`Samsung Electronic's Exhibit 1060
`Exhibit 1060, Page 1
`
`
`
`IN THE UNITED STATES
`PATENT AND TRADEMARK OFFICE
`
`!
`
`iil
`
`-
`ea
`~
`=~PATENT APPLICATION
`Se-Ronald Eugene Miller
`==" John Z.Pastalan
`=—
`“George E. Rittenhouse
`o
`
`CASE 1-1-1
`
`TITLE
`
`Pulse DC Reactive Sputtering Method
`
`ASSISTANT COMMISSIONER FOR PATENTS
`WASHINGTON,D.C, 20231
`
`SIR:
`
`
`
`
`UBCEaseas|
`“Expressait" malt
`number=iS
`
`
`
`hull
`
`
`
`
`
`tieWitsessessaouillWMWeMag
`
`MyaallMistHall
`WallMe
`
`Well
`
`NEW APPLICATION UNDER37 CFR 1.53(b)
`Enclosed are the following papers relating to the above-named application for patent:
`Specification
`4 Informal sheets of drawing(s)
`Information Disclosure Statement
`
`
`
`Basic Fee
`
`
`
`
`Multiple Dependent
`Claim(s), if applicable
`
`Please file the application and charge Lucent Technologies Deposit Account No. 12-2325 the
`amount of $790, to coverthe filing fee. Duplicate copies ofthis letter are enclosed. In the event
`of non-payment or improper payment of a required fee, the Commissioner is authorized to
`charge or to credit Deposit Account No. 12-2325 as required to correct the error.
`
`The Assistant Commissioner for Patents is hereby authorized to treat any concurrentorfuture re-
`ply, requiring a petition for extension of time under 37 CFR § 1.136 forits timely submission, as
`incorporating a petition for extension of time for the appropriate length of time if not submitted
`with the reply.
`
`(Room 3C-512),
`to Docket Administrator
`correspondence
`all
`address
`Please
`Lucent Technologies Inc., 600 Mountain Avenue, P. O. Box 636, Murray Hill, New Jersey
`07974-0636. However, telephone calls should be made to me at 908-582-3246.
`
`Respectfully,
`
`aeJonn M. Harman
`Reg. No. 38173
`Attorney forApplicant(s)
`
`9
`asus
`A
`pae_f—-(-F7o
`Lucent Technologies Inc.
`600 Mountain Avenue
`P. O. Box 636
`Murray Hill, New Jersey 07974-0636
`
`PT 13 12/97
`
`Copy provided by USPTO from the IFWImage Database on 09-03-2020
`
`Ex. 1060, Page 2
`Ex. 1060, Page 2
`
`
`
`
`
`Miller 1-1-1
`
`PULSE DC REACTIVE SPUTTERING METHOD
`
`FOR FABRICATING PIEZOELECTRIC RESONATORS
`
`Background of the Invention
`
`1, Field of the Invention
`
`The invention relates to piezoelectric resonators. More particularly, the invention
`
`relates to deposition techniques used in fabricating piezoelectric resonators and the
`
`piezoelectric resonators made by those deposition techniques.
`
`10
`
`2. Description of the Related Art
`
`Piezoelectric resonators are devices comprising a wafer of piezoelectric material
`
`such as quartz, zinc oxide (ZnO), aluminum nitride (AIN) or ceramic material mounted or
`
`otherwise formed on a substrate (e.g., silicon or aluminum oxide). Uponthe application
`
`15
`
`of a voltage to the piezoelectric material, e.g., via electrodes, the piezoelectric material
`
`vibrates in a certain vibrational mode depending on the orientation or polarization of the
`piezoelectric material andat a certain (resonant) frequency depending onthe thickness of
`
`the piezoelectric material.
`
`Piezoelectric resonators provide clearly defined mechanical resonances and are
`
`20.
`
`useful, e.g., for discriminating between signals based on frequency diversity (i.e., a filter).
`
`Also, piezoelectric resonators are useful in providing stable frequency signals, e.g., as a
`
`frequencystabilizing feedback elementin an oscillator circuit.
`
`Typically, the resonant frequency of the piezoelectric material is inversely
`
`proportional to its thickness. Accordingly, for piezoelectric resonators to operate at high
`
`frequencies, e.g., frequencies greater than approximately 700 Megahertz (MHz),the
`thickness of the piezoelectric material must be reducedto the point of depositing a thin
`piezoelectric film on the substrate. Conventional deposition techniques for depositing
`
`such piezoelectric films include, e.g., chemical vapor deposition (CVD) and sputter
`
`deposition such as RF sputter deposition.
`
`avilaMaalMall
`
`a e
`
`eMadMatt
`
`eal
`thal
`
`Copy provided by USPTO from the IFW Image Database on 09-03-2020
`
`Ex. 1060, Page 3
`Ex. 1060, Page 3
`
`
`
`SSEYESee
`
`Miller 1-1-1
`
`Sputter deposition involves a vacuum deposition process in which a sputtering
`
`target is bombarded with ions, typically an ionized noble gas such as argon, and the atoms
`
`of the target material are mechanically freed by momentum transfer and available for
`
`coating a nearby substrate. Suitable target materials include, e.g., aluminum, silicon and
`
`5
`
`titanium. In a reactive sputtering process, a reactive gas is introduced into the deposition
`
`chamberandreacts with the target material to producea target insulating film that
`
`subsequently is sputtered onto the substrate or reacts with freed target material to form a
`
`coating material that is sputtered onto the substrate. Suitable reactive gases include
`
`oxygen,nitrogen, ammonia and hydrogen.
`
`10
`
`In DC reactive sputtering, the target material and the reactive gas react in a plasma
`
`to produce the coating material. The plasma is formed by the noble gas when an direct
`
`current (DC)electric potential is applied within the sputtering chamber. For example,
`
`aluminum atoms from an aluminum target react with nitrogen (reactive gas) at the target
`
`to produce an insulating film of aluminum nitride (AIN), which is sputtered onto the
`substrate with ions of argon (noble gas). Other suitable coatings include, e.g., oxides
`
`15
`
`such as aluminum oxide (Al,03), carbides such as silicon carbide (SiC), and nitrides such
`
`as titanium nitride (TiN) or zinc oxide (ZnO).
`
`However, sputter deposition and reactive sputtering techniques including DC
`reactive sputtering often do not provide adequate deposition rates. Accordingly, such
`techniques take longer to perform, which is undesirable from the standpointof required
`processing time and ultimately is undesirable from an economic standpoint. Also, the
`
`20
`
`relatively lengthy deposition period increases the introduction of impurities into the
`
`piezoelectric film being deposited.
`
`Onespecific type of reactive sputtering that often is used in, e.g., silicon
`
`25
`
`processing methods, is pulse DC reactive sputtering. Since the target insulating film is an
`
`insulator(e.g., AIN), the noble gas ions tend to accumulateonits surface, reducing the
`
`sputter rate and ultimately terminating the sputter process. In pulse DC reactive
`
`sputtering, the electric potential formed between the cathode and the anodein the
`
`chamberis reversed periodically to prevent charge accumulation on the target insulating
`
`HlMyll
`ollWhbb
`
`4
`
`E
`;
`
`
`
`30~—sfilm. More specifically, the positive portion of the applied voltage neutralizes
`
`ri 5
`Copyprovided by USPTOfrom
`
`the IFWImage Database on 09-03-2020
`
`Ex. 1060, Page 4
`Ex. 1060, Page 4
`
`
`
`
`
`Miller 1-1-1
`
`accumulation of the noble gas ions on the surface of the target insulating film, and the
`
`negative portion of the applied voltage, if sufficient, causes ions from the noble gas to
`
`impinge uponthe target insulating film formed on the target material, physically
`
`removing ions thereof and allowing them to accumulate on the substrate. This forms the
`
`deposited layer or coating.
`
`In additionto silicon processing, pulse DC reactive sputtering techniquesalso are
`
`useful in depositing,e.g., wear resistant coatings such as tungsten carbide (WC) or
`
`titanium nitride (TiN)on,e.g., drill bits, wear plates and valve spindles. See generally,
`
`e.g., U.S. Pat. Nos. 5,651,865 and 5,718,813. In pulse DC reactive sputtering, the major
`
`qualitative concernsare the ultimate film constituency (i.e., reduced impurities introduced
`
`into the deposited film), film stress and film texture. Film texture generally characterizes
`
`the physical structure of the film resulting from the shape, arrangementand proportions of
`
`its components.
`
`With respect to the deposition of thin piezoelectric films such as aluminum nitride
`
`15
`
`(AIN), an important consideration includesthe crystal orientation of the atoms within the
`
`final deposited film. That is, the crystal structure cannot be amorphous; it must be of a
`
`single crystal nature. This is because piezoelectricity occurs from the alignmentof the
`
`atomic dipoles within the film, and an amorphous film produces random dipole moments
`
`with no macroscopic response. Also, it is desired that the film orientation be
`
`perpendicular to the substrate to facilitate the launching of longitudinal waves in a
`
`structure. It is believed that current deposition techniques are concerned primarily with
`
`deposition rates and consideration such as crystal structure are not taken into account.
`
`Accordingly, it is desirable to have available an improved technique for
`
`depositing thin films of piezoelectric material such as aluminum nitride (AIN) on a
`
`substrate that provides piezoelectric films with improved control of film constituency,
`
`stress and texture.
`
`Su
`
`the Invention
`
`The invention is embodied in a pulse DC reactive sputtering method for thin film
`
`deposition. The inventive methodis used, e.g., for depositing thin films of piezoelectric
`
`Copyprovided by USPTOfrom the IF W Image Database on 09-03-2020
`
`Ex. 1060, Page 5
`Ex. 1060, Page 5
`
`
`
`eeees
`
`Miller 1-1-1
`
`materials such as aluminum nitride on substrates with patterned electrodes during the
`
`fabrication of piezoelectric resonators. Embodiments of the invention includethe steps of
`
`providing a target material such as aluminum within the sputtering chamber,positioning a
`
`substrate such as silicon within the sputtering chamber, providing a noble gas such as
`
`5
`
`argon into the sputtering chamber, directing a reactive gas such as nitrogen within the
`
`sputtering chamber, applying a pulsed DC voltage across the electrodes within the
`
`sputtering chambersufficient to cause ions from the noble gas to impinge upon the thin
`
`insulating layer (¢.g., AIN) formed on the target material, physically removing ions
`
`thereof and allowing them to accumulate onthe substrate. According to embodiments of
`
`10
`
`the invention, the pulse width of the positive portion of the applied voltage is adjusted
`
`based onits effect on the desired film constituency, stress, and texture. By comparison,
`
`conventional arrangements establish pulse widths based on their effect on improving
`
`depositionrates, regardless ofits effect on the film texture. Alternatively, embodiments
`of the invention adjust the direction and delivery of the reactive gas within the sputtering
`
`+
`
`15
`
`chamber, e.g., toward the target material, to further enhance the desired film constituency,
`stress, and texture through more efficient reaction by the reactive gas.
`
`Brief Description of the Drawings
`
`In the drawings:
`
`20
`
`Figs. la-b are simplified side, cross-sectional views of non-via, Bragg reflection
`
`piezoelectric resonators;
`Fig. 2 is a simplified schematic diagram of a pulse DC reactive sputtering ,
`
`arrangement;
`
`Fig. 3 is a simplified block diagram of a method for fabricating piezoelectric
`
`25
`
`resonators according to embodiments ofthe invention;
`
`Fig. 4a is a graphical diagram of the voltage applied to the electrodes of a pulsed
`
`DC reactive sputtering arrangement according to an embodimentofthe invention; and
`
`Fig. 4b is a graphical diagram of the voltage applied to the electrodes of a
`
`conventional pulsed DC reactive sputtering arrangement.
`
`:
`
`CopyprovidedbyUSPTOfromtheIFWImageDatabaseon09-03-2020
`
`Ex. 1060, Page 6
`Ex. 1060, Page 6
`
`
`
`Miller 1-i-1
`
`Detailed Description
`
`Although specific features, configurations and arrangements are discussed
`
`hereinbelow,it should be understood that such is done forillustrative purposes only. A
`
`person skilled in the relevant art will recognize that other steps, configurations and
`
`arrangements are useful without departing from the spirit and scope of the invention.
`
`Embodiments of the invention include piezoelectric resonators with improved
`
`piezoelectric film quality and control of methods for making such piezoelectric resonators
`
`using pulse DC reactive sputtering for the deposition of thin films of piezoelectric
`
`material on substrates. Embodiments of the invention are based on the realization that
`
`varying or adjusting the pulse width of the positive portion of the applied DC voltage
`
`improves the control and crystallinity of the deposited piezoelectric material.
