`«2 United States Patent
`
`
`
`
`
`US 6,887,353 B1
`(10) Patent No.:
`
`
`
`
`
`
`
`Dingetal. May3, 2005
`
`(45) Date of Patent:
`
`US006887353B1
`
`
`
`
`
`
`
`(54) TADLORED BARRIER LAYER WHICH
`PROVIDES IMPROVED COPPER
`
`
`
`INTERCONNECT ELECTROMIGRATION
`
`RESISTANCE
`
`
`
`
`
`
`
`(75)
`
`
`
`
`
`
`
`
`
`Inventors: Peijun Ding, San Jose, CA (US); Tony
`
`
`
`
`Chiang, Mountain View, CA (US);
`
`
`
`
`
`Barry L. Chin, Saratoga, CA (US)
`
`
`
`
`
`
`
`(73) Assignee: Applied Materials, Inc., Santa Clara,
`
`
`CA (US)
`
`
`(*) Notice:
`
`
`
`
`
`
`
`
`
`Subject to any disclaimer, the term ofthis
`
`
`
`
`
`patent is extended or adjusted under 35
`
`
`
`
`U.S.C. 154(b) by 863 days.
`
`
`
`
`
`(21) Appl. No.: 08/995,108
`
`
`
`
`
`(22)
`Filed:
`Dec. 19, 1997
`
`
`
`
`
`
`
`
`(51)
`Int. Ch? oe C23C 14/00; C23C 14/32;
`O11. 21/44
`
`
`
`
`
`
`
`(52) US. Chcece 204/192.15; 204/192.17;
`
`
`
`204/192.22; 204/192.25; 438/656
`
`
`
`
`
`
`(58) Field of Search 0000. 204/192.15, 192.17,
`
`
`
`
`
`204/192.22, 192.25; 438/652, 656, 660
`
`
`(56)
`
`
`
`References Cited
`U.S. PATENT DOCUMENTS
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`4,319,264 A
`3/1982 Gangulee et al. o......... 357/71
`
`
`
`
`
`
`4,985,750 A *
`1/1991 Hoshino ..........
`eee 257/751
`
`
`
`
`
`
`§,186,718 A
`2/1993 Tepman etal.
`.. 29/25.01
`...
`
`
`
`
`
`
`5,236,868 A
`8/1993 Nulman...........
`vee 437/190
`
`
`
`
`
`
`5,240,880 A *
`8/1993 Hindmanet al.
`w+ 438/656
`
`
`
`
`
`
`5,281,485 A
`1/1994 Colgan ctal.
`ve 428/457
`
`5,320,728 A
`we 204/192
`6/1994 ‘Tcpman........
`5,391,517 A *
`2/1995 Gelatos et al. ow. 438/643
`5/1996 Nulmanetal. ....00.. 438/653
`5,521,120 A *
`
`
`
`
`
`
`.......
`5,571,752 A * 11/1996 Chen etal.
`v- 438/642
`
`
`
`
`
`
`
`5,676,587 A
`10/1997 T.anders et al.
`......00.000.. 451/57
`
`
`
`
`
`
`5,707,498 A *
`1/1998 Ngan........
`204/192.12
`
`
`
`
`
`
`5,795,796 A *
`8/1998 Kim occ 438/660
`
`
`
`
`
`FOREIGN PATENT DOCUMENTS
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`EP
`
`EP
`
`
`0570 205 Al
`11/1993 we HOIL/21/321
`
`
`
`
`
`
`
`0 751 566 A2
`VW/1997 ee HO1L/23/532
`
`
`
`
`
`
`
`OTHER PUBLICATIONS
`
`
`
`
`
`
`
`
`
`
`
`Karen Holloway et al., “Tantalum as a Diffusion as a
`
`
`
`
`
`
`
`
`
`
`Diffusion Barrier Between Copper and Silicon:
`|'ailure
`
`
`
`
`
`
`
`Mechanism and Effect of Nitrogen Additions”, J. Appl.
`
`
`
`
`
`
`
`Phys. 71 (11), Jun. 1, 1992, pp. 5433-5444.
`
`
`
`
`
`
`
`Katsutaka Sasaki et al., “Stoichiometry of Ta—N Film andIts
`
`
`
`
`
`
`
`
`Application for Diffusion Barrier in the Al, Ta/Ta—N/Si
`
`
`
`
`
`
`
`Contact System”, Japanese Journal of Applied Physics, vol.
`
`
`
`
`
`
`29, No. 6, Jun. 1990, pp. 1043-1047.
`
`
`
`
`
`
`
`
`
`
`E. M. Zielinski et al., “The Effects of Processing on the
`
`
`
`
`
`
`
`Microstructure of Copper Thin Films on Tantalum Barrier
`
`
`
`
`
`
`
`
`
`
`Layers”, Mat. Res. Soc. Symp. Proc. vol. 391, (1995,) pp
`303-308.
`
`
`
`
`
`
`
`
`
`PCYInternational Search Report dated Mar. 25, 1999.
`
`
`
`
`
`
`
`Gang Bai et al., “Copper Interconnection Depostion Tech-
`
`
`
`
`
`
`
`niques and Integration”, 1996 Symposium on VLSI Tech-
`
`
`
`
`
`
`nology, Digests of Technical Papers (0-7803-3342-X/96,
`
`TEEE).
`
`
`
`
`
`
`
`
`
`
`
`S. M. Rossnagel and J. Hopwood, “Metal ion deposition
`
`
`
`
`
`
`
`from ionized magnetron sputtering discharge”, J. Vac. Sci.
`
`
`
`
`
`
`
`
`
`Technol. B, vol. 12, No. 1, pp. 449-453 (Jan./Feb. 1994).
`
`
`
`
`
`
`
`
`
`S. M. Rossnagel et al., “Thin, high atomic weight refractory
`
`
`
`
`
`
`
`
`
`film deposition for diffusion barrier, adhesion layer, and seed
`
`
`
`
`
`
`
`
`
`layer applications”, J. Vac. Sci. Technol. B, vol. 14, No. 3,
`
`
`
`
`pp. 1819-1827 (May/Tun. 1996).
`
`
`
`
`
`
`
`C. Steinbruchel, “Patterning of Copper for Multilevel Met-
`
`
`
`
`
`
`allization: Reactive Ion Etching and Chemical—Mechanical
`
`
`
`
`
`
`
`Polishing”, Applied Surface Science, 91, pp. 139-146
`
`(1995).
`
`
`
`
`
`
`
`
`
`USS. Appl. No. 08/824,911, filed Mar. 27, 1997, of Ngan et
`al.
`
`
`
`
`
`
`
`
`
`
`US. Appl. No. 08/863,451, filed May. 27, 1997, of Chiang
`et al.
`
`
`
`
`
`
`
`
`
`
`
`US. Appl. No. 08/924,487,filed Aug. 23, 1997, of Ngan ct
`al.
`
`
`
`
`
`
`* cited by examiner
`
`
`
`
`
`
`
`
`Primary Examiner—Patrick Ryan
`Assistant Examiner—Julian Mercado
`
`
`
`
`
`
`
`
`(74) Attorney, Agent, or Firm—Shirley L. Church
`
`
`
`(57)
`
`ABSTRACT
`
`
`
`
`
`
`
`Disclosed herein is a barrier layer structure useful in forming
`
`
`
`
`
`
`copper interconnects and electrical contacts of semiconduc-
`
`
`
`
`
`
`
`
`
`tor devices. The barrier layer structure comprisