fe, Co, Ni, Cr and Si, and contains at
`
`
`
`
`
`
`
`
`least one kind of recycled alloy powder prepared by using a
`
`
`
`
`
`
`target used at least once for sputtering.
`
`
`
`
`
`
`
`
`
`In the second aspect of the invention, for the purpose of
`
`
`
`
`
`
`
`ensuring a practical level of the content of metal impurities
`
`
`
`
`
`
`
`
`
`
`in the alloy powder used for makingthe target, the recycled
`
`
`
`
`
`alloy powder is prepared by powdering by an atomizing
`
`
`
`
`
`
`
`
`method an ingot prepared by a target used at least once for
`
`
`
`
`
`
`
`
`
`sputtering and a material not used before for makinga target.
`
`
`
`
`
`
`From the standpoint of making fine powder minimized in
`
`
`
`
`
`
`composition segregation, typically used as the atomizing
`
`
`
`
`
`
`method is a gas atomizing method. However, a single-roll
`
`
`
`
`
`
`method or a centrifugal disc method is also usable.
`
`
`
`
`
`
`
`In the present
`invention, recycled alloy powder is a
`
`
`
`
`
`
`substance obtained by powdering an ingot prepared from a
`
`
`
`
`
`
`
`
`
`target used at least once for sputtering, and a new material
`
`
`
`
`
`
`
`
`
`not used before for makinga target. In the present invention,
`
`
`
`
`
`
`
`
`recycled alloy powder typically contains rare earth alloy
`
`
`
`
`
`
`
`
`
`powder prepared from a target used at least once for sput-
`
`
`
`
`
`tering by 30 weight % or more, or preferably by 50 weight
`% or more.
`
`
`
`
`
`
`
`
`
`
`
`In the present invention, a rare earth elementis the generic
`
`
`
`
`
`
`
`name of lanthanoids, Sc (scandium) and Y (yttrium) to
`
`
`
`
`
`
`
`lanthanoids. More specifically, it is the general name of La
`
`
`
`
`
`
`(lanthanum, Ce (cerium), Pr
`(praseodymium), Nd
`
`
`
`
`
`
`(neodymium), Pm (promethium), Sm (samarium), Eu
`
`
`
`
`
`
`(europium), Gd (gadolinium), Tb (terbium), Dy
`
`
`
`
`(dysprosium), Ho (holmium), Er (erbium), Tm (thulium), Yb
`
`
`
`(ytterbium), Lu (lutetium), Y and Sc.
`
`
`
`
`
`
`
`
`In the present invention, alloy powder typically contains
`
`
`
`
`
`
`
`
`50 weight % or more of rare earth alloy powder having a
`
`
`
`
`
`
`
`magnetic permeability not larger than 2. In order to control
`
`
`
`
`
`
`
`the magnetic permeability of the rare earth alloy powder not
`
`
`
`
`
`
`
`
`
`
`to exceed 2, content of rare earth metal in the rare earth alloy
`
`
`
`
`
`
`
`
`
`powderis typically not less than 30 weight %, and prefer-
`
`
`
`
`
`ably not less than 35 weight %.
`
`
`
`
`
`
`
`In the present invention, in order to makea target having
`
`
`
`
`
`
`
`a magnetic permeability not larger than 2, magnetic perme-
`
`
`
`
`
`
`ability of alloy powderis controlled not to exceed 2.
`
`
`
`
`
`
`
`
`In the present invention, content of metal impurities in the
`
`
`
`
`
`
`
`
`
`
`target is typically not more than 0.1 weight %, and content
`
`
`
`
`
`
`
`
`
`
`of metal impurities in the alloy powderis not more than 0.1
`
`weight %.
`
`
`
`
`
`
`
`
`In the present invention, theoretic density ratio of the
`
`
`
`
`
`
`
`
`
`target is typically not less than 97%, and preferably not less
`than 98%.