`
`Alternatively, adjusting the direction and delivery of the reactive gas within the sputtering
`
`chamberfurther enhances such desired results. Typically, such adjustments are at the
`
`expense ofdeposition rate, which drives conventional pulse DC reactive sputtering
`
`techniques. However, increased deposition rates, in general, produce metal-rich films
`
`that degrade the crystalline structure of the deposited piezoelectric material.
`
`Referring now to Fig. la, a simplified diagram of a piezoelectric resonator 100 is
`
`shown. The piezoelectric resonator 100 comprises a substrate 110, a layer or body 120 of
`piezoelectric material, and an acoustic reflecting region 125 such as a Braggreflecting
`region therebetween. Alternatively, as shown in Fig. 1b, the layer 120 of piezoelectric
`
`material is suspended above the substrate 110 by a suspended membrane 127of,e.g., air
`
`or silicon nitride (SiN,). A pair of electrodes 130, 135 are coupled or otherwise attached
`
`to piezoelectric material 120 of both arrangements, e.g., by conventional means.
`
`The layer 120 of piezoelectric material is made of any suitable material that has
`
`piezoelectric qualities sufficient for the particular resonator application. Typical
`
`piezoelectric materials include, e.g., quartz, zinc oxide (ZnO), aluminum nitride (AIN)
`
`and ceramic materials such as lithium niobate (LiNbO),lithium tantalate (LiTaQ3),
`
`paratellurite (TeOQ.) and lead titanate zirconate (PZT-SA). The substrate 110 is madeof,
`
`e.g., silicon (Si), aluminum oxide (Al,O3) or other suitable materials such as quartz,
`
`
`
`MaraljaaTetMaalWaal
`
`15
`
`20
`
`25
`
`30
`
`sapphire, polysilicon and aerogel.
`
`Copyprovided by USPTO from the IFW Image Database on 09-03-2020
`
`Ex. 1060, Page 7
`Ex. 1060, Page 7
`
`
`
`
`
`Miller 1-1-1
`
`In use, the piezoelectric resonator 100 typically has a voltage potential applied
`
`across electrode 130, 135, which causes the layer 120 of piezoelectric material to vibrate
`
`at a resonant frequency,fo, due to the piezoelectric effect, thus operating as a resonator.
`
`The operating frequencyof the piezoelectric resonator 100 depends on the total thickness
`
`of the piezoelectric layer 120 and the electrodes 130, 135, which total thickness is due
`
`mostly to the thickness of the piezoelectric layer 120. More specifically, the operating
`
`frequency is inversely proportional to the thickness of the piezoelectric layer 120 and the
`
`electrodes 130, 135. Accordingly, for high operating frequencies,e.g., frequencies
`
`greater than approximately 700 Megahertz (MHz), the thickness of the piezoeleciric layer
`
`120 has been reducedto the extentthat the piezoelectric layer 120 is merely a thin film
`deposited on the substrate 110. Typical thicknesses of the piezoelectric film range from
`
`approximately five hundred (500) nanometers (nm) to approximately ten (10) microns
`
`weld
`
`(um).
`
`Asdiscussed previously herein, conventional sputtering techniques such as sputter
`
`deposition, reactive sputter deposition, and DC reactive sputtering do not provide
`
`adequate deposition rates. However, one type of conventional sputtering technique that
`
`often provides an adequate deposition rate is pulse DC reactive sputtering. Referring now
`
`to Fig. 2, a typical pulse DC reactive sputtering arrangement 200 is shown.
`
`The conventional arrangement 200 includes a chamber 210 (e.g., a plasma
`
`20.
`
`chamber) and a pair of electrodes 220, 225 configured within the chamber 210. The
`
`electrodes 220, 225 are capable of supplying an electric potential therebetween, as
`
`indicated generally by the polarity signs associated therewith. Theelectric potential
`
`applied to the electrodes is controlled, e.g., by any suitable control means (shown
`
`generally as 230), including pulse width control.
`
`25
`
`The arrangement 200 includes a first source 240 capable of supplying a noble gas,
`€.g., argon (Ar), into the chamber 210. Other suitable noble gases include, e.g., xenon
`(Xe) and krypton (Kr). Also, the arrangement 200 includes a second source 250 capable
`
`of supplying a reactive gas into the chamber 210,e.g., via a gas delivery ring 255. The
`
`reactive gas is, €.g., oxygen, nitrogen or other suitable gas.
