`DOL 10,1007/s40005-012-0002-y
`
`RESEARCH ARTICLE
`
`Formulation and in vitro evaluation of transdermal drug delivery
`system for donepezil
`
`Robhash Kusam Subedi « Je-Phil Ryoo -
`Cheol Moon - Myung-Kwan Chun -
`Hoo-Kyun Choi
`
`Received: 18 October 2011 / Accepted: 28 November 2011 / Published online: 20 January 2012
`© The Korean Society of Pharmaceutical Sciences and Technology and Springer Dordrecht 2012
`
`Abstract The effects of different formulation variables
`
`on the transdermal absorption of donepezil were investi-
`gated. The permeation of donepezil from various pressure
`sensitive adhesive matrices was evaluated using flow-
`through diffusion cell system at 37°C. The penetration of
`donepezil from the matrices was found to be influenced by
`the nature of adhesives. 1:1 combination of acrylic rubber
`hybrid adhesives (Duro-Tak® 87-503A and Duro-Tak®
`87-504A) provided good adhesion force and high flux of
`donepezil. Significant increase in flux was obtained using
`Brij” 30, Brij” 52, and their combination, as penetration
`enhancers. Manual assessment using thumb test revealed
`that patches containing combination of enhancers pos-
`sessed good adhesive properties. The formulation con-
`taining combination of Brij® 30 and Brij® 52, each at the
`level of 5% v/w with 15% w/w drug load in 1:1 combi-
`nation of Duro-Tak® 87-503A and Duro-Tak® 87-504A
`matrix was found to be the best. No significant alteration in
`morphology and assay values were observed during the
`physical and chemical stability tests conducted for the
`study period of 3 months.
`
`Keywords Donepezil - Transdermal drug delivery -
`Percutaneous penetration - Chemical enhancers -
`Alzheimer’s disease
`
`
`
`R. K. Subedi - M.-K. Chun - H.-K. Choi (D4)
`BK21 Project Team, College of Pharmacy, Chosun University,
`375 Seosuk-dong, Dong-gu, Gwangju 501-759, South Korea
`e-mail: hgchoi@chosun.ac.kr
`
`J.-P. Ryoo - C. Moon
`NAL Pharmaceuticals Ltd, Monmouth Junction, New Jersey,
`USA
`
`Donepezil is a centrally acting reversible acetylcholines-
`tearase inhibitor and exerts its
`therapeutic effect by
`increasing acetylcholine concentrations and enhancing
`cholinergic function (Rogers and Friedhoff 1998; Sugimoto
`et al. 1995). Commercially, donepezil
`is available in the
`form oftablet underthe trade nameAricept”.Initial dose is
`5 mg per day, which can be increased to 10 mg per day
`after an adjustmentperiod of at least 4 weeks (Rogerset al.
`1998). In mostof the cases, it is not convenient for patients
`suffering from Alzheimer’s disease (AD) to comply with
`the self-medication schedule. Moreover, various
`side
`effects including diarrhea, nausea, anorexia, and muscle
`convulsion are reported (da Silva et al. 2006). These
`adverse effects are mainly due to increase in gastric acid
`secretion caused by enhanced cholinergic activity through
`the gastrointestinal tract. Donepezil-nanoclay hybrids have
`been suggested to reduce the adverse effects of donepezil
`(Park et al. 2008). It was reported that clay used in the
`study could reduce the acidity by absorbing proton and
`control the drug release behavior. As an alternative to oral
`delivery, microparticles of donepezil as monthly subcuta-
`neous injection has been reported (Zhang et al. 2007). The
`microparticles were prepared using poly (p, L-lactide-co-
`glycolide) by an oil-water emulsion solvent evaporation
`technique. However, due to the better patient compliance,
`controlled delivery of drug, ease of administration as well
`as termination, a transdermal product of donepezil would
`be more appropriate in providing clinical benefit of pro-
`longed response to patients suffering from AD.
`However, due to the barrier function ofskin, not all drugs
`can be delivered transdermally (Subediet al. 2010). In many
`cases, the absorption maynotresult in sufficient plasma drug
`concentration. Various studies have been conducted, along
`with their pros and cons, to develop transdermal product
`of donepezil. Matrix based transdermal system has been
`
`a Springer
`
`0001
`
`Noven Pharmaceuticals, Inc.
`EX2021
`Mylan Tech., Inc. v. Noven Pharma., Inc.
`IPR2018-00173
`
`
`
`R. K. Subedietal.
