`and Au/Si(100) Systems
`
`by
`
`Steven Naflel
`
`Graduate Program
`
`in
`
`Chemistry
`
`Submitted in partial fulfilment
`
`of the requirements for the degree of
`
`Doctor of Philosophy
`
`Faculty of Graduate Studies
`
`The University ofWestern Ontario
`
`London, Ontario
`
`July, 1999
`
`© Steven J. Nafiel 1999
`
`Reproduced with permission of the copyright owner. Further reproduction prohibited without permission.
`
`TSMC 1223
`
`TSMC 1223
`
`
`
`I * I
`
`National Library
`of Canada
`
`Bibliothéque naiionale
`du Canada
`
`Acquisitions and
`Bibliographic Services
`395 Wellington Street
`Ottawa ON K1A 0N4
`Canada
`
`'
`Acquisitions et
`servrces bibliographiques
`395. rue Wellington
`Ottawa ON K1A 0N4
`Canada
`
`.
`
`Yaurfile Volre re'la'wnce
`
`cams Not/9 reference
`
`The author has granted a non—
`exclusive licence allowing the
`National Library of Canada to
`reproduce, loan, distribute or sell
`copies of this thesis in microform,
`paper or electronic formats.
`
`L’auteur a accordé une licence non
`exclusive permettant a la
`Bibliothéque nationale du Canada de
`reproduire, préter, distribuer ou
`vendre des copies de cette these sous
`la forme de microfiche/film, de
`reproduction sur papier ou sur format
`électronique.
`
`L’auteur conserve la propriété du
`The author retains oWnership of the
`droit d’auteur qui protege cette these.
`copyright in this thesis. Neither the
`thesis nor Stibstantial extracts from it Ni la these ni des extraits substantiels
`
`may be printed or otherwise
`reproduced without the author’s
`permission.
`
`de celle—ci ne doivent étre imprimés
`ou aunement reproduits sans son
`autorisation.
`
`04612425464)
`
`Canad'éi
`
`Reproduced with permission of the COpyright owner. Further reproduction prohibited without permission.
`
`
`
`ABSTRACT
`
`This thesis encompasses studies of the electronic and physical structure of three transition
`
`metal interfaces with Si(lOO) substrates.
`
`The first case concerns a high resolution photoemission (PES) study of the initial stages (0
`
`to ~25 ML) of the formation of the Au/Si(100) interface at room temperature. The interface was
`
`V studied using Si 2p and Au 4f core-level PES, using synchrotron radiation. It was found that the Au
`
`and Si react immediately upon deposition to form a Au-Si phase. This initial Au-Si phase is seen to
`
`. change to a second Au~Si phase by 3.6 ML (1 ML = 6.78><1014 atoms/cmz) of Au mverage. As the
`
`coverage is increased a layer of the second Au-Si phase remains on the surface while pure Au layers
`
`form underneath it
`
`Second we report a Si 1:33;, Si K-, Co L3; and Co K—edge X.ray absorption near-edge
`
`structures (XANES) study of a series of cobalt and cobalt silicide thin films prepared by thermally
`
`annealing deposited Co layers on Si(lOO) substrates. By collecting both Total Electron Yield>(TEY)
`
`and Fluorescence Yield (FLY) XANES at the above edges we monitored the electronic and physical
`
`structural differences between films annealed under different conditions. It was found that the as
`
`deposited Co film exhibits noticeable intermixing at the Co-Si interface. The annealed films
`
`consisted of CoSiZ; however, both SiO2 and metallic Co were found in the near surface region of
`
`these films. The origin of the metallic Co remains undetermined.
`
`I
`
`Thirdly, we report a Si L323 Si K-, Ni L32; and Ni K-edge, TEY and FLY XANES study of a
`
`series of nickel and nickel silicide thin fih‘ns prepared by thermally annealing deposited Ni layers on
`
`Si( 100) substrates. The unannealed films again showed noticeable intermixing at the Ni-Si interface.
`
`The annealed Ni films produced primarily NiSi and NiSi2 films depending on the final annealing
`
`temperature. Using the XANES spectra from the Ni-Si blanket films as a reference we determined
`that Ni-Si sub-micron lines formed on Si(100) were predominantly NiSi; however, the corwersion of
`
`the Ni/Si system to a pure NiSi phase appeared to be affected by the line thickness, with the
`
`conversion becoming less complete as the lines become narrower.
`
`» Keywords: X—ray Absorption Near-Edge Structure, XANES, Photoemission Spectroscopy, PES,
`
`Silicide Thin Films, Electronic Structure, Physical Structure, Au/Si( 100), Nickel Silicide, Cobalt
`Silicide, Total Electron Yield, Flucrescence Yield.
`
`iii
`
`Reproduced with permission of the copyright owner. Further reproduction prohibited without permission.
`
`
`
`CO-AUTHORSHIP
`
`The following thesis contains material based on previously published manuscripts co-
`
`authored by Steven Nafiel, T. K. Sham, Ian Coulthard, YongFeng Hu, Martin Zinke-Allmang,
`
`D.-X. Xu, Suhit Das and L. Erickson. The eXperimental work and WIEN calculations
`
`presented in this thesis were preformed by Steven Nafiel, except as follows:
`
`Some of the photoemission data on clean silicon (100) and the fitting of the clean
`silicon spectra presented in the introduction of Chapter 3 were preformed by Dr. Detong
`
`' Jiang and were part ofunpublished work done in collaboration with Dr. Peter Norton.
`
`M. Zinke-Allmang provided one of the cobalt thin film samples examined in Chapter
`
`4. Jim Garret from the Materials Preparation Group at McMaster University provided the
`
`bulk CoSi2 saniple analysed in Chapter 4. The remaining cobalt silicide samples were
`provided by M. Saran ofNorthern Telecom. Some of the Si K-edge data of Chapter 4 was
`
`taken by YongFeng Hu, while, some ofthe Co K—edge data were taken by Ian Coulthard and
`
`T. K. Sham
`
`Dr. Suhit Das, D.-X. Xu and L Erickson provided the nickel silicide thin film and line
`
`samples analysed in Chapter 5. Some of the Ni K—edge data in Chapter 5 were taken by Ian
`
`Coulthard and T. K. Sham.
`
`For copyright releases see the Appendix.
`
`iv
`
`Reproduced with permission of the copyright owner. Further reproduction prohibited without permission.
`
`
`
`To Connie
`
`Reproduced with permission of the copyright owner. Further reproduction prohibited without permission.
`
`
`
`ACKNOWLEDGEMENTS
`
`First I would like to thank my supervisors Professor T. K. Sham and Professor P.
`
`K Norton without whose patience, encouragement and direction this work would not
`
`have been possible. Their optimism and vision have helped me through some difficult
`
`times. My gratitude for the commitment of their time and resources to this project can not
`
`be overstated.
`
`I want to acknowledge the people that helped me with some of the technical and
`
`experimental aspects of this work: Dr. Detong Jiang, Dr. Ian Coulthard, Dr. Kim Tan, Dr.
`
`YongFeng Hu, Dr. D.-X. Xu, Dr. S. R. Das, Dr. J. Garret, Dr. Keith Griffiths, Dr. John
`Tse, Dr. Dennis Krug, Dr. Martin Zinke-Allmang and
`Saran.
`
`I would also like to thank my lab mates: Dr. Mark Kuhn, Dr. Arthur Bzowski, Dr.
`
`Jian-Zhang Xiong, Dr. Ramaswami Sammynaiken. Thanks also to my friends who made
`
`student life bearable: Len Luyt, Jonathan Rochleau, Greg Canning, Marina Suominen—
`Fuller, Mike Scaini, Glenn Munro, Joy Munro, Claire Brown, Al Brown, Christine Brown,
`
`Nicki Curtis, Robin Martin, Alison Paprica and Paul Wiseman.
`
`Special thanks to my parents and brother for their patience, support and
`
`understanding in dealing with the eternal student.
`
`A very special thanks to Connie whose entrance into my life has encouraged and
`
`inspired me to do my best.
`
`Reproduced with permission of the copyright owner. Further reproduction prohibited without permission.
`
`
`
`TABLE OF CONTENTS
`
`CERTIFICATE OF EXAMINATION .
`.
`ABSTRACT
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.1 .
`
`CO—AUTHORSHIP .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`ii
`iii
`
`iv
`
`DEDICATION .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`. v
`
`. vi
`
`ACKNOWLEDGEMENTS .
`
`.
`
`.
`
`TABLEOFCONTENTS .
`LIST OF TABLES .
`.
`.
`.
`
`.
`.
`
`.
`.
`
`.
`.
`
`.
`
`.-.
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.'
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`. vii
`. x
`
`. xi
`
`LISTOFFIGURES .
`
`.
`
`.
`
`.
`
`CHAPTER 1: Introduction .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.‘
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`l
`
`. 7
`
`1.1
`
`References .
`
`.
`
`.
`
`.
`
`ECHAPTER 2: Theory and Experimental Techniques .
`2.1.
`Introduction
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`
`2.2
`
`X-ray absorption .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`.K
`
`.
`.
`
`.
`
`.
`.
`
`.l .
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.. .
`.
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`.
`
`.
`.
`
`. 9
`. 9
`
`. ..
`
`.
`.
`
`.
`.
`
`.
`.
`
`11
`
`11
`15
`
`2.2.1 X—ray absorption .
`.
`.
`.
`.
`2.2.2
`Sampling depth ofXAS .
`
`2.3
`
`2.4
`
`Photoemission Spectroscopy .
`
`Synchrotron Radiation .
`
`‘1.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`. 22
`
`, 24
`
`. 24
`
`2.4.1
`
`Introduction . .
`
`.
`
`.
`
`.
`
`2.4.2 Synchrotron sources
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`,.
`
`.
`
`. 25
`
`. 27
`
`2.4.3 Properties
`
`.
`
`.
`
`.
`
`.
`
`2.4.4 Monochromators .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`2.4.4.1 Grating monochromators
`
`2.4.4.2 Crystal monochromators
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`l
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`. 30
`
`. 32
`
`. 33
`
`vii
`
`Reproduced with permission of the copyright owner, Further reproduction prohibited Without permission.
`
`
`
`2.5
`
`2.6
`
`Calculation of Density of States
`
`Summary .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`. 35
`
`. 37
`
`. 39
`
`2.7
`
`References .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`CHAPTER3: The Gold on Silicon (100) Interface .
`
`3.1
`
`Introduction .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.‘
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`.
`.8.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`. 42
`
`. 42
`
`. 42
`. 43
`
`3.1.1
`Introduction .
`.
`.
`3.1.2 The Au/Si system .
`
`3.1.3 -Si(100) .
`
`3.2
`
`Experiment .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`. _
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`..
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`, 47
`
`. 56
`
`3.2.1 Experimental equipment
`
`3.2.2 Sample preparation .
`
`.
`
`Results and Discussion .
`.
`.
`.
`331 Si 2p core—leveldata .
`3.3.2 Difference spectra
`.
`.
`
`.
`
`.
`
`.
`.
`.
`
`.
`
`.
`
`.
`.
`.
`
`.
`
`.
`
`.
`.
`.
`
`.
`
`.
`
`.
`.
`.
`
`.
`
`.
`
`.
`.
`.
`
`.
`
`.
`
`.
`.
`.
`
`.
`
`.
`
`.
`.
`.
`
`.
`
`.
`.
`.
`
`.
`
`.
`
`.
`.
`.
`
`.
`
`.
`
`.
`.
`.
`
`.
`
`.
`
`.
`.
`.
`
`.
`
`.
`
`.. .
`
`.
`.
`.
`
`.
`.
`.
`
`.
`
`.
`
`.
`
`.
`.
`.
`
`.
`.
`
`.
`
`_
`
`.
`.
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`.
`
`.
`.
`
`. 56
`
`. 59
`
`. 60
`. 60
`. 65
`
`. 68
`. 72
`
`3.3
`
`3.4
`
`3.3.3 Au 4f core—level data .
`Conclusions
`.
`.
`.
`.
`.
`.
`.
`.
`.
`
`3.5
`
`References.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`CHAPTER 4: Cobalt Silicide Thin Films .
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`_
`
`.
`
`.
`
`.
`
`. 74
`
`. 77
`
`. 77
`
`4.1 '
`
`Introduction .
`
`4.2
`
`Samples
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`_
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`_
`
`.
`
`.
`
`.
`
`.
`
`.
`
`81
`
`83
`
`4.3
`
`4.4
`
`Experiment.
`
`.
`
`.,
`
`.
`
`.
`
`.
`
`.
`
`Results and Dichssion .
`
`.
`
`.
`
`.
`
`.
`
`4.4.1 SiLm-edge spectra .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`._ .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`,
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`. 88
`
`.
`
`88
`
`4.4.2 Co Liz-edge spectra
`
`4.4.3
`
`Si K~edge spectra .
`
`.
`
`4.4.4 CoK-edge spectra .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`. 94
`
`.
`
`101
`
`. ..
`
`106
`
`viii
`
`Reproduced with permission of the copyright owner. Further reproduction prohibited without permission.
`
`
`
`4.5 Conclusions.................. .
`4.6
`Calculations of Cobalt Silicides .
`.
`.
`.
`.
`.'
`.
`.
`.
`.
`
`4.7
`
`References .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`i .
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`. ..109
`.
`.
`. 110
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`114
`
`117
`
`CHAPTER 5: Nickel Silicide Thin Films
`
`5.1
`5.2
`
`Introduction .
`Samples
`.
`.'
`.
`
`.
`.
`
`.
`.
`
`.
`.
`
`.
`.
`
`.
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`117
`121
`
`122
`
`5.3
`
`5.4
`
`Experiment .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`Results and Discussion for Nickel Silicide Films
`
`5.4.1
`
`Si Liz-edge spectra.
`
`.
`
`.' .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`124
`
`124
`
`128
`
`5.4.2 Ni Liz—edge spectra .
`
`SiK-edge spectra” .
`5.4.3
`5.4.4 Ni K-edge spectra
`
`5.4.5 Conclusions
`Nickel Silicide Lines
`
`.
`.
`
`.
`.
`
`.
`.
`
`5.5
`
`.
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`.
`
`.
`
`.y .
`.
`.
`
`.
`.
`
`.
`.
`
`.
`.
`
`.
`.
`
`.
`.
`
`.
`.
`
`.
`.
`
`.
`.
`
`.
`.
`.1 .
`
`.
`.
`
`.
`.
`
`.
`.
`
`.
`.
`
`.
`.
`
`.
`.
`
`.
`.
`
`.
`.
`
`.
`.
`
`.
`.
`
`.
`.
`
`.
`.
`
`.
`.
`
`.
`.
`
`132
`136
`
`140
`141 '
`
`5.5.1
`
`Introduction .
`
`5.5.2 Experiment .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`141
`
`.. 141
`
`.
`
`142
`
`5.5.3 Results and Discussion .
`
`5.5.4 Conclusions
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`' .
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.5
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`.
`
`.
`.
`
`147
`
`147
`152
`
`5.6
`5.7
`
`Calculations of Nickel Silicides .
`References .
`.
`.
`.5 .
`.
`.
`.
`.
`.
`.
`
`CHAPTERG: Summary .
`
`.
`
`.
`
`.
`
`.
`
`e.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`;
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`_
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`155
`
`160
`
`APPENDIX .
`
`VITA .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`165
`
`ix
`
`Reproduced with permission of the copyright owner. Further reproduction prohibited without permission.
`
`
`
`LIST OF TABLES
`
`Table 2.1.
`
`Photon penetration depth and X—ray absorption sampling depth
`
`estimates .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`Table 2.2.
`
`Synchrotron radiation sources used for studies presented in this
`
`.
`
`.
`
`.
`
`.
`
`18
`
`. 29
`
`. 33
`
`Table 2.3.
`
`Table 3.1.
`
`Table 4.1.
`
`thesis .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.’ .
`
`.
`
`Beamlines used for work presented in this thesis .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`,
`
`.
`
`Core-level binding energy shifis of the components seen in the Si
`
`2p photoemission spectra of clean silicon .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`53
`
`. 81
`
`Important properties of the cobalt silicides .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`Table 4.2.
`
`Description and preparation conditions of the cobalt silicide
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`. 82
`
`.
`
`.
`
`.
`
`120
`
`121
`
`139
`
`Table 5.1
`
`Table 5.2.
`
`samples
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`Important properties of the nickel silicides .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`Description and preparation conditions of the nickel silicide thin
`
`film samples
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`Table 5.3.
`
`Measured X—ray absorption threshold shifts ofNiSi and NiSi2 .
`
`Reproduced with permission of the copyright owner. Further reproduction prohibited without permission.
`
`
`
`LIST OF FIGURES
`
`Figure 1.1.
`
`Periodic table showing the elements that form compounds
`
`with silicon .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`Figure 1.2.
`
`Schematic diagram of a CMOS logic device showing the use
`
`of silicides .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`Figure 1.3.