`
`Copy provided by USPTOfrom the IFW Image Database on 09-03-2020
`
`Ex. 1060, Page 8
`Ex. 1060, Page 8
`
`
`
`Miller 1-1-1
`
`A (conductive) target 260 is positioned within the chamber210, e.g., in electrical
`
`connection with one of the two electrodes 220. In this manner, the target 260 serves as
`
`the cathode during the sputter portion of the cycle when a negative electrical potential is
`
`applied across electrodes 220, 225. The target 260 is, e.g., a relatively flat plate of
`
`aluminum or other suitable material such as zinc.
`
`
`
`The substrate 110 upon which the piezoelectric thin film is to be coatedis
`
`positioned within the chamber 210, e.g., above the target 260 and the gas delivery ring
`
`255. The substrate 110 is made of, e.g., silicon, aluminum oxide (Al,O3) or other suitable
`
`material such as quartz, sapphire, polysilicon and aerogel.
`
`sellHITthe
`
`U
`
`all
`
`WhatTclth,
`
`Malltbe
`
`—tn
`
`20
`
`In operation, the first source 240 provides noble gas into the chamber 210. A
`
`second source 250 delivers reactive gas into the sputtering chamber 210. According to
`
`embodiments of the invention, the gas delivery ring 255 directs the delivery of the
`
`reactive gas at the target 260 (as will be discussed in greater detail hereinbelow). The
`
`reactive gas producesa relatively thin insulating film (e.g., AIN) on the target 260. Upon
`
`the application of a sufficient electric potential across the electrodes 220, 225, ionization
`
`of the noble gas occurs and ions therefrom sputter the thin nitride film on the target 260.
`
`Atoms ofthe nitride film onthe target 260 are freed by the ion bombardmentand thus are
`
`made available for coating the substrate 110.
`
`Pulsed DC reactive sputtering arrangements offer an additional variation to the
`
`arrangement described in that the electric potential supplied between the electrodes
`
`includes a positive voltage pulse. Conventionally, the voltage is pulsed, e.g., to reduce
`
`the possibility of arching (see, e.g., U.S. Patent No. 5,651,865) and to prevent excessive
`
`accumulation of noble gas ions on the surface of the target material. However, according
`
`to embodiments of the invention, the pulse yields an extra degree of freedom in the film
`
`deposition to improvethe film quality and reproducibility.
`
`For example, conventional pulse DC reactive sputtering arrangements supply a
`
`positive DC voltage of approximately 50 volts typically for approximately 25% ofthe
`
`duty cycle and then a negative DC voltage of approximately 200-500 volts for remaining
`
`75% of the duty cycle. The duty cycle ratio of positive DC voltage to negative DC
`
`30
`
`voltage conventional is adjusted based on the effect it has on deposition rate and noble
`
`Copyprovided by USPTOfrom the IFWImage Database on 09-03-2020
`
`Ex. 1060, Page 9
`Ex. 1060, Page 9
`
`
`
`Miller 1-1-1
`
`gas ion accumulation. As mentioned previously herein, the amplitude and pulse width of
`
`the applied DC voltageis controlled, e.g., by any suitable control means (shown generally
`
`as 230).
`
`However, the conventional desire to neutralize accumulated charge onthe target
`film and maximum deposition rate results in a film thatis slightly metal-rich. This
`stoichiometry producesa relatively poorfilm texture. Therefore, according to
`embodimentsof the invention, the pulse width is adjusted to produce a stoichiometry that
`improves the film texture.
`
`In pulse DC reactive sputtering systems, whetherit be in silicon processingor in
`
`fabricating piezoelectric resonators, other variables also are managed in an attempt to
`
`improve the deposition rate and the overall quality of the deposited films without
`
`sacrificing too much from either. Such variables include, e.g., substrate temperature,
`
`substrate bias, deposition, gas ratio and chamber pressure. However, just as with the
`
`pulse width, many of these variables are advantageous to one aspect and simultaneously
`
`are disadvantageous to another aspect. Therefore, many of the variables often are
`
`adjusted with such considerations in mind and, accordingly, are set in a manner that
`
`amounts to a compromise between the two conflicting aspects. In general, the more
`
`important variables are chamberpressure, reactive gas delivery, deposition power and gas
`
`ratio.