`
`
`
`
`
`
`
`
`
`In the present invention, the sputtering apparatus using
`
`
`
`
`
`
`the target is typically a magnetron sputtering apparatus.
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`Ex. 1056, Page 8
`
`Ex. 1056, Page 8
`
`
`
`
`
`US 6,409,965 B1
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`Explained below are embodiments of the invention with
`
`
`
`
`
`
`
`
`reference to the drawings. In all figures illustrating the
`
`
`
`
`
`
`embodiments, the same or equivalent parts or elements are
`labeled with common reference numerals.
`
`
`
`
`
`
`
`
`
`First explained is a manufacturing method of a sputtering
`
`
`
`
`
`
`
`target according to the first embodiment of the invention.
`
`
`
`
`
`
`In the sputtering target manufacturing method according
`
`
`
`
`
`
`to the first embodiment, a target of a quaternary FeTbCoCr
`
`
`
`
`
`
`
`
`
`
`
`5
`
`
`
`
`
`
`
`However, the target can be made in any other sputtering
`
`
`
`
`apparatus, such as opposed-electrodes sputtering apparatus,
`
`
`
`
`
`electron cyclotron resonance (ECR) sputtering apparatus,
`
`
`
`
`high-frequency sputtering apparatus,
`reactive sputtering
`
`
`
`
`
`apparatus, bias sputtering apparatus, collimate sputtering
`
`
`
`
`
`apparatus or long-distance (LD) sputtering apparatus.
`
`
`
`
`
`
`
`
`In the present invention, the sputtering targetis preferably
`
`
`
`
`
`
`
`
`made of alloy powder which contains at least one kind of
`
`
`
`
`
`
`
`
`rare earth alloy powderselected from the group consisting of
`
`
`
`
`
`
`
`FeTbCo, FeTbCr, FeTbCoCr, FeGdCo, FeDyCo and FeGd-
`
`
`
`
`
`
`
`CoSi by 65 weight % or more, and containing at least one
`
`
`
`
`
`
`
`kind of recycled alloy powder prepared by using a target
`
`
`
`
`
`
`
`
`
`which is madeof at least one kind of rare earth alloy selected
`
`
`
`
`
`
`
`from the group consisting of FeTbCo, FeTbCr, FeTbCoCr,
`
`
`
`
`
`
`
`
`FeGdCo, FeDyCo and FeGdCoSi used at least once for
`
`sputtering.
`
`
`
`
`
`
`According to the sputtering target and its manufacturing
`
`
`
`
`
`
`
`method having the above summarized structures according
`
`
`
`
`
`
`
`
`
`to the invention, since the sputtering target is madeof alloy
`
`
`
`
`
`
`
`
`
`powder which contains at least one kind of rare earth alloy
`
`
`
`
`
`
`
`
`
`powder madeofat least one kind of rare earth element and
`
`
`
`
`
`
`
`
`
`
`least
`two kinds of elements selected from the group
`at
`
`
`
`
`
`
`
`
`
`consisting of Fe, Co, Ni, Cr and Si, and containsat least one
`
`
`
`
`
`
`
`
`kind of recycled alloy powder prepared from a target used at
`
`
`
`
`
`
`
`
`
`least once for sputtering, the sputtering target can be lowered
`
`
`
`
`
`
`in magnetic permeability, and increased in thickness.
`
`
`
`
`
`
`
`
`The above, and other, objects, features and advantage of
`
`
`
`
`
`
`
`
`
`the present invention will becomereadily apparent from the
`
`
`
`
`
`
`following detailed description thereof which is to be read in
`
`
`
`
`
`connection with the accompanying drawings.