`
`Schematic diagram illustrating heat induced synthesis of thin
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`3
`
`. 4
`
`.
`
`5
`
`film transition metal silicides .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`Figure 2.1.
`
`Part of the electromagnetic spectrum covered by synchrotron
`
`radiation and a few of the research interests in this range .
`
`.
`
`.
`
`.
`
`.
`
`10
`
`Figure 2.2.
`
`Schematic diagram of the X-ray absorption process in transmission
`
`mode .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`Figure 2.3.
`
`Diagram illustrating X-ray absorption and photoemission spectra
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`10
`
`12
`
`'
`
`in metals .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`Figure 2.4. Ni K—edge X—ray absorption spectrum taken in total electron
`
`yield mode showing the pre—edge, whiteline, XANES and
`
`EXAFS regions
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`Figure 2.5. Mechanisms for the decay of a core-hole after the absorption
`
`of an X—ray photon .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`Figure 2.6.
`
`Schematic diagram of the geometry of Total Electron Yield and
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`13
`
`l6 ‘
`
`16
`
`Fluorescent yield X-ray absorption detection modes
`
`.
`
`.
`
`.
`
`.
`
`.
`
`Figure 2.7.
`
`Plot of the universal curve for the mean free path of electrons in
`
`solids as a fimction of the kinetic energy of the electrons (Ex)
`
`2.
`
`.
`
`19
`
`Figure 2.8.
`
`Schematic diagram of electron production in a solid after the
`
`absorption of a photon .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`_
`
`.
`
`.
`
`Figure 2.9.
`
`Schematic diagram illustrating the photoemission process
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`. 20
`
`. 22
`
`Figure 2.10. Representation of a synchrotron storage ring showing the major
`
`components
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`. 26
`
`Reproduced with permission of the copyright owner. Further reproduction prohibited without permission,
`
`
`
`Figure 2.11. Bending magnet flux of the SRC storage ring under two typical
`
`operating conditions .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`,
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`. 29
`
`Figure 2.12. Schematic ofthe CSRF Grasshopper beamline located at SRC .
`
`. 31
`
`Figure 2.13. Schematic of a typical Double Crystal Monochromator beamline . 34
`
`Figure 2.14. Partitioning of the unit cell into atomic spheres and an interstitial
`
`region _
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`. 36
`
`. 44
`
`Figure 3.1.
`
`The Au-Si phase diagram .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`Figure 3.2.
`
`General picture of the Au/Si interfacial structure .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`. 46
`
`Figure 3.3.
`
`The Miller indices of three common crystal planes. The diamond
`
`structure of crystalline silicon. The atomic arrangement of atoms
`
`for the ideal Si(111) and Si(100) crystal planes .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`. 48
`
`Figure 3.4.
`
`Simplified views of the unreconstructed Si(100) surface and the
`
`reconstructed Si(lOO)-2><1 surface .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`Figure 3.5.
`
`Si 2p core-level spectra of a clean Si(100)~2><1 surface and
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`. 49
`
`. 52
`
`representative fitting components .
`
`.
`
`.
`
`.
`
`Figure 3.6.
`
`Si 2p core-level spectra of the clean Si(lOO)—2><l surface .
`
`Figure 3.7.
`
`Comparison of two Si 2p core-level spectra taken from the
`
`front side and the back side of the same sample .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`. 54
`
`. 55
`
`Figure 3.8.
`
`Schematic diagram of the PES experimental chamber, the important
`
`analytical devices and the sample mount used to study the
`
`Au/Si(100) system .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`_
`
`. 57
`
`Figure 3.9.
`
`1 MeV He+ Rutherford Backscattering Spectrum of the 3.6 ML Au
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`. 58
`
`covered Si(100) wafer
`
`.
`
`.
`
`.
`
`.
`
`Figure 3.10.
`
`Si 2p core-level spectra of clean Si(100) and Au covered Si(100)
`
`taken at a photon energy of 130 eV .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`. 61
`
`Figure 3.11.
`
`Si 2p core-level spectra of clean Si(lOO) and Au covered Si( 100)
`
`taken at a photon energy of 160 eV .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`Figure 3.12. Difference between 3.6 ML and 0.36 ML Au covered and clean
`
`Si(100) spectra .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`. 64
`
`. 66
`
`xii
`
`Reproduced with permission of the copyright owner. Further reproduction prohibited without permission.