`
`Methods
`
`Patch preparation
`
`Since patches prepared using salt form showed very low
`permeability (data not shown), donepezil hydrochloride
`was converted to the free base form using equimolar
`amount of sodium hydroxide. Differential scanning calor-
`igrams showedthat the melting point of donepezil hydro-
`chloride (230°C) was reduced to around 90°C after the
`conversion (Fig. 1). The drug solution was obtained by
`dissolving donepezil
`in ethyl acetate, and permeation
`enhancer(s) were added. Adhesive solution and drug
`solution were mixed andstirred sufficiently. The mixture
`wascast on release liner coated with silicone and solvent
`was removed by evaporation at 80°C for 20 min. Then the
`dried adhesive layer was laminated onto the backing
`membrane. The drug and enhancers are expressed as
`weight % with respect to dry PSA polymer throughout the
`article.
`
`Measurement of in vitro skin permeation rate
`
`Skin permeation rates of various donepezil/enhancer for-
`mulations were determined using flow through diffusion
`cells. Permeation experiments were done onisolated hairless
`mouse skin. A system comprising a multi channelperistaltic
`pump,a fraction collector, a circulating water bath and flow-
`through diffusion cells was used. Each flow-throughcell had
`two arms, which allowedthe receiver cell medium pumped
`to a fraction collector. The diffusion cell temperature was
`maintained at 37°C bycirculating water through the outer
`part of jacketed receiver cell. The surface area of receiver
`cell opening was 2 cm”,andits volume was 5.5 ml. Skin was
`excised from hairless mouse that was humanly sacrificed
`
`
`
`—— donepezil base
`sees donepezil HCL
`
`
`-
`r
`r
`:
`50
`100
`150
`200
`
`¢
`250
`
`0
`
`-23
`
`-24
`
`-25
`
`-26
`
`27
`
`-28
`
`Cc
`
`= 8
`
`E®
`
`= Q
`
`c
`uw
`
`Temp(°C)
`
`Fig. 1 Differential scanning calorimetric thermogram of donepezil as
`base and hydrochloride salt form
`
`reported for donepezil (Kazunosukeet al. 2008). However,
`to achieve the sufficient transdermal flux through hairless
`mouse skin, extremely high drug loading (35% w/w) was
`used. This may lead to crystallization of drug in the polymer
`matrix and may cause problem with adhesive force. Another
`study suggested the use of salt form that is converted to the
`base form in situ within the matrix type delivery system
`(Terahara etal. 2009). Salt form of donepezil precipitates in
`the adhesive matrix forming particles in the patch, which
`reducesthe aesthetic value of the patch. Reservoir type patch
`system was also described for delivery of Alzheimer’s
`pharmaceuticals, particularly donepezil (Walia and Rama-
`raju 2008). The matrix patchesare slimmer and smaller than
`the reservoir patch, and are preferred both in termsof ease of
`production and better patient compliance. Therefore, there is
`a need to explore a commercially viable transdermal matrix
`based system for donepezil which can give higher flux at
`lowerdrug load, through properselection of formulation and
`process variables.
`The present study was conducted to investigate the
`feasibility of developing stable matrix based transdermal
`system for donepezil.
`In vitro permeation studies were
`done
`to characterize passive diffusion with various
`adhesives and chemical enhancers. Effect of different
`
`formulation variables on permeation of donepezil was
`evaluated.
`
`Materials and methods
`
`Materials
`
`Donepezil hydrochloride was generous gift from Samil
`Pharmaceuticals
`(Seoul, South Korea). Polyglyceryl-3
`oleate (Plurol olieque® CC497), propylene glycol mono
`laurate (Lauroglycol), and polyoxy glycerate (Labrafil®
`1944) were obtained from Gattefosse (Paramus, NJ, USA).
`PEG sorbitan monooleate (Tween® 80), sorbitan monool-
`eate (Span® 80), propylene glycol (PG), oleyl alcohol was
`purchased from Junsei Chemicals (Japan). Isopropyl pal-
`mitate (IPP),
`isopropyl myristate (IPM), PEG-12 palm
`kernel glycerides (Crovol® PK40), and PEG-20 almond
`glycerides (Crovol® A40) were obtained from Croda
`(Parsippany, NJ, USA). Lauryl alcohol (R)-(+) Limonene,
`Brij” 30 and Brij” 52 were purchased from Sigma
`Chemical (St. Louis, MO, USA). Acrylic rubber hybrid,
`polyisobutylene
`(PIB)
`and
`styrene—butadiene—styrene
`(SBS) pressure sensitive adhesive (PSA)
`solutions
`in
`organic solvents were obtained from National Starch and
`Chemical Company (Bridgewater, NJ, USA). Silicone PSA
`was obtained from Dow Corning (Midland, MI, USA). All
`other chemicals were reagent grade or above and were used
`without further purification.
