`United States Patent [11] 3,617,824 .
`
`
`
`
`
`(72]
`
`
`[32] Priority
`
`[33]
`[31]
`
`
`
`
`
`Inventors Daizaburo Shinoda;
`
`
`
`
`
`
`Masaoki Ishikawa; Hiroki Muta; Shizuo
`haan Nobuo Kawamura,all of Tokyo,
`
`
`
`
`
`
`[21] Appl. No. 743,900
`
`
`
`
`.
`[22] Filed
`July 10, 1968
`
`
`
`
`
`
`
`
`
`[45] Patented Nov. 2, 1971
`{73} Assignee Nippon Electric Company, Limited
`
`
`
`
`
`
`Tokyo, Japan
`
`
`
`
`
`July 12, 1965
`Japan
`
`42/79,658
`
`[56]
`References Cited
`
`
`
`UNITED STATES PATENTS
`
`
`
`3,381,182
`4/1968 Thorton...
`
`
`
`
`3,287,612 11/1966 Lepselter..
`
`
`
`
`vee
`9/1968 Lehman...
`3,402,081
`
`
`
`.
` Polinsky 0...ese
`3,336,661
`8/1967
`
`
`
`3,460,003
`8/1969 Hampikian
`ee eenereerress
`aa
`
`
`
`
`3/1969 Ruggerio.seaeseeecensenevaseees
`3,434,020
`
`
`
`
`Primary Examiner—John W. Huckert
`
`
`
`Assistant Examiner—Martin H. Edlow
`
`
`
`Attorney—Hopgoodand Calimafde
`
`
`
`
`
`
`317/234
`
`317/235
`
`148/188
`
`29/589
`
`317/234
`
`317/235
`
`
`
`
`
`[54] MOS DEVICE WITH A METAL-SILICIDE GATE
`
`
`
`
`3 Claims, 7 Drawing Figs.
`
`
`
`
`
`[82] U.S. Chae eentcccsserassearecerscensnneeevennee 317/235 R, ABSTRACT:A semiconductor device obtains in whichasili-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`317/235 B, 317/235 AG, 317/234 L
`cide film of 3d, 4d and Sd transition metal such asiron (Fe),
`
`
`
`
`
`
`
`
`
`
`Int. Ch...Lane saeesanseeccsccencnersensnenseessarsanees HOM11/14
`cobalt (Co), nickel (Ni), molybdenum (Mo), palladium (Pd),
`[51]
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`platinum (Pt), or the like, is used as a conductive meansin
`117/212,
`[50] Field of Search..........c.cccccscccssesssssonsesseenes
`
`
`
`
`
`
`
`
`
`
`
`
`
`place of the conventional simple metal and whose structure is
`106 A; 317/234 (5.2), 234 (5.4), 235 (21.1), 235
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`semiconductor-insular-silicide.
`(46), 235 B, 235 AG, 234L
`
`
`
`
`
`
`
`
`
`
`
`Page 1 of 6
`
`TSMCExhibit 1003
`
`TSMC Exhibit 1003
`
`Page 1 of 6
`
`
`
`PATENTEDOV 2
`
`Isr
`
`(3,617,824
`
`
`
`
`
`[LLL
`
`
`
`LSSADSESSKKKRes
`
`
`
`
`SKCeaeSe
`G
`FEN.PREan FIG.7.