`
`
`
`Figure 3.13. Au 4f core~level spectra of clean and Au covered Si(lOO) taken at
`
`a photon energy of 160 eV and 130 eV .
`
`.
`
`Figure 3.14. Representative fits to the core—level data .
`
`Figure 4.1.
`
`The Co-Si phase diagram .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`. 69
`
`. 70
`
`. 79
`
`Figure 4.2.
`
`Schematic of the basic Co-Si thin film structure‘before and after
`
`Figure 4.3.
`
`' annealing .
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`Schematic diagram of the eitperimental XANES setup on
`
`beamline X1 l—A and the He amplified TEY detector .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`Figure 4.4.
`
`Schematic. diagram ofthe experimental XANES setup on the
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`. 82
`
`. 84
`
`. 86
`
`. Canadian DCM and the channel plate fluorescence detector
`
`Figure 4.5.
`
`Schematic diagram of the experimental XANES setup on the
`Canadian Grasshopper beamline and the Au mesh Io detector .
`
`Figure 4.6.
`
`Si L3_2~edge spectra of a Si(lOO) wafer in both TEY and FLY
`
`detection modes
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`. 87
`
`. 90
`
`Figure 4.7.
`
`Si Lag-edge spectra of the Co-Si thin films, CoSi2 and Si(lOO) taken
`
`in TEY‘mode .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`. 92
`
`Figure 4.8.
`
`Si Liz-edge spectra of the Co—Si thin films, CoSiZ and Si(lOO) taken
`
`.
`
`.
`
`,
`
`.
`
`.
`
`.
`
`. 93
`
`inFLYmode.
`
`.
`
`.v
`
`,
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`Figure 4.9.
`
`Co Lifedge spectra of the Co-Si films and CoSi2 taken in FLY
`
`mode .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`Figure 4.10. Co Liz—edge spectra of the Co-Si films and CoSiz taken in TEY
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`. 95
`
`. 98
`
`mode .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`Figure 4.11. Subtraction of scaled bulk CoSi2 spectra fi'om the TEY spectra
`
`of the annealed Co—Si films, compared to the TEY spectrum of
`
`the unannealed film ;
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`._ .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`. 99
`
`Figure 4.12.
`
`Si K—edge spectra of the Co-Si films, Si(lOO) and CoSi2 taken in
`
`FLYmode .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`. ..
`
`102
`
`Figure 4.13.
`
`Si K-edge spectra of the Co—Si films, Si( 100) and CoSi2 taken in
`TEY mode .
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`,
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.V
`.
`.
`
`.
`
`104
`
`xiii
`
`Reproduced with permission of the copyright owner. Further reproduction prohibited without permission.
`
`
`
`Figure 4.14.
`
`Comparison of Si K—edge spectra of CoSi2 taken in different
`
`detection modes and sample preparation conditions
`
`.
`
`.
`
`.
`
`.
`
`.
`
`Figure 4.15.
`
`C0 K—edge spectra of the Co-Si films and CoSi2 taken in TEY
`
`mode
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`,
`
`.
`
`.
`
`.
`
`.
`
`Figure 4.16.
`
`Comparison of TEY and FLY Co K-edge spectra for Co-Si (4)
`
`Figure 4.17.
`
`Schematic of the structure of the studied Co—Si films .
`
`.
`
`.
`
`.
`
`Figure 4.18.
`
`Calculated total and partial densities of states for COZSi, CoSi
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`_
`
`.
`
`.
`
`.
`
`.
`
`105
`
`107
`
`108
`
`110
`
`111
`
`and 03312 .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`Figure 4.19.
`
`Comparisons of CoSi2 data and calculations
`
`_
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`113
`
`Figure 5.1.
`
`Figure 5.2.
`
`The Ni-Si phase diagram .
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`Schematic ofthe basic nickel silicide thin film structure before and
`
`118
`
`afier annealing .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`122
`
`Figure 5.3.
`
`Si Liz—edge XANES spectra of the Ni-Si films and Si(100) taken in
`TEY mode .
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.2
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`
`125
`
`Figure 5.4.
`
`Si Liz-edge spectra of the Ni-Si films and Si(100) taken in FLY
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`_
`
`.
`
`127
`
`mode .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`Figure 5.5.
`
`Ni Liz-edge spectra of the Ni-Si films and Ni foil taken in TEY
`
`mode .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`Figure 5.6.
`
`Ni L—edge whiteline difference curves between Ni foil and the
`
`nickel silicides
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`Figure 5.7.
`
`Ni L3_2—edge spectra of the Ni~Si films and Ni foil taken in FLY
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`,
`
`.
`
`129
`
`131
`
`133
`
`mode .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`Si K—edge spectra of the Ni-Si films, Ni foil, and both clean and v
`ambient Si(100) taken in TEY mode .
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`
`Si K-edge spectra for nickel silicide film Ni—Si (3) and Ni—Siv(4)
`and comparison with NiSi and NiSi2 spectra .
`.
`.
`.
`.
`.
`.
`.
`.
`
`.
`
`.
`
`.
`
`_
`
`134
`
`137
`
`138
`
`_ 140
`
`.
`
`.
`
`.
`
`Figure 5.8.
`
`Figure 5.9.
`
`Figure 5.10.
`
`Ni K-edge spectra of the Ni-Si films and Ni foil taken in TEY
`
`mode .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`Figure 5.11.
`
`Schematic of the structure ofthe studied Ni-Si films
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`Xiv'
`
`Reproduced with permission of the copyright owner. Further reproduction prohibited without permission.
`
`'
`
`
`
`. Figure 5.12.
`
`Figure 5.13.
`
`Schematic diagram of the silicide lines on Si(100)
`.
`.
`.
`.
`.
`.
`.
`.
`Ni Liz-edge spectra of the Ni—Si films, Ni lines and Ni foil taken in
`
`142
`
`TEY mode .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`143
`
`Figure 5.14.
`
`N1 Liz-edge spectra of the Ni-Si films, Ni lines and Ni foil taken in
`
`FLY mode .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`- .
`
`.
`
`.
`
`.
`
`.
`
`Figure 5.15.
`
`Ni Ls-edge XANES spectra of the Ni—Si lines compared to the
`
`spectra for NiSi in both TEY and FLY .
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`.
`
`Figure 5.16.-
`
`Calculated tetal and partial densities of states for NiZSi, NiSi and
`
`Figure 5.17.
`
`Figure 5.18.
`
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`.
`NiSi2 .
`Comparisons ofNiSiz data and calculations .
`Comparisons ofNiSi data and calculations .
`.
`
`.
`.
`.
`
`.
`.
`.
`
`.
`.
`.
`
`.
`.
`.
`
`.
`.
`.
`
`.
`.
`.I
`
`.
`.
`.
`
`.
`.
`.
`
`.
`.
`.
`
`.
`
`.
`
`.
`.
`.
`
`145
`
`146
`
`148
`150
`151
`
`Reproduced with permission of the copyright owner. Further reproduction prohibited withOut permission.
`
`
`
`CHAPTER 1: INTRODUCTION
`
`Metal silicides were studied formany years before the advent of silicon based solid
`
`state electronics. The growing dependence of our society on silicon based electronic
`
`devices has made the properties of silicon compounds of prominent importance to our
`
`present and fiJture.
`
`i
`
`Metal silicides first attracted attention at the turn of the century after the
`
`development of the electric fumace by H. Moissan [1]. The development of the fiJmace
`
`allowed various silicides to be systematically prepared at about this time. The early
`
`studies of silicides generally focused on understanding the physical properties of silicides
`in terms of their electronic and crystal structures. Other studies were stimulated by the
`
`high temperature stability of many refractory silicides [2].
`
`In the 1960's, M. P. Lepselter
`
`-
`
`[3] at Bell Laboratories pioneered the use of silicides as Schottky barriers. Silicide studies
`
`since have focused on the use of metal silicides in integrated circuit technology. See
`
`[2][4][5][6][7][8][9] for reviews. Such a focused effort has produced large volumes of
`
`information on the thermodynamic, kinetic, physical, and electrical properties of most of
`
`the silicides. Although the majority of studies have been centered on the device
`characteristics and usefulness of metal silicides, silicides have also been studied as model
`
`systems for binary alloy formation in thin films [10] and interfacial reactions [11].
`
`Perhaps no other industry drives itself to improve its products as fast as the
`
`semiconductor industry. Since Gordon Moore’s famous talk at the International Electron
`
`Devices Meeting (IEDM) in 1975, the industry has met or bettered his predicted growth
`
`rate in chip complexity (and decreased minimum feature size)[12]. Moore predicted a
`
`growth in chip complexity by a factor of two every year, now called Moore’s law.