`
`g) Springer
`
`0002
`
`
`
`stability of the patches kept in refrigerator (2-8°C), room
`temperature (RT) and 40°C oven were monitored visually
`at different time intervals. Chemical stability was assessed
`using previously reported stability indicating analytical
`method (Hanatani et al. 2008). HPLC system (Shimadzu
`Scientific Instruments, MD), consisting of a UV detector
`(SPD-10A), reversed-phase C;g column (4.6 x 150 mm,
`5 pm, Shiseido), a pump (LC-10AD), and an automatic
`injector (SIL-10A) wasused. Briefly, the wavelength of the
`UV detector was 271 nm,
`the column temperature was
`maintained at 25°C,
`the flow rate was
`1 ml/min and
`injection volume was 20 ul. The mobile phase used con-
`sisted of sodium|-decansulfonate aqueous solution/Acet-
`onitrile/70% perchloric acid = 650/350/1 (volume ratio);
`sodium 1-decansulfonate concentration was 10 mM oftotal
`
`mobile phase.
`
`Results and discussion
`
`Selection of pressure sensitive adhesive matrix
`
`The effect of the PSA matrix on the permeation of do-
`nepezil was investigated using silicone, PIB, SBS, acrylic
`and acrylic rubber hybrid adhesive matrixes, Permeation
`profile of donepezil from various PSA matrices is shown
`in Fig. 2. Solubility of donepezil was found to be inad-
`equate in silicone and PIB adhesive matrices and some of
`donepezil was suspended in the matrix. The glass transi-
`tion temperature of PSA,interaction between the drug and
`functional group of PSA, adhesive force and many other
`properties can influence flux of drug from PSA across the
`skin (Hai et al. 2008; Venkatraman and Gale 1998). The
`permeation rate was lowest in the PIB matrix, followed
`
`.
`
`100
`
`em 300 —e— PIB
`5
`SeQeae
`SBS
`Sb
`---*—-- Acrylic non functional
`/
`= 250 a Acrylic hydroxy functional
`3 —-=—=Acrylic rubber hybrid /
`
`
`Differential scanning calorimetry (DSC)
`= 200
`——-o-— Acrylic carboxy functional
`/ -A
`2
`——*— Silicone
`Z a
`vo
`= 150
`veaaa
`§
`“of
`<™
`2
`AL ge
`=
`LL a Ua
`6
`z
`aoO gos
`a
`go oe
`sa
`=_
`E=
`
`v
`T
`20
`
`Transdermal drug delivery system for donepezil
`
`with diethyl ether. Subcutaneous fat was removed with
`scissors and scalpel. Each of the flow-through diffusion cell
`components was connected via silicone rubber tubing with
`an internal diameter of 0.015 inches. The receiver cell was
`filled with a pH 6 buffer solution and the media wasstirred
`by Teflon-coated magnetic bar. The prepared patch was
`placed on the stratum corneum and the excised skin was
`mounted onto each receiver cell. And O-ring and cell top
`wasplaced on the top of each skin. These components were
`then clamped. The amountof drug permeatedacrossthe skin
`was calculated from the cumulative release. The samples
`were collected every 4 h for 24 h and assayed by HPLC.
`
`Analytical method
`
`Donepezil was analyzed by HPLC system (Shimadzu
`Scientific Instruments, MD), consisting of a UV detector
`(SPD-10A), reversed-phase C,g column (4.6 x 100 mm,
`5 um, Gemini), a pump (LC-I0AD), and an automatic
`injector (SIL-10A). Briefly,
`the wavelength of the UV
`detector was 315 nm, the column temperature was main-
`tained at 30°C, the flow rate was | ml/min and injection
`volume was 10 ul. Mobile phase consisted of Acetonitrile/
`phosphate buffer 0.1 M with triethanolamine (0.01% v/v)
`adjusted to pH 2.7 with 85% phosphoric acid (30/70).
`
`Content analysis
`
`4 cm” patch samples were cut, and weighed. Release liner
`was separated and weighed. Backing membrane containing
`the matrix was transferred in 50 ml vial with screwed cap
`(Schott Duran). Then, 50 ml of HPLC grade methanol and
`teflon coated magnetic bar was added. The container was
`then capped and sealed with Parafilm®. Then, the samples
`were sonicated for 30 min followedby stirring for 12 h. The
`backing membrane was removedfrom the container, washed
`with ethyl acetate to remove the PSA matrix, and weighed.
`The solution wasfiltered through Whatman® nylon mem-
`branefilter (13 mm,0.45 tum) and analyzed by HPLC.