`BRIEF DESCRIPTION OF THE DRAWINGS
`
`
`
`
`
`
`
`
`
`FIG. 1 is a graph showingrelation between deposition rate
`
`
`
`
`
`
`and target lifetime in a sputtering process according to the
`
`invention;
`
`
`
`
`
`
`FIG. 2 is a graph showing dependency of magnetic
`
`
`
`
`
`
`
`
`permeability of rare earth alloy powder used for manufac-
`
`
`
`
`
`
`
`turing a target upon content of rare earth metals;
`
`
`
`
`
`
`FIG. 3 is a graph showing dependency of magnetic
`
`
`
`
`
`
`
`permeability and theoretic density ratio of a target according
`
`
`
`
`
`
`
`
`
`to the invention upon content of rare earth alloy powder in
`
`
`alloy powder;
`
`
`
`
`
`FIG. 4 is a graph showing dependency of magnetic
`
`
`
`
`
`
`permeability and theoretic density ratio of a target according
`
`
`
`
`
`
`
`
`to the invention upon content of rare earth alloy powder
`
`
`
`
`
`
`having a magnetic permeability not larger than 2 in alloy
`
`powder;
`
`
`
`
`
`FIG. 5 is a diagram roughly showing configuration of a
`
`
`
`
`
`
`
`
`gas atomizing apparatus for preparing recycled alloy powder
`
`
`
`
`according to the invention; and
`
`
`
`
`
`
`
`
`FIGS. 6A through 6D are diagrams for explaining a
`
`
`
`
`
`
`compression sintering process for manufacturing a target
`
`
`
`according to the invention.
`DETAILED DESCRIPTION OF THE
`
`
`PREFERRED EMBODIMENTS
`
`
`
`
`
`
`
`
`
`
`
`
`6
`
`
`
`
`
`
`
`
`
`alloy used at least once for magnetron sputtering and new
`
`
`
`
`
`
`
`
`
`
`
`metals which are the same metals (Fe, Tb, Co, Cr) compos-
`
`
`
`
`
`
`
`
`
`ing the quaternary alloy are blended to contain the used
`
`
`
`
`
`
`
`
`target by 30 weight % or more, such as 50 weight %, for
`
`
`
`
`
`
`
`example,
`in the first embodiment, and an ingot is made
`
`
`
`
`
`
`
`therefrom in a vacuum melting furnace (not shown). As
`
`
`
`
`
`
`
`
`explained later, this ingot is processed into recycled alloy
`
`
`
`
`
`
`
`
`
`powder containing rare earth alloy powder such that the
`
`
`
`
`
`
`
`
`
`content of rare earth metals in the rare earth alloy powder
`
`
`
`
`
`
`
`
`
`forming the recycled alloy powderis at least 35 weight %,
`
`
`
`
`
`
`
`such as 42 weight %, for example, in the first embodiment.
`
`
`
`
`
`
`
`
`After that,
`the ingot
`is powdered in an inactive gas
`
`
`
`
`
`
`
`
`atmosphere like argon (Ar) gas by a gas atomizing process
`
`
`
`
`
`
`
`
`to prepare recycled alloy powder of FeTbCoCr alloy. Mag-
`
`
`
`
`
`
`
`
`
`netic permeability of this recycled alloy powder has been
`
`
`
`
`
`
`confirmed to be 1.5 by measurement. A gas atomizing
`
`
`
`
`
`
`
`
`apparatus used for the gas atomizing process is explained
`below.
`
`
`
`
`
`
`
`
`
`As shownin FIG. 5, the gas atomizing apparatus accord-
`
`
`
`
`
`
`
`ing to the invention includes a vacuum melting furnace 1,
`
`
`
`
`
`
`
`granulating chamber 2, cyclone 3 and container 4 which are
`
`
`connected in sequence.
`
`
`
`
`
`
`
`The vacuum melting furnace 1 is a furnace for melting
`
`
`
`
`
`materials by high-frequency induction heating, for example.
`
`
`
`
`
`
`
`A nozzle 5 is provided directly under the vacuum melting
`
`
`
`
`
`
`
`
`furnace 1, and a gasinlet6 for jetting a gas is provided neat
`the nozzle 5.