`veCY
`
`
`
`
`
`DAIZABURO LNTORS
`|
`
`Nn
`MASAOK 4SH1AWA
`
`
`
`
`INVENTOR
`
`M/ROK! MUTA
`SHIZUO ASANABE
`NOBUO WAWAMURA
`
`BY
`
`Page 2 of 6
`
`ATTORNEYS
`
`Page 2 of 6
`
`
`
`
`lative layers formed in contact with each other over the sub-
`
`
`
`
`
`
`
`
`
`
`strate should have excellent adhesive property, heat- and
`
`
`
`
`
`
`
`
`
`
`
`
`
`shock- resisting property, adaptability to photomask-etching
`
`
`
`
`
`
`
`process, and stability against various electrical conditions to
`
`
`
`
`
`
`which the substrate is subjected in processing. According to
`
`
`
`
`
`
`
`
`the common process of manufacturing the LSI device, theal-
`
`
`
`
`
`
`
`
`
`kaline (mostly sodium) ions, which enter into the insulative
`
`
`
`
`
`
`
`film (silicon dioxide layer) in the process of evaporation or
`
`
`
`
`
`
`
`
`
`sputtering metal layer to form the conductive layer over the
`
`
`
`
`
`
`
`
`insulative film, adversely affect the electrical stability of boun-
`
`
`
`
`
`
`
`
`
`
`dary layers between the silicon substrate and the oxide film.
`
`
`
`
`
`
`
`
`The deterioration in the boundary layer adversely affects the
`reliability of the LSI device the same as the MOS-type device.
`
`
`
`
`
`
`
`
`
`Also,
`in the conventional structure of the LSI device,
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`neither aluminum nor molybdenumis satisfactory to form the
`
`
`
`
`
`
`
`
`layer, because the former easily deteriorate in the
`metal
`
`
`
`
`
`
`
`
`processof forming thereoverthe oxide insulative layer and the
`
`
`
`
`
`
`latter is insufficient in its adhesive and contacting property.
`For these reasons, it has been difficult to provide the LSI
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`devices of high reliability, which satisfy the above-mentioned
`
`requirements.
`
`
`
`
`
`
`
`Anobjectof the present invention is therefore, to provide a
`
`
`
`
`
`
`
`
`highly stable and highly reliable semiconductor device satisfy-
`
`
`
`
`
`ing all of the requirements mentioned above.
`SUMMARYOFTHE INVENTION
`
`
`
`
`1
`MOS DEVICE WITH A METAL-SILICIDE GATE
`
`
`
`
`
`BACKGROUNDOF THE INVENTION
`
`
`
`This invention relates to a semiconductor device having a
`
`
`
`
`
`
`
`semiconductor substrate, an insulator film formed over one
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`major surface of the substrate, and a conductive layer
`
`
`
`
`deposited on the insulatorfilm.
`
`
`
`
`
`
`Recently it has been necessary to develop semiconductor
`
`
`
`
`
`
`
`for producing highly reliable and effective
`techniques
`semiconductor devices, which are miniaturized modified for
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`higher frequency use, and subjected to the large-scale integra-
`
`
`
`
`
`
`
`
`tion. To provide the desired highreliability, a sufficiently heat-
`resistive and stable ohmic contact, PN junction, Schottky bar-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`rier and/or conductive layer should be unfailingly produced.
`For this purpose,
`is important to stabilize the contact
`it
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`between semiconductor elementandinsulatingfilm; insulator
`film and conductive film; and conductive film and lead wire.
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`From this point of view, the conductor used for ohmic contact
`
`
`
`
`
`should satisfy the following requirements:
`1. Good adherence and low contact resistance to the
`
`
`
`
`
`
`
`
`semiconductorsilicon (Si).
`
`
`
`2. Good adherence to the insulating film such assilicon
`
`
`
`
`
`
`
`dioxide (SiO,) orsilicon nitride (Si,N,).
`
`
`
`
`
`
`
`
`
`
`3. Adaptability to the photomask-etching process.
`4. Availability to provide stable bonding to gold (Au) which ,
`
`
`
`
`
`
`
`
`is used for the lead wire.
`
`
`
`
`
`
`
`
`
`
`
`
`
`Conventionally, aluminum (Al) is the most commonly used
`Accordingto this invention, a semiconductor device obtains
`
`
`
`
`
`
`metal for the ohmic contact of a semiconductor device. How-
`
`
`
`
`
`
`
`
`in whichasilicide film of 3d, 4d and 5d transition metal such
`
`
`
`
`
`
`
`
`
`30
`
`ever, there are two rather severe problemsassociated with the
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`as iron (Fe), cobalt (Co), nickel (Ni), molybdenum (Mo),
`
`
`
`
`
`
`
`use of aluminum thoughit satisfies requirements (1) through
`palladium (Pd), platinum (Pt), or thelike, is used as a conduc-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`(a). One of them is caused by the fact that an aluminum layer
`
`
`
`
`
`
`
`
`
`tive means in place of the conventional simple metal and
`
`
`
`
`
`
`
`
`
`forms a high-resistance alloy with the gold lead wire, which
`whose structure is semiconductor-insulator-silicide.