`
`Thermal analysis was carried out to characterize donepezil
`hydrochloride and base form, using a DSC unit (Pyris 6
`DSC, Perkin-Elmer, Netherlands).
`Indium was used to
`calibrate the temperature scale and enthalpic response.
`Samples were placed in aluminum pans and heated at a
`scanning rate of 5°C/min from 25 to 250°C.
`
`Stability
`
`25
`
`15
`
`1
`
`Stability studies of the optimized formulation were con-
`ducted at three different temperature conditions. Physical
`
`Fig. 2. Screening ofdifferent pressure sensitive adhesives at 10% w/w
`of drug load. Values are expressed as mean (n = 3)
`
`0003
`
`Q Springer
`
`Time(h)
`
`
`
`R. K. Subediet al.
`
`—— 60m
`—o— 85m
`—
`100 pm
`—— 120m
`
`J
`
`J
`AL
`
`9
`
`p
`
`
`
`—~ 500
`we
`9g
`2
`= 400
`
`Cumulativeamountpenetrated iS
`
`
`
`S
`
`=S
`
`
`
`by highly crossed linked acrylic adhesive containing
`carboxyl
`functional group, Duro-Tak® 87-2677. This
`could be due to the interaction between amine group of
`donepezil and carboxyl group of the adhesive. In previous
`study, low permeation rate of tacrine was observed due to
`the interaction between the amine group of tacrine and
`carboxyl group of acrylic adhesive (Kim et al. 2000).
`Permeation rate of donepezil in the acrylic rubber hybrid
`adhesive matrix, Duro-Tak® 87-502A was highest fol-
`lowed by silicone, Dow Corning BioPSA® 7-4302. Fur-
`ther study on different kinds of acrylic rubber hybrid
`adhesives containing hydroxyl functional group revealed
`that Duro-Tak® 87-504A provided higher flux for do-
`nepezil (Fig. 3). Permeation of donepezil from Duro-Tak”
`87-502A and 87-503A matrices was similar. Acrylic
`rubber hybrid PSAs are prepared from an acrylic polymer
`grafted with a hydrogenated rubber. The hybrid PSA
`comprises of polymer from ethylene-butylene macromer
`and hydroxyethyl acrylate monomer
`(Foreman et al.
`2003). Higher flux obtained for donepezil from acrylic
`rubber hybrid PSAs could be attributed to the suitable
`polar monomer favorably affecting the thermodynamic
`behavior of donepezil in the matrix (Cantor and Wirtanen
`2002).
`Since matrix thickness is an important functional char-
`acteristics of matrix based transdermal system,its effect on
`the permeation of donepezil was also investigated. Per-
`meation profile of donepezil was unchanged when matrix
`increased from 65 to 85 um (Fig. 4). However, further
`increase in matrix thickness resulted in lower permeation
`profile of donepezil. Matrix thickness of 85 j1m was chosen
`for further experiments based on better adhesive properties
`as compared to 60 um matrix.
`
`Time (h)
`
`Fig. 4 Effect of acrylic rubber hybrid matrix thickness on the
`permeation of donepezil. Values are expressed as mean (n = 3)
`
`Effect of enhancer
`
`To reversibly overcome the barrier properties of stratum
`corneum, penetration enhancers are commonly employed
`in the transdermal systems (Williams and Barry 2004).
`Enhancer screening was carried out with both Duro-Tak®
`87-502A and 87-504A matrices. Table | gives the sum-
`mary of enhancer screening at the level of 5% v/w with
`15% w/w drug load in Duro-Tak” 87-502A acrylic rubber
`hybrid matrix. Due to higher solubility of donepezil
`in
`Duro-Tak® 87-502A acrylic rubber hybrid matrix, drug
`load was increased to 15%. Brij” 30, Plurol olieque®
`
`Table 1 Summary of enhancer screeningat the level of 5% v/w with
`15% wiw drug load in Duro-Tak® 87-502A acrylic rubber hybrid
`matrix. Values are expressed as mean (n = 3)
`
`S. No.