`
`Embodiments of the invention are based on the realization that adjusting the pulse
`
`width ofthe positive portion of the applied DC voltage significantly increases the film
`
`texture for a given range of other deposition parameters. Furthermore, providing a gas
`
`delivery system that directs the reactive gas directly to the active sputter area further
`
`enhances the film texture. Accordingly, embodiments of the invention offer piezoelectric
`
`resonators having thin films of piezoelectric material with improved texture compared to
`
`similarly deposited films without the inventive pulse width adjustments and gas delivery.
`
`Fig. 3 shows generally a method 300 for fabricating a piezoelectric resonator
`
`according to embodiments of the invention. Reference will be made periodically to the
`
`WoWWeWT
`
`10
`
`15
`
`20
`
`25
`
`pulse DC reactive sputtering arrangement 200 shown in Fig. 2 during the discussion
`
`30
`
`hereinbelow of the method 300. However, it should be remembered that the exemplary
`
`Copy provided by USPTOfrom the IFW Image Database on 09-03-2020
`
`Ex. 1060, Page 10
`Ex. 1060, Page 10
`
`
`
`
`
`Miller 1-1-1
`
`
`
`MiresanalWWHieWiadMeal
`
`IHellA.
`
`method 300 shown in Fig. 3 and the pulse DC reactive sputtering arrangement 200 shown
`in Fig. 2 are for illustration purposes only and are not meant to be a limitation of the
`
`invention.
`
`The first step 310 of the inventive method 300 is to provide the target material
`
`260 for use within the sputtering chamber 210 suitable for use in pulse DC reactive
`
`sputtering techniques. As discussed previously herein, the target material is, e.g.,
`
`aluminum,zinc or other suitable (conductive) material. The next step 320 is to provide or
`
`otherwise position the substrate 110 within the sputtering chamber 210. The substrate
`
`110 is positioned within the chamber 210, e.g., above the target 260. The substrate is
`
`made of, e.g., silicon, aluminum oxide (Al,03) or other suitable material such as quartz,
`
`sapphire, polysilicon and aerogel.
`
`The next step 330 is to introduce a noble gas (¢.g., via the first source 240) into
`
`the sputtering chamber 210. The next step 350 is to introduce the reactive gas into the
`
`sputtering chamber 210. According to embodiments ofthe invention, the reactive gas is
`
`directed onto the target 260,e.g., by the gas delivery ring 255. The nextstep 340 is to
`apply a sufficient electrical potential across the electrodes 220, 225 to cause ions of the
`
`noble to be directed toward the target 260 along with reactive gas with sufficient energy
`
`to cause atoms ofthe target material and the insulating layer formed onthe target 260 to
`
`be released from the target 260. The next step 360 is to adjust the pulse width to
`
`20
`
`neutralize the accumulated charge on the surface of the target 260. As discussed
`previously herein, the reactive gas forms a thin film on the surface of the target 260,
`whichis released and, in turn, coats the substrate and forms a layer thereon.
`
`As discussed previously herein, pulse DC reactive sputtering arrangements
`
`provide a periodic positive DC voltage across the electrodes 220, 225 separated by
`
`periods in which a negative voltage potential exists across the electrodes and target
`
`sputtering occurs. The application of this periodic positive voltage pulse is done for a
`
`numberof reasons, as discussed hereinabove, including to improve film texture and
`
`increase piezoelectric response.
`
`According to embodiments of the invention, the method 300 includes an adjusting
`
`30
`
`step 360 to adjust the pulse width of the applied periodic DC pulses for purposes of
`
`Copy provided by USPTO from the IFWImage Database on 09-03-2020
`
`Ex. 1060, Page 11
`Ex. 1060, Page 11
`
`
`
`
`
`Miller 1-1-1
`
`improvingthe crystalline quality of the coating or layer. The pulse width and other
`parameters associated with the applied voltage signal are controlled, e.g., by a control
`
`means 230, shown generally in Fig. 2.
`
`According to embodiments of the invention,in general, with a given set of
`deposition parameters, adjusting the pulse width and directing the gas components to the
`
`active sputtering region on the surface of the target 260 improve the film texture ofthe
`final deposited layer. According to embodiments ofthe invention, the pulse width ofthe
`positive portion of the pulsed DC voltage is adjusted to be within the range from
`approximately 5-40% of the pulsed DC voltage duty cycle.
`
`By comparison, conventional pulsed DC reactive sputtering arrangements often
`
`establish pulse widths based on increasing or maximizing depositionrates, with little if
`
`any regard for the crystalline quality of the deposited layer that ultimately is formed on
`
`the substrate. Conventional pulse widths typically are set to no more than approximately
`
`25% of the duty cycle and typically remain at or near 25% ofthe duty cycle.
`
`Figs. 4a-b illustrate the voltage applied betweenthe electrodes in pulsed DC
`
`Teactive sputtering arrangements according to embodiments ofthe invention (Fig. 4a) and
`
`according to conventional configurations (Fig. 4b). As shown in Fig, 4a, the applied
`
`voltage pulses according to embodiments of the inventiontypically are less than 25% of
`
`the duty cycle, which is smailer than the applied voltage pulses in conventional
`arrangements, as shownin Fig. 4b.
`According to embodimentsof the invention, regions of piezoelectric material are
`
`formed that have full width at half maximum (FWHM) rocking curves of less than
`
`approximately 2.5, but typically within the range from approximately 1.8 to 2.5. By
`
`comparison, conventional methods produce piezoelectric materials that have full width at
`
`half maximum rocking curvesofat least 2.5, more typically within the range from
`
`approximately 3 to 5.
`
`wellWETMadatl
`
`HesMellMall
`Wiadltte
`
`20
`
`25
`
`It will be apparent to those skilled in the art that many changes and substitutions
`
`can be made to the embodiments of the piezoelectric resonators deposition techniques
`
`herein described without departing from the spirit and scope of the invention as defined
`
`30
`
`by the appended claims andtheir full scope of equivalents.
`
`10
`
`Copy provided by USPTO fromthe IFW Image Database on 09-03-2020
`
`Ex. 1060, Page 12
`Ex. 1060, Page 12
`
`
`
`
`
`Miller 1-1-1
`
`WHATIS CLAIMEDIS:
`
`1. A method of pulse DC reactive sputtering, said method comprising the steps
`
`of:
`
`providing a target material within a sputtering chamber;
`
`positioning a substrate within said sputtering chamber;
`
`introducing a noble gas into said sputtering chamber;
`
`introducing a reactive gas into said sputtering chamber, wherein said reactive gas
`
`reacts with a portion of said target material to form an insulating film on said target
`
`material;
`
`applying a pulsed DC voltage across a pair of electrodes that are positioned within
`
`said sputtering chamberin such a way that ions from said noble gas impinge upon the
`
`target material and the insulating layer formed on said target material, wherein the freed
`
`atoms of the target material and the insulating layer are available for accumulation on said
`
`substrate to form a coating thereon; and
`
`adjusting the pulse width of said pulsed DC voltage to improve the crystalline
`
`structure of the coating formed on said substrate.
`
`2. The method as recited in claim 1, wherein the pulsed DC voltage includes a
`
`positive portion and a negative portion, and wherein said adjusting step adjusts the
`
`positive portion of the pulsed DC voltage to be within the range from approximately 5-
`
`40% of the pulsed DC voltage duty cycle.
`
`3. The method as recited in claim 1, further comprising the step of directing said
`
`reactive gas toward said target material within said sputtering chamber.
`
`4. The method as recited in claim 1, wherein the pulsed DC voltage includes a
`
`positive portion and a negative portion, and wherein said applying step further comprises
`
`10
`
`11
`
`12
`
`13
`
`14
`
`15
`
`tewebo
`
`11
`
`Copy provided by USPTO from the IFW Image Database on 09-03-2020
`
`Ex. 1060, Page 13
`Ex. 1060, Page 13
`
`
`
`
`
`Miller 1-1-1
`
`applying the positive portion of the pulsed DC voltage sufficient to limit the
`
`accumulation of ions of said noble gas on said target material.
`
`5. The method as recited in claim 1, wherein said reactive gas is selected from the
`
`group consisting of nitrogen, oxygen, ammonia and hydrogen.
`
`6. The methodas recited in claim 1, wherein said target material is selected from
`
`the group consisting of aluminum,quartz, zinc oxide (ZnO), aluminum nitride (AIN),
`
`lithium niobate (LINDO3), lithium tantalate (LiTaO;), paratellurite (TeO.) and lead
`
`titanate zirconate (PZT-SA).
`
`7. The methodas recited in claim 1, wherein said noble gas is selected from the
`
`group consisting of argon (Ar), xenon (Xe) and krypton (Kr).
`
`8. The method as recited in claim 1, wherein said substrate is selected from the
`
`group consisting ofsilicon, aluminum oxide (Al,O3), quartz, sapphire, polysilicon and
`
`aerogel.
`
`9. A method of making a piezoelectric resonator, said method comprising the
`
`steps of:
`
`providing a sputtering chamber including a target material;
`
`positioning a substrate within said sputtering chamber;
`
`introducing a noble gas into said sputtering chamber;
`
`directing a reactive gas within said sputtering chamber toward the target material,
`
`wherein said reactive gas reacts with a portion ofsaid target material to form an
`
`insulating film on said target material;
`applying a pulsed DC voltage across a pair of electrodes that are positioned within
`
`said sputtering chamber in such a way that ions from said noble gas impinge uponthe
`target material and the insulating layer formed on said target material, wherein the freed
`
`woahLABHlHallUa
`Mial¥TheeMaadEMedEMilth
`
`iDveebl
`
`12
`
`Copy provided by USPTO from the IFW Image Database on 09-03-2020
`
`Ex. 1060, Page 14
`Ex. 1060, Page 14
`
`
`
`
`
`SAWIWhetlHeath
`
`Hevane
`
`AWMMadeWeeAllhalMl
`
`Miller 1-1-1
`
`atoms of the target material and the insulating layer are available for accumulation on said
`
`substrate to form a coating thereon; and
`
`adjusting the pulse width of said pulsed DC voltage to improvethe crystalline
`
`structure of the coating formed on said substrate.
`
`10. The method as recited in claim 9, wherein said adjusting step adjusts the
`
`pulse width of the positive portion of the pulsed DC voltage to be within approximately
`
`53-40% of the duty cycle.
`
`11. The method as recited in claim 9, wherein said target material is selected
`
`from the group consisting of aluminum, quartz, zinc oxide (ZnO), aluminum nitride
`
`(ANN), lithium niobate (LiNbO), lithium tantalate (LiTaO3), paratellurite (TeO2) and lead
`
`titanate zirconate (PZT-SA).
`
`12. The method as recited in claim 9, wherein said reactive gas is selected from
`
`the group consisting of nitrogen, oxygen, ammonia and hydrogen.
`
`13. The method as recited in claim 9, wherein said noble gas is selected from the
`
`group consisting of argon (Ar), xenon (Xe) and krypton (Kr).
`
`14. The method as recited in claim 9, wherein said substrate is selected from the
`
`group consisting ofsilicon, aluminum oxide (Al,O3), quartz, sapphire, polysilicon and
`
`aerogel.
`
`135. A piezoelectric resonator, comprising:
`
`a substrate;
`
`aregion of piezoelectric material;
`
`an acoustic reflection region operably coupled between said substrate and said
`
`region ofpiezoelectric material; and
`
`a pair of electrodes coupled to said region of piezoelectric material,
`
`nOAF&FWw
`
`Copy provided by USPTO from the IFW Image Database on 09-03-2020
`
`Ex. 1060, Page 15
`Ex. 1060, Page 15
`
`
`
`Miller 1-1-1
`
`wherein said region of piezoelectric material has a full width at half maximum
`
`(FWHM)rocking curve ofless than approximately 2.5.
`
`16. The resonatoras recited in claim 15, wherein said region of piezoelectric
`
`material has a full width, half maximum rocking curve of within the range from
`
`approximately 1.8 to 2.5.
`
`17. The resonator as recited in claim 15, wherein said substrate is selected from
`
`the group consisting of silicon, aluminum oxide (Al,03), quartz, sapphire, polysilicon and
`
`aerogel.
`
`18. The resonatoras recited in claim 15, wherein said region of piezoelectric
`
`material is selected from the group consisting of aluminum, quartz, zinc oxide (ZnO),
`
`aluminum nitride (AIN),lithium niobate (LINbO3), lithium tantalate (LiTaO3),
`
`paratellurite