`In the
`
`
`
`
`
`adversely effects the ohmic contact. Therefore, aluminum is
`
`
`
`
`
`
`
`present invention, it is found that the silicide of transition
`
`
`
`
`
`
`
`
`
`not sufficiently suited for use in a highly reliable ohmic con-
`
`
`
`
`
`
`
`
`
`metal forms an excellent ohmic or Schottky barrier contact
`
`
`
`
`
`
`
`tact.
`
`between itself and silicon and -has good adherenceto silicon,
`
`
`
`
`
`
`
`
`
`Recently, a method of forming an ohmic contact has been
`
`
`
`
`
`
`
`silicon dioxide, silicon nitride and so on. Also thesilicide has
`
`
`
`
`
`
`
`
`
`
`developed which avoid those problems in the use of alu-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`the low resistivity and adaptability to photomask etching, and
`minum. The process contains the following steps: After heat
`
`
`
`
`
`
`
`
`
`it does not cause a deterioration in the electrical characteristic
`
`
`
`
`
`
`
`
`treatment, a platinum silicide is formed in the boundary layer
`
`
`
`
`
`
`
`ofthe insulator film in the forming process ofsilicide onto the
`
`
`
`
`
`
`
`
`
`
`on the silicon substrate. The nonreacted part of platinum is
`
`
`
`
`
`
`
`
`insulator.
`
`removed therefrom by chemical treatment and, then titanium
`
`
`
`
`
`
`
`Therefore the semiconductor device is thus characterized in
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`(Ti) and platinum are sputtered thereon and gold is deposited
`that thesilicide forms good contact to semiconductor,thesili-
`
`
`
`
`
`
`
`
`
`
`
`
`thereto by electrolytic plating.
`cide-insulator-semiconductor characteristics is extremely sta-
`
`
`
`
`is possible to provide a
`it
`According to this method,
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`ble and the manufacturing processis simple. This the present
`semiconductor device which has highly stable and reliable
`
`
`
`
`
`
`
`
`invention is applicable to planar-type semiconductors,field ef-
`
`
`
`
`
`ohmic contacts as compared with the method using aluminum.
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`fect semiconductorsof the insulated gate type, and large-scale
`However,this methodis inevitably complicated andit is rather
`
`
`
`
`
`
`
`
`integrated circuits having a multilevel interconnection struc-
`
`
`
`
`
`
`difficult to realize a mass-production system.
`
`
`
`
`ture.
`
`On the other hand,
`in order to obtain a semiconductor
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`The present invention will be explained in particular con-
`device having a Schottkybarrier, the metallic film should have
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`junction with the accompanying drawings.
`such propertythat (1') it is easily and well bondedtosilicon
`
`
`
`
`
`
`
`
`
`
`FIG. 1 is a longitudinal cross-sectional view illustrating the
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`and is capable of forming a stable rectifying layer. Also, the
`first embodimentofthis invention,
`
`
`
`
`
`
`
`
`
`
`
`
`metallic film should satisfy the foregoing requirements (2)
`FIG. 2 is a longitudinal cross-sectional view illustrating a
`
`
`
`
`
`
`
`through (4).
`modification of the first embodimentshownin Fig.1;
`
`
`
`
`
`
`Molybdenum (Mo), palladium (Pd) orthe like satisfies the
`
`
`
`
`
`
`
`
`FIG. 3 is a longitudinal cross-sectional view illustrating the
`
`
`
`
`
`requirement(1') but does not meet (2). In view of the forego-
`
`
`
`
`
`
`
`
`
`
`second embodimentof this invention;
`
`
`
`
`ing, there is no material available which can perfectly satisfy
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`FIG. 4 is a graph showing capacitance vs. applied voltage
`
`
`
`
`
`
`
`
`
`
`the requirements (1) through (4) or (1') through (4) in the
`
`
`
`
`characteristic of the device of Fig. 3;
`case of ohmic contact or Schottky barrier respectively, as long
`
`
`
`
`
`
`
`FIG. 5 is a longitudinal cross-sectional view of the third em-
`
`
`
`
`
`
`as a simple metal substance is used therein. For this reason,
`
`
`
`
`
`
`
`
`
`bodimentofthis invention;
`
`
`
`the highly stable ohmic contact or Schottky barrier has hither-
`
`
`
`
`
`
`
`
`
`FIGS. 6(A) through 6(C) show the multilevel structure of
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`to been formedby only resorting to the multilayer technique.
`an integrated circuit to which the presentinventionis applied;
`
`
`
`
`
`
`
`
`A similar problem arises in the case of the MOS-type
`
`
`
`
`
`
`
`
`
`
`and
`
`semiconductor device which has the metal-insulator-semicon-
`
`
`
`
`
`
`FIG. 7 is a partial cross-sectional view illustrating the fourth
`
`
`
`
`
`
`ductorlayerstructure.
`
`
`
`embodimentofthis invention.
`
`
`
`Such structure additionally dominates the characteristic
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`In the simple PP junction diode shown in FIG. 1, whichis a
`andreliability of the device by the electricalstability of the in-
`
`
`
`
`
`
`
`
`first embodimentthis invention, as insulating film 12 is formed
`terior state between the semiconductorsubstrate and insulator
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`formed on the substrate.
`
`
`
`
`
`
`
`
`over an n-type single crystal silicon substrate 11, by thermally
`
`
`
`
`
`
`
`
`
`
`
`growing silicon dioxide. Through a small circular hole prear-
`
`
`
`
`
`
`
`Similarly, in the field of the large-scale integration (LSI),
`
`
`
`
`
`
`
`
`rangedatsaid insulatingfilm 12, a P-type impurity is diffused
`the multilevel technique has been adopted to provide the in-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`so that the diffused region 13 of P-type conduction is formed
`terconnection among the elements in the substrate. In the
`
`
`
`
`
`
`
`
`in the substrate 11. To establish a favorable ohmic contact
`multilevel interconnection structure, the conductive and insu-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`2
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`3,617,824
`
`
`
`
`
`
`
`20
`
`
`
`25
`
`
`
`35
`
`
`
`40
`
`
`
`45
`
`
`
`50
`
`
`
`55
`
`
`
`60
`
`
`
`65
`
`
`
`70
`
`
`
`
`
`75
`
`
`
`Page 3 of 6
`
`Page 3 of 6
`
`
`
`3,617,824
`
`
`
`
`
`20
`
`
`
`25
`
`
`
`30
`
`
`
`
`
`35
`
`
`
`40
`
`45
`
`
`
`50
`
`
`
`55
`
`
`
`60
`
`
`
`65
`
`
`
`
`
`
`
`
`4
`3
`sistance of 10 ohm-cm after oxidation in dry oxygen at 1,150°
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`onto the P-type diffusion region 13, a cobalt silicide 14 is
`C. for 2 hours. The oxide film on the lower side of the sub-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`deposited on the entire surface including the insulating film 12
`strate 11 is removed by chemical process, and on the upper
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`ofsilicon dioxide by vacuum evaporation of cathode-sputter-
`side ofthesilicon oxide film 12 there is deposited a metalsili-
`
`
`
`
`
`
`
`
`
`ing to about 2,000 Angstrom thickness. Then, a stable con-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`cide 14, e.g., cobalt silicide, by evaporation at a high vacuum
`ductive metal film 15, such as a gold or platinum film,
`is
`
`
`
`
`
`
`
`
`
`to a thickness of about 2,000 A., and then a suitable metal 15
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`deposited thereon, to about 5,000 Angstrom thickness. After
`
`
`
`
`
`
`
`
`
`
`is vaporized thereon. After the deposition of the metalfilm 15,
`
`
`
`
`
`
`
`
`
`this deposition of metal film, said metal film 15 and transition
`the metal film 15 and cobaltsilicide film 14 are shaped into a
`metalsilicide film 14 are etched into a specific shape by the
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`predetermined configurations by photomask etching. Thesil-
`photomask-etching process. In the foregoing manner, the in-
`
`
`
`
`
`
`icon substrate 11 is cut to a suitable size, and lead wires 31, 32
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`vention provides-a highly stable and highly reliable semicon-
`are connected, respectively, to the lower side of the silicon
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`ductor device through a simple process. In this embodiment,
`
`
`
`
`
`piece and to the metalfilm 15.
`
`
`
`
`
`
`
`
`the specific resistance of the ohmic contact formed between
`
`
`
`
`
`
`The capacity-voltage characteristics of the diode structure
`
`
`
`
`
`
`
`
`cobalt silicide 14 and p-type region 13 whose specific resistivi-
`of the cobalt silicide-silicon dioxide-silicon thus formed are
`
`
`
`
`
`
`
`
`ty is 2x10" ohm-cm is less than about 4X10'* ohm-cm *. This
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`shownin Fig. 4. The capacity-voltage characteristic of the
`
`
`
`
`
`
`
`
`specific contact resistance is very small compared with the
`
`
`
`
`
`
`
`
`diode just formed is represented by the curveain the figure,
`
`
`
`
`
`
`
`specific contact resistance, (i.e., 3.7X10% ohm-cm.* of the
`
`
`
`
`
`
`
`
`while the capacity-voltage characteristic of the diode after the
`
`
`
`
`
`
`
`
`conventional device. Even when the P-type region 13 is
`heat treatment in air at 250° C. for 30 minutes with the appli-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`replaced by an n-type silicon of specific resistivity 1x10? ohm-
`cation of an electric field of 3X10'6 V/cm. with the metal
`
`
`
`
`
`
`
`
`
`
`cm. and platinumsilicide (PtSi) is used as the transition metal
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`maintained positive andthe silicon negative is represented by
`silicide 14, a favorable ohmic contact of the specific contact
`
`
`
`
`
`
`
`
`the curve b.
`resistance 6X101* ohm-cm.?is obtained. It is to be noted that
`
`
`
`
`
`
`
`
`
`
`Whencalculated from the curve a of FIG. 4, the surface
`
`
`
`
`
`
`
`
`the ohmic contact obtained according to this invention is sta-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`charged carrier density of the resulting diode is about 5X101!/
`ble from the thermalas well as the mechanicalpointof view.
`
`
`
`
`
`
`
`
`
`The sameeffect as stated above can be obtained from this
`cm.? and, as can be seen from the curve b of FIG. 2, the sur-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`face-charged carrier density remains substantially unchanged
`embodimenteven if modified to a certain extent. More par-
`
`
`
`
`
`
`
`even with a heat treatment with the voltage applied. It will be
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`ticularly, referring to FIG. 2, the heat treatment may be ac-
`thus apparent that a diode having surface states betweensil-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`complished after depositing the transition metalsilicide 14.
`icon andsilicon dioxide can be obtained.
`
`
`
`
`
`
`Alternatively a stable conduction metal film 15, such as a
`
`
`
`
`
`
`
`Fig. 5 showsa field effect transistor of MOStype, a form of
`
`
`
`
`
`
`
`
`platinum orgold film may be added thereto via a metallic film
`
`
`
`
`
`
`
`
`
`semiconductor device obtained in accordance with the
`
`
`
`
`
`
`
`21 oftitanium or chromium (Cr), after depositing a transition
`
`
`
`
`
`
`
`presentinvention. Within a P-typesilicon substrate 11 thereis
`
`
`
`
`
`
`
`metal silicide 14. In FIG, 2 the same reference numerals are
`
`
`
`
`
`
`
`
`
`
`formed an N*-type region source 51 and drain 52. Holes are
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`used to designate the same elementsas in Fig.1,
`
`
`
`
`
`
`
`
`then madeat predetermined pointsof thesilicon dioxide film
`
`
`
`
`
`
`
`Still another example related to the Schottky barrier diode
`12, Next, cobalt silicide 14 and a simple metal 15 are
`
`
`
`
`
`
`
`
`
`
`
`
`
`will be explained below.