`
`Enhancer
`
`1
`2
`3
`4
`
`5
`6
`7
`
`8
`9
`
`10
`11
`12
`
`13
`
`Control
`Brij” 30
`Plurol olieque” CC497
`Crovol® A 40
`
`Oley! alcohol
`Lauryl alcohol
`IPM
`
`Sugarester P-1670
`Limonene
`
`Span™ 80
`Transcutol”
`IPP
`
`Cineole
`
`ER*
`
`1.00
`2.10
`1.47
`1.32
`
`1.37
`1.34
`1.12
`
`1.33
`1.06
`
`1.25
`1.17
`1.17
`
`1.11
`
`:
`
`—e— 87-502 A
`Oe 87-503 A
`—-w-- 87-504 A
`
`¥
`
`“
`
`
`
`0
`
`5
`
`10
`
`15
`
`20
`
`25
`
`
`
`
`
`
`
`Cumulativeamountpenetrated(ug/em*)
`
`Time(h)
`
`Fig. 3 Screening of different rubber acrylic hybrid pressure sensitive
`adhesives at 15% w/w drug load. Values are expressed as mean
`(n = 3)
`
`1.09
`Labrafil® 1944
`14
`1.04
`Incrocas® 30
`15
`
`
`16 1.29 Brij” 52
`* ER enhancementratio
`
`g) Springer
`
`0004
`
`
`
`Transdermal drug delivery system for donepezil
`
`
`
`
`
`Cumulativeamountpenetrated(ug/em”)
`
`700 4
`
`60-4
`
`—e— 87-502 A, 5% Brij 30
`“Or 87-503A, 5% Brij 30
`
`©
`
`
`
`0
`
`5
`
`10
`
`15
`
`20
`
`25
`
`ratios in both Duro-Tak® 87-502A and Duro-Tak® 87-504A
`matrices and waschosenfor further experiments. Brij® 30 is
`a surfactant which belongs to the class of polyoxyethylene
`(POE)alkyl ethers. The EO chain length and HLB value of
`Brij® 30 is 4 and 9.7 respectively. Studies have shown that
`POEalkyl ethers containing EO chain length of 2-5 and
`HLBvalue 7-9 are effective promoters for the percutaneous
`absorption of drug molecules (Park et al. 2000). Brij® 30
`could efficiently disrupt the lipid arrangements in SC via
`both hydrophilic and lipophilic molecular mechanism,
`thereby enhancing the penetration of donepezil (Breuer
`1979; Walters et al. 1987).
`
`Time (h)
`
`Effect of combining enhancers
`
`Fig. 5 Permeation profile of donepezil at 15% drug load, in presence
`of5% Brij 30°, from Duro-Tak™ 87-502A and Duro-Tak™ 87-503A
`matrices. (n = 3)
`
`CC497, Crovol® A40, oleyl alcohol, lauryl alcohol, sugar
`ester P-1670, Span® 80 and Brij” 52 significantly enhanced
`the in vitro flux of donepezil from Duro-Tak® 87-502A
`matrix. The enhancing effect of Brij® 30 was compared
`between Duro-Tak® 87-502A and Duro-Tak® 87-503A. As
`can be seen in Fig. 5, no significant difference was observed.
`Table 2 gives the summary of enhancer screening at
`the level of 5% v/w with 10% w/w drug load in Duro-Tak®
`87-504A acrylic rubber hybrid matrix. Amongthe enhancers
`screened, Brij” 30, Brij” 52, IPM, glycerol and diethoxy-
`ethyl
`succinate were associated with the significant
`enhancing effect. Brij® 30 provided highest enhancement
`
`Table 2 Effect of penetration enhancers, at the level of 5% v/w, with
`10% w/w of drug load in Duro-Tak® 87-504A matrix. Values are
`expressed as mean (n = 3)
`S.
`Enhancer
`ERS.
`Enhancer
`ER
`No.
`No.
`
`To further increase the transdermalflux of donepezil, effect
`of combining selected enhancers at the level of 2.5% v/w
`with 5% v/w of Brij” 30 wasstudied. Especially for drug in
`adhesive type of TDDS, presenceof additives can modify the
`mechanical characteristics of PSA, and might make the
`adhesive more susceptible to creep/cohesive failure. Hence,
`adhesive propertiesof the patches containing combination of
`enhancers were also assessed manually using thumbtest.
`Table 3 provides the summary of results obtained using
`combination of Brij® 30 with selected enhancers in Duro-
`Tak® 87-502A matrix at 15% w/w drug load. Enhancement
`ratios were calculated using flux from Brij” 30 as control.
`Only combinations ofBrij® 30 with Brij® 52, Crovol® A40
`and Plurol olieque® CC497 were found to have higher
`enhancementratio as compared to Brij” 30 alone. Adhesive
`properties of patches containing combination of Brij® 30
`with Plurol olieque® CC497 or Span® 80 were foundto be
`unsatisfactory. Brij” 52 could be added upto 5% in addition
`to 5% Brij® 30 without impairing the adhesive property of
`the patch. Based on the flux and adhesion properties,
`
`Table 3 Summary ofthe results obtained using combination ofBrij”
`30 at the level of 5% v/w with selected enhancers at the level of 2.5%
`1.18
` Diisopropyl adipate
`14
`1.00
`Control
`1
`
`2~~BBrij® 30 1.70 15 Oley!oleate 1.11
`
`
`
`v/w in Duro-Tak® 87-502A matrix containing 15% w/w drug load.