`
`In
`
`Reproduced with permission of'the copyright owner. Further reproduction prohibited without permission.
`
`
`
`order to better define the trends in increasing complexity and identify the technological
`
`advances necessary to continue the trends, the Semiconductor Industry Association
`
`introduced the National Technology Roadmap for Semiconductors [13] in 1992 (with
`
`revised editions in 1995 and 1997). The roadmap has succeeded in driving innovations in
`
`the industry even faster, as companies compete to be the first to meet the projected
`
`guidelines for new architectures. As a result, more recent studies [l4][15][l6][17] of
`
`metal silicides have focused on meeting the challenges posed by the ever decreasing
`
`dimensions and complexity of ultra large scale integration (ULSI).
`
`More than half the elements in the periodic table form compounds with silicon (see
`
`Figure 1.1). The transition metals form a large number of silicides of various
`
`compositions, with most metals forming more than three stable compounds However,
`
`not all of the compounds seen in the bulk phase diagrams form in the thin film regime.
`
`The technically useful silicides fall into three main groups: the metal rich silicides MXSi, the
`
`monosilicides MSi, and the disilicides MSiz. The most important'of these have been the
`disilicides.
`_
`i
`'
`'
`Silicides have found applications in integrated circuit technology as: interconnects,
`
`ohmic contacts to source, drain and gate in CMOS (Complementary Metal Oxide
`
`Semiconductor) devices, see Figure 1.2, Schottky barrier devices, and more recently, as
`
`difliision barriers along Al metal interconnects. In order to be useful in these applications
`
`a compound must, in general: have good conductivity, be compatible with current
`
`manufacturing techniques and be reliable [2][15][l8]. These three conditions can entail:
`
`low resistivity, high temperature stability, ease of formation, ability and ease of patterning,
`
`minimal junction penetration, no reaction with other metals or silicon oxide layers, good
`
`adhesion to other layers and resistance to electromigration [2][18]. Certainly no silicide
`
`can meet all these conditions.
`
`The wide variety of compounds, complex phase transitions and the needto satisfy
`
`such a large set of conditions to obtain good‘device performance, has driven the
`
`fundamental investigations into metal silicides. This has generated a large body of
`
`knowledge about the properties of metal silicides. Research has especially focused on
`
`Reproduced with permission of the copyright'owner. Further reproduction prohibited without permission.
`
`
`
`
`HHHHEHHHHHIHHH:
`IIIIIIIIIHEHIH
`
`
`
`.2023"EBmgscsacn.5:885385299.35%9239:55;._J3:3”.
`
`
`
`
`
`Reproduced with permission of the copyright owner. Further reproduction prohibited without permission.
`
`
`
`— Metal Silicides
`
`A1 interconnects
`
`-WW studs
`
`
`
`
`
`
`
`
`Metal
`
`SSS
`VII/A
`
`SiO2 layers
`
`
`
`
`
` ‘\
`
`
`
`
`
`
`
`
`
`
`s
`
`Figu rc 1.2.V Schematic diagram ot‘a CMOS logic device showing the use ot‘silicides.
`
`those metals which were found to have good compatibility with the conditions of
`
`integrated circuit (IC) manufacture, namely Pt, Pd, W, Mo, Ti, Co, Ni and Ta [18].
`In general, a CMOS device, such as the one schematically represented above, has
`
`between 3 and 5 interconnect layers above the transistors. Currently such devices are
`produced with a minimum feature size (approximately the width of the gate) of 0.25 pm.
`
`i
`
`In 0.25 pm technology the source and drain are about 60 nm deep and the gate oxide is
`
`about 4—5 nm thick [19]. The semiconductor industry plans to reach a minimum feature
`size of 0.18 pm by the end of 1999 and a minimum feature size of 0.07 pm by the year
`
`'
`2009[19].
`Research on the metal silicides used in industrial processes has mainly focused on
`
`the overall device performance. However, as the minimum feature size of solid state
`
`transistors moves toward 0.1 pm, problems associated with the properties of the
`
`interconnects and contacts, such as parasitic resistance and capacitance [5][18], as well as
`
`problems associated with the control of reactions in thin films, such as junction penetration
`
`Reproduced with permission of the copyright owner. Further reproduction prohibited without permission.
`
`
`
`5
`
`[5][9][20], have become the most prominent challe