`
`
`
`
`
`
`
`
`The granulating chamber 2 is a processing chamber for
`
`
`
`
`
`
`
`powdering a material molten in the vacuum melting furnace
`
`
`
`
`
`
`
`
`
`1 by spraying it in form of fine mist and thereby preparing
`
`
`
`
`
`
`
`
`a powder material. The cyclone 3 and the container 4 are
`
`
`
`
`
`used for storing a powdered material.
`
`
`
`
`
`
`
`
`By using the gas atomizing apparatus having the above-
`
`
`
`
`
`explained configuration, recycled alloy powder of FeTb-
`
`
`
`CoCralloy is prepared.
`
`
`
`
`
`
`
`
`
`
`That is, an ingot prepared from the used target and new
`
`
`
`
`
`
`
`
`metals of the same components is melted in the vacuum
`
`
`
`
`
`
`
`
`melting furnace 1. After that, the molten material of the used
`
`
`
`
`
`
`
`target is continuously sprayed into the granulating chamber
`
`
`
`
`
`
`
`
`
`2 from the vacuum melting furnace 1 through the nozzle 5,
`
`
`
`
`
`
`
`
`and an inactive gas such as Ar gas, for example, is jetted into
`
`
`
`
`
`
`
`
`
`the granulating chamber 2 through the gas inlet 6. As a
`
`
`
`
`
`
`
`result, the molten material form fine mist.
`
`
`
`
`
`
`
`Thereafter, the molten material in form of fine mist is
`
`
`
`
`
`
`
`
`quickly cooled and powdered into recycled alloy powder 7
`
`
`
`
`
`
`
`
`while it falls down. Then, the recycled alloy powder 7 is
`
`
`
`
`
`
`
`
`introduced into the cyclone 3. Thereafter, the recycled alloy
`
`
`
`
`
`
`
`
`
`powder7 falls from the cyclone 3 into the container 4 and
`
`
`
`
`
`
`
`
`
`
`
`is stored there. Grain size and grain size profile of the
`
`
`
`
`
`
`
`globular grains 7 is controlled taking account of the tem-
`
`
`
`
`
`
`
`
`
`
`perature of the molten material, flow rate of the molten
`
`
`
`
`
`
`
`
`
`material from the nozzle 5, nozzle diameter, flow rate of the
`
`
`
`
`
`
`
`
`
`
`jetted inactive gas, and so forth. After that, the recycled alloy
`
`
`
`
`
`
`
`powder7 is classified to form an optimum grain size profile.
`
`
`
`
`
`
`
`
`After that, the recycled alloy powder 7 is blended with
`
`
`
`
`
`
`
`
`
`powder containing Fe, Tb, Co and Cr, for example, and by
`
`
`
`
`
`
`
`dry mixture thereof in an Ar gas atmosphere, alloy powder
`
`
`
`
`
`
`
`for manufacturing the target is prepared. Respective mate-
`
`
`
`
`
`
`
`
`
`
`
`rials of this alloy powder are blended such that the alloy
`
`
`
`
`
`
`
`
`powder contains rare earth alloy powder by at least 65
`
`
`
`
`
`
`
`
`
`weight %, or preferably by at least 70 weight %, and rare
`
`
`
`
`
`
`
`earth alloy powder having a magnetic permeability not
`
`
`
`
`
`
`
`
`
`
`larger than 2 by at
`least 50 weight %.