`Values are expressed as mean (# = 3)
`
`
`
`3 16—LabrasolPlurol oleique™ 1.02 1.19
`CC497
`Combination of enhancers
`ER
`Adhesive
`property
`
`4
`
`Crovol® A 40
`
`—-:1.20
`
`17
`
`Tween® 80
`
`1.09
`
`0.97
`Limonene
`18
`1.11
`Oleyl alcohol
`5
`Brij” 30
`1.00
`Good
`
`
`
`6 Lauryl alcohol§0.94 19—Glycerol 1.24
`Brij” 30, Plurol olieque” CC497
`1.20
`Unsatisfactory
`7
`IPM
`1.22
`20
`Diisopropy! dirrerate
`1.13
`Brij® 30, Span” 80
`0.78
`8
` Span® 80
`1.17
`21
` Crovol® PK40
`Ll
`Brij” 30, Oleyl alcohol
`0.83
`9
`Transcutol®
`0.94
`22
`Hexyl Laurate
`1.17
`Brij” 30, Brij” 52
`1.37
`10
`IPP
`1.00
`23
`Octyl dodecyl ester
`0.99
`Brij® 30, Crovol® A40
`1.27
`
`
`
`
`11 24—Isotridecyl isononanoateCineole 1.07 0.99
`Brij® 30, IPP
`0.80
`12
`Brij® 52
`142
`25
`2-ethylhexyl
`1.05
`Brij® 30, Lauryl alcohol
`0.75
`hydroxystearate
`Brij” 30, Transcutol®
`0.70
` Diethoxylethyl
`succinate
`
`Brij® 30, Cineole
`0.81
`
`13.
`
`Alkyl 2-ethyl
`hexanate
`
`1.20
`
`26
`
`1.32
`
`Good
`
`0005
`
`Q Springer
`
`
`
`6 c
`
`ombination of Brij® 30 and Brij® 52, each at the level of 5%
`v/w, was selected for further studies.
`
`Effect of combination matrix
`
`Patches made with Duro-Tak® 87-504A showed superior
`adhesion properties to those formulated in Duro-Tak®
`87-503A or Duro-Tak® 87-502A matrix. It
`is because,
`among the acrylic rubber hybrid PSAs, only Duro-Tak®
`87-504A is tackified. However, highest drug loading was
`possible in Duro-Tak® 87-503A matrix. Drug loading
`capacity was studied using various levels of drug load in
`each matrix. The rank order obtained was Duro-Tak®
`87-503A > Duro-Tak® 87-502A > Duro-Tak® 87-504A.
`The level of drug loading up to which clear patches could
`be made determined the drug loading capacity of the
`matrix. Therefore, to obtain superior adhesion and perme-
`ation properties, combination of Duro-Tak® 87-503A and
`Duro-Tak” 87-504A matrix was studied. Benefit of mixing
`PSAs for the improvement of adhesion properties is a
`known art. Kanios described the combination of acrylic-
`based polymers with silicone-based polymers to optimize
`drug solubility and skin adhesion (Kanious 2006). Simi-
`larly,
`transdermal patch of
`tulobuterol
`formulated in
`polyethylene grafted acrylic polymer was mixed with
`acrylic adhesive containing hydroxyl functional group to
`improve the peeling off effect
`in the presence of water
`(Kim and Choi 2003). Adhesion of transdermal patch to the
`skin is an important factor directly related to drug delivery
`and therapeutic effects. Since drug absorption process is
`determined by partitioning of drug between TDDSand the
`skin, complete skin contact over the entire delivery surface
`for the labeled application period is essential (Wokovich
`et al. 2006). If the TDDSlifts off or partially detaches from
`the skin surface, it may lead to change of drug absorption
`in an unpredictable manner. In the worst case, it could lead
`to therapeutic failure. Drug load up to 10% w/w in Duro-
`Tak® 87-504A resulted in clear patches. Whereas, higher
`amount of drug could be loaded in Duro-Tak® 87-503A
`matrix without visible particles. Solutions of PSAs con-
`taining 10% w/w drug in Duro-Tak® 87-504A and 20% w/w
`drug in Duro-Tak® 87-503A were mixed at variousratios.
`Figure 6 shows the permeation of donepezil from such
`combination matrices. Based on the higher permeation
`profile obtained, 1:1 combination was selected for further
`study.