`deposited by evaporation on the surface, and a source elec-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`Referring again to Figure 1, the semiconductorsubstrate 11
`trode 53, gate electrode 54,and drain electrode 55 are etched
`
`
`
`
`
`
`
`
`
`
`and region 13 are of N-type silicon whose specific resistivities
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`to the desired shapes by photomask etching. In such field ef-
`are respectively 2X10" ohm-cm. and 0.8 ohm-cm. A silicon
`
`
`
`
`
`
`
`
`fect transistors of the MOStype, thestability of surface states
`
`
`
`
`
`
`
`
`
`dioxide film 12 is thermally grown on the surface of each of
`
`
`
`
`
`
`
`ofthesilicon substrate the gate electrode has a direct bearing
`
`
`
`
`
`
`
`
`
`
`the regions 11 and 13. A circular hole is provided in the oxide
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`upon the reliabliity of the operating characteristics. The
`file 12, to expose the surfaceofsilicon. The exposed surfaceis
`
`
`
`
`
`
`
`
`
`transistor of this embodiment has such stable surface states
`
`
`
`
`
`
`
`
`
`cleaned by chemical treatment. After this process,a transition
`
`
`
`
`
`
`
`that the transistor functions mostsatisfactorily without varia-
`
`
`
`
`
`
`
`
`metalsilicide 14, such as cobalt silicide, is evaporated thereon
`
`
`
`
`
`
`
`
`
`
`
`
`tion of the operating characteristics.
`to about 2,000 thickness under a super high vacuum condi-
`
`
`
`
`
`
`
`
`With the embodiments of FIGS. 3 and5, it is feasible for the
`
`
`
`
`
`
`
`tion. Further, an electrode 15 is deposited onto thesilicide 14.
`
`
`
`
`
`
`
`
`gate electrode to be formedofsilicide, to maintain the surface
`
`
`
`
`
`
`The resultant metal layers are then formed into a specific
`
`
`
`
`
`
`
`
`
`
`
`
`
`stability of the gate insulator.
`shape through a photoetching process. The characteristic of
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`Referring to FIGS. 6(A) through (C) and Fig. 7, the fourth
`
`
`
`
`
`
`
`
`the Schottky barrier diode are tabulated below, in comparison
`embodimentofthis invention has a multilevel interconnection
`
`
`
`
`
`
`with those of a conventional diode having molybdenum (Mo).
`structure.
`
`
`
`
`
`
`
`
`
`Fig. 6A shows an integrated circuit substrate in which cir-
`
`
`
`
`
`
`
`
`cuit components such as transistors, diodes, and resistors is
`
`
`
`
`
`
`
`formed and interconnected with a composite conductive film
`
`
`
`
`
`
`
`such as silicide-metal-silicide. On the surface of the semicon-
`
`
`
`
`
`
`ductor, an insulating film of silicon dioxide and/or anotherin-
`
`
`
`
`
`
`
`sulator is deposited by a chemical reaction or sputtering.
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`Apertures are formed in the insulator layer in the desired pat-
`tern for photomask etching use, as shown in FIG. 6B. Next, a
`
`
`
`
`
`
`
`
`
`metal silicide and a low-resistance metal are deposited on the
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`insulator and through apertures provide multilevel intercon-
`nection amongthecircuits as shownin FIG. 6C.
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`A partial sectional view ofthe resulting integrated circuit 70
`
`
`
`
`
`
`
`is shownin FIG. 7. Referring to FIG. 7, a silicon substrate 11 is
`
`
`
`
`
`
`
`
`
`coated bysilicon dioxide 12. In the substrate 11, transistors,
`diodes and resistors are formed. Interconnection among the
`
`
`
`
`
`
`
`
`elements is achieved by films of a metalsilicide 71, 72 and a
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`low-resistance metal 73 which altogether form a triple layer.
`
`
`
`
`
`
`
`
`The entire surface of the integrated circuit substrate, except
`
`
`
`
`
`
`
`
`
`for the through-holes, is covered by an insulating film 74.
`
`
`
`
`
`
`
`Through the apertures,
`the upper level
`interconnections
`formed by a metal silicide 75 and a low-resistance metal 76
`
`
`
`
`
`
`
`are connected to the underlyingcircuits.
`
`
`
`
`
`
`
`
`
`
`
`
`According to this embodiment, integrated circuits of high
`
`
`
`
`
`
`
`
`degree of integration are obtained, and the multilevel inter-
`
`
`
`
`
`Current
`Current
`Metal which forms
`
`
`
`
`value
`Schottky barrier
`value
`
`
`
`Height
`(specific resist-
`when for-
`when in-
`
`
`
`
`
`
`of
`ance of N-type
`word vol-
`verse vol-
`Peak
`
`
`
`
`
`
`
`barrier
`silicon: 0.8 ohm-cm.)
`tage is
`tage is
`withstand
`
`
`
`
`
`
`
`voltage
`{contact area:
`ev.
`1 volt
`4 volts
`|
`
`
`
`
`
`
`
`
`1.9x10"5 cm.?)
`(ampere}
`(ampere)
`{volt)
`
`
`
`
`
`
`
`
`
`18
`16x10"
`80x10"
`0.65
`CoSi
`
`
`
`
`
`18
`30x10"
`88x10
`0.58
`FeSi
`
`
`
`
`
`20
`15x10"
`78x10"
`PdSi
`0.73
`
`
`
`
`
`25
`10x 101°
`70x16"
`0.82
`PtSi
`
`
`
`
`
`40x10"*
`68x10"
`Mo
`0.65
`15
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`Asis evidently shownin the table, the Schottky diode of this
`
`
`
`
`
`
`
`invention is highly efficient and its production process can be
`
`
`
`
`
`
`
`simplified and, further, the heat-resisting property is markedly
`improved owingto the useofsaid silicide.
`
`
`
`
`
`
`Fig. 3 is a sectional view showing a second embodiment of
`
`
`
`
`
`
`this invention, whose structure is a MOSdiode obtainedin ac-
`
`
`
`
`
`
`
`cordancewith the present invention.
`
`
`
`
`
`Referring to Fig. 3, a silicon dioxide film 12 is formed on the
`
`
`
`
`
`
`
`surface of an N-typesilicon substrate 11 having a specific re-
`
`
`
`
`
`
`
`
`70
`
`
`
`75
`
`
`
`\\\
`
`\
`
`Page4 of 6
`
`“~\
`
`Page 4 of 6
`
`
`
`
`5
`connection attained in accordance with the inventionis highly
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`reliable becauseit is extremely stabilized thermally and elec-
`
`trically.
`The metalsilicide to be used in the invention is not limited
`
`
`
`
`
`
`
`
`to what has been shownin the described embodiments but any
`
`
`
`
`
`
`
`
`
`
`metalsilicide may be used so long as sucha silicide is chemi-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`cally stable, low in specific resistance, and satisfactory as re-
`
`
`
`
`
`
`
`
`gards its bonding property towardsilicon andinsulating film.
`Various experiments have been conducted and it was found
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`that the following transition metals silicide are especially
`favorablefor the purpose ofthis invention:
`
`
`
`
`
`
`3d Transition Meta!Silicide
`
`
`
`
`
`
`
`
`
`
`titanium silicides (TisSi,, TiSi,) vanadium silicides
`
`
`
`
`
`
`
`(V;Sis, VSi,), chromium silicides (Cr,Si, CrSi, CrSi,),
`
`
`
`
`
`
`manganesesilicides (MnsSi;, MnSi, Mn,Si;), iron silicides
`
`
`
`
`
`
`
`(FeSi, FeSi,) cobalt silicides (Co,Si, CoSi, CoSi,),
`
`
`
`
`
`nickelsilicides (NiSi,, Ni,Si, NiSi).
`4d or 5d Transition MetalSilicide
`
`
`
`
`
`
`
`
`
`
`palladium silicides (Pd,Si, PdSi), platinum silicides (Pt,Si,
`PtSi).
`
`
`
`
`
`
`
`
`
`While the invention has been explained in connection with
`
`
`
`
`
`
`
`
`specific embodiments,it is to be understood that this explana-
`
`
`
`
`
`Page 5 of 6
`
`3,617,824
`
`
`
`
`6
`
`
`
`
`
`
`
`
`tion is made only by way of example andnotas a limitation to
`
`
`
`
`the scopeof the invention.
`Claimsfor Patent
`
`
`
`1. Ina field effect semiconductor device of MOS type hav-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`ing a semiconductorsubstrate, the improvement comprising a
`
`
`
`
`
`
`
`layer of metal silicide means deposited on an insulative layer
`lying on the surface of the semiconductor substrate, said
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`meansforminga stable capacitance-voltage said metalsilicide
`
`
`
`
`
`
`
`
`being selected characteristic from the group consisting of
`
`
`
`
`
`
`
`platinumsilicide, cobalt silicide and palladiumsilicide.
`2. The improvementas claimed in claim 1, wherein said
`
`
`
`
`
`
`
`metalsilicide is cobalt silicide and wherein a layer of metal of
`
`
`
`
`
`
`
`
`low electrical resistance covers the metalsilicide layer.
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`3. The improvement as claimed in claim 1, wherein two im-
`
`
`
`
`
`
`
`purity-diffused regions having the opposite conductivity type
`to said substrate are formedin said substrate in such a relation
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`that the portion ofthe surface of said semiconductor substrate
`
`
`
`
`
`
`
`
`
`lying under said metal silicide layer may be interposed
`betweensaid two regions, andelectrical leadout members are
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`applied to eachof said regions said metalsilicide layer.
`*
`&
`*
`*
`*
`
`5
`
`10
`
`15
`
`
`
`20
`
`
`
`25
`
`
`
`30
`
`
`
`35
`
`
`
`40
`
`
`
`45
`
`
`
`50
`
`
`
`355
`
`
`
`60
`
`
`
`65
`
`
`
`70
`
`
`
`75
`
`
`
`Page 5 of 6
`
`
`
`
`
`
`
`UNITED STATES PATENT OFFICE
`
`
`CERTIFICATE OF CORRECTION
`
`
`
`
`
`Patent No. Dated_November 2, 19713,617,824
`
`
`
`
`
`
`
`
`Inventor(s)
`
`
`
`
`Daizaburo Shinoda, et al
`
`
`
`
`
`
`
`
`
`
`
`
`It is certified that error appears in the above-identified patent
`and that said Letters Patent are hereby corrected as shown below:
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`Column 6, line 8, after "voltage" should read
`-- characteristic --; line 9, after
`"selected" cancel
`
`
`
`
`
`
`
`"characteristic"; line 12, after "layer of" should read
`
`
`
`
`
`
`
`--a --; line 21, after "regions" should read -- and --.
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`Signed and sealed this 10th day of October 1972.
`
`
`
`Commissioner of Patents
`
`
`(SEAL)
`Attest:
`
`
`
`
`EDWARD M,. FLETCHER, JR.
`
`
`Attesting Officer
`
`
`
`
`ROBERT GOTTSCHALK
`
`
`
`
`
`
`ORM PO-1050 (10-69)
`
`USCOMM-DC 60378-P69
`f U.S. GOVERNMENT PRINTING OFFICE : 1949 O—366-334,
`
`Page6 of 6
`
`Page 6 of 6
`
`