`In this first
`
`
`
`
`
`
`
`embodiment, the alloy powder is prepared to contain 80
`
`
`
`
`
`
`
`
`weight %, for example, of recycled alloy powder having a
`
`
`
`
`
`
`
`magnetic permeability of 1.5 and contain another material as
`
`10
`
`15
`
`
`
`20
`
`25
`
`
`
`30
`
`35
`
`
`
`40
`
`
`
`45
`
`
`
`50
`
`
`
`55
`
`
`
`60
`
`
`
`65
`
`
`
`Ex. 1056, Page 9
`
`Ex. 1056, Page 9
`
`
`
`
`
`US 6,409,965 B1
`
`
`
`
`
`10
`
`15
`
`
`
`20
`
`
`
`30
`
`
`the sputtering
`
`
`
`8
`7
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`reduced, and the price of magneto-optical recording medi-
`its remainder part, which is adjusted to make a predeter-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`ums manufactured by sputtering using this target can be
`mined target composition. Namely,
`they are blended to
`reduced.
`
`
`
`
`
`
`
`enable fabrication of a target containing 66 atomic % of Fe,
`
`
`
`
`
`
`
`
`
`
`
`
`Next explained is a manufacturing methodofa sputtering
`24 atomic % of Tb, 7 atomic % of Co and 3 atomic % of Cr.
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`target according to the second embodimentof the invention.
`As a result, mixed powder satisfying the above-indicated
`
`
`
`
`
`
`
`
`
`
`The used target used in the second embodimentis made of
`requirements is prepared.
`
`
`
`
`a ternary FeTbCoalloy.
`
`
`
`
`Subsequently, using this mixed powder,
`
`
`
`
`
`
`
`In the sputtering target manufacturing method according
`
`
`target is manufactured.
`
`
`
`
`
`
`
`
`to the second embodiment, a target of a FeTbCoalloy used
`
`
`
`
`
`
`
`
`Thatis, first as shown in FIG. 6A, using a container 11
`
`
`
`
`
`
`
`
`
`
`at least once for magnetron sputtering and new metals of the
`
`
`
`
`
`
`
`
`storing mixed powder 10, the mixed powder 10 is supplied
`
`
`
`
`
`
`
`
`
`same components (Fe, Tb, Co) are blended to contain the
`
`
`
`
`
`
`
`
`into a carbon mold 12 from aboveit. Next, as shown in FIG.
`
`
`
`
`
`
`
`used target by 30 weight % or more, such as 50 weight %,
`
`
`
`
`
`
`
`
`6B, a compression punch rod 13 is inserted into the carbon
`
`
`
`
`
`
`
`for example, in the second embodiment, and an ingot is
`
`
`
`
`
`
`
`
`
`mold 12 from above the carbon mold and the mixed powder
`
`
`
`
`
`
`
`made therefrom in a vacuum melting furnace (not shown).
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`10 supplied therein. After that, as shown in FIG. 6C, the
`Similarly to the first embodiment,this ingot is processed into
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`carbon mold 12 is set
`in a predetermined compression
`recycled alloy powder containing rare earth alloy powder
`such that the content of rare earth metals in the rare earth
`
`
`
`
`
`
`
`
`sintering apparatus (not shown), and heated and sintered
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`there under a pressure applied onto the mixed powder 10
`alloy powder forming the recycled alloy powderis at least
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`35 weight %, such as 43 weight %, for example,
`in the
`through the compression punch rod 13. After it is sintered,
`second embodiment.
`
`
`
`
`
`
`
`
`
`
`
`as shown in FIG. 6D, the pressure is removed, and it is
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`is powdered in an inactive gas
`After that,
`the ingot
`cooled. Then, a sintered material 15 made by sintering the
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`atmosphere by a gas atomizing process to prepare recycled
`mixed powder 10 is removed from the carbon mold 12.
`
`
`
`
`
`
`
`alloy powder of FeTbCo alloy. Magnetic permeability of this
`
`
`
`
`
`
`
`
`
`After that, the outer circumferential surface and top and
`
`
`
`
`
`
`
`
`
`recycled alloy powder has been confirmed to be 0.9 by
`
`
`
`
`
`
`
`
`
`bottom surfaces of the sintered material 15 prepared as
`
`
`
`
`
`
`
`
`
`measurement. The gas