`The effect of drug loading in the combination matrix
`selected was also studied in the presence of combination
`enhancers. Figure 7 showsthe effect of drug loading on the
`permeation of donepezil from 1:1 combination of Duro-
`Tak® 87-503A and Duro-Tak® 87-504A matrix. As seen in
`the figure, permeation of donepezil increased linearly up to
`15% w/w drug load. Beyond that point
`the extent of
`
`g) Springer
`
`Fig. 6 Effect of combining Duro-Tak® 87-503A and Duro-Tak® 87-
`504A matrices at various ratios on the permeation of donepezil.
`Values are expressed as mean (7 = 3)
`
`
`
`Invitroflux(g/cm?)
`
`800
`
`700
`
`600
`
`500
`
`400
`
`300
`
`200
`
` T T T T T T
`
`1
`
`
`
`
`4
`6
`8
`10
`12
`14
`16
`18
`20
`22
`
`Drug loading (% w/w with respect to dry polymer)
`
`Fig. 7 Effect of drug loading, in presence of 5% v/w Brij® 30 and
`5% viw Brij® 52, on the permeation of donepezil
`from 1:1
`combination of Duro-Tak® 87-503A and Duro-Tak® 87-504A matrix.
`Values are expressed as mean (m = 3)
`
`increase was reduced, indicating the matrix is almost sat-
`urated with the drug.
`
`Stability
`
`In order to explore the commercial viability, stability
`studies were also conducted with the optimized formula-
`tion containing combination of Brij® 30 and Brij® 52, each
`at the level of 5% v/w with 15% w/w drug load in 1:1
`combination of Duro-Tak® 87-503A and Duro-Tak® 87-
`504A matrix. Patches were checked visually for any
`change during the study period. Chemical stability of the
`patches was check periodically by using stability indicating
`analysis method. Table 4 provides summary of the physical
`and chemicalstability testing. No change in morphology of
`
`0006
`
`
`
`
`
`
`
`4Cumulativeamountpenetrated(g/cm)
`
`R. K. Subediet al.
`
`—e 503A:504A (1:3)
`=O SORAS04A (1:1)
`—-w-- 503A:504A (3:1)
`
`a
`
`1
`
`go4oS
`
`:
`
`:
`
`: =
`
`
`
`0
`
`5
`
`10
`
`15
`
`20
`
`25
`
`Time(h)
`
`
`
`Transdermal drug delivery system for donepezil
`
`7
`
`Table 4 Summary of chemical and physicalstability of donepezil patch containing 15% w/w drug, 5% v/w Brij” 30 and 5%v/w Brij® 52 in 1:1
`
`combination matrix of Duro-Tak® 87-503A and Duro-Tak™ 87-504A, Values are expressed as mean + standard deviation (n = 3)
`
`Month
`
`Refrigerator
`
`1
`2
`3
`
`
`97.72:50
`95.5 + 1.99
`95.0 + 2.78
`
`Assay
`
`RT
`
`96.3 + 0.66
`96.1 + 2.42
`92.0 + 1.46
`
`40°C
`
`Physical stability
`
`96.4 + 3.62
`98.0 + 2.55
`94.4 + 3.42
`
`Refrigerator
`
`Clear
`Clear
`Clear
`
`RT
`
`Clear
`Clear
`Clear
`
`40°C
`
`Clear
`Clear
`Clear
`
`the patch was observed. At 3rd month, patches stored in RT
`showed slight decline in the assay value. However, during
`content analysis, no peak other than the peak of donepezil
`was observed. Chemical stability of patches stored in
`refrigerator and 40°C did not show significant decline in
`assay values during the study period of 3 months.
`
`Conclusion
`
`The obtained flux and the adhesive properties of the patch
`suggest
`that
`therapeutic amount of donepezil could be
`systemically delivered with a reasonable patch size. Con-
`sidering the half life of 70 h for donepezil and high initial
`flux obtained from the optimized formulation,
`it may be
`possible to transdermally deliver donepezil for an extended
`period of time. Based on daily dose of 4.6 mg and average
`flux of approximately 20 tg/cm7/h,less than 30 cm? active
`patch surface area is required to deliver therapeutic amount
`of donepezil for a period of 3 days through hairless mouse
`skin. However, the permeation rate of donepezil has not
`been compared between hairless mouse skin and human
`skin. Even if we assumethat the hairless mouse skin is two
`times more permeable than humanskin, it
`is feasible to
`develop multiple day transdermal drug delivery system for
`donepezil using a reasonable patch size.
`
`References
`
`Breuer MM (1979) The interaction between surfactants and kerati-
`nous tissues. J Soc Cosmet 30:41-64
`for
`Cantor AS, Wirtanen DJ
`(2002) Novel acrylic adhesives
`transdermal drug delivery. Pharma Technol N Am 26(1):28-38
`da Silva CHTP, Campo VL, Carvalho I, Taft CA (2006) Molecular
`modeling, docking and ADMETstudies applied to the design of
`a novel hybrid for treatment of Alzheimer’s disease. J Mol Graph
`Model 25:169-175
`Foreman PB, Shah SM, Chandran R, Eaton PS (2003) Rubber-acrylic
`adhesive formulation. US Patent No. 20030166767
`Hai NT, Kim J, Park E-S, Chi S-C (2008) Formulation and
`biopharmaceutical evaluation of transdermal patch containing
`benztropine. Int J Pharm 357:55-60
`Hanatani A, Sekiya J, Terashi S, Nishi S, Washiro S, Akemi H (2008)
`Stabilized donepezil-containing patch preparation. US Patent
`2008/0131490 Al
`
`Kanious D (2006) Device for transdermal administration of drugs
`including acrylic polymers. US Patent 2006/0078602 Al
`Kazunosuke A, Yasunari M, Takaaki T (2008) Transdermal absorp-
`tion patch. US Patent No. 2008/0138388 Al
`Kim B-D, Choi H-K (2003) Penetration enhancementof /'3-selective
`agonist, tulobuterol, across hairless mouse skin. J Kor Pharm Sci
`33:79-84
`
`Kim J-H, Cho YJ, Choi H-K (2000) Effect of vehicles and pressure
`sensitive adhesives on the permeation of tacrine across hairless
`mouse skin. Int J Pharm 196:105-113
`Nakanishi M, Terahara T, Michinaka Y, Aida K, Hattori W, Kuroda
`Takao (2009) Transdermally absorbable Donepezil Preparation.
`US Patent No. 20090175929A1
`Park ES, Chang SY, Hahn M, Chi SC (2000) Enhancing effect of
`polyoxyethylene alkyl ethers on the skin permeation of ibupro-
`fen. Int J Pharm 209:10-119
`
`Park JK, Choy YB, Oh J-M, Kim JY, Hwang S-J, Choy J-H (2008)
`Controlled release of donepezil intercalated in smectite clays. Int
`J Pharm 359:198-204
`Rogers SL, Friedhoff LT (1998) Long-term efficacy and safety of
`donepezil
`in the treatment of Alzheimer’s disease: an interim
`analysis of the results of a US multicenter open label extension
`study. Eur Neuropsychopharmacol 8:67-75
`Rogers SL, Farlow MR, Doody RS, Mohs R, Friedhoff LT (1998) A
`24-week, double-blind, placebo-controlled trial of donepezil in
`patients with Alzheimer’s disease. Neurology 50:136-145
`Subedi RK, Oh SY, Chun M-K, Choi H-K (2010) Recent advancesin
`transdermal drug delivery. Arch Pharm Res 33:339-351
`Sugimoto H, limura Y, Yamanishi Y, Yamatsu K (1995) Syntheses
`and structure- activity relationships of acetylcholinesterase
`inhibitors: 1-benzyl-4-[(5,6-dimethoxy-1-oxoindan-2-yl)methy]]
`piperidine hydrochloride and related compounds. J Med Chem
`38:48214829
`Terahara T, Kazunosuke A, Naruhito H, Shuji S$ (2008) Pharmaceu-
`tical preparation of percutaneous absorption type. US Patent No.
`20080 138388A1
`
`Valia KH, Ramaraju VS (2008) Transdermal methods and system for
`Alzheimer’s disease. US Patent No. 2008021113
`Venkatraman S, Gale R (1998) Skin adhesives and skin adhesion: 1.
`transdermal drug delivery systems. Biomaterials 19:1119-1136
`Walters KA, Walker M, Olejnik O (1987) Non-ionic surfactanteffects
`on hairless mouse skin permeability characteristics. J Pharm
`Pharmacol 40:525-529
`Williams AC, Barry BW (2004) Penetration enhancers. Adv Drug
`Deliv 56:603-618
`Wokovich AM, Prodduturi S$, Doub WH, Hussain AS, Buhse LF
`(2006) Transdermal drug delivery system (TDDS) adhesion as a
`critical
`safety, efficacy and quality attribute. Eur J Pharm
`Biopharm 64:1-8
`Zhang P, Chen L, Gu W, Xu Z, Gao Y, Li Y (2007) In vitro and in
`vivo evaluation of donepezil-sustained release microparticles for
`the treatment of Alzheimer’s disease. Biomaterials 28:1882-
`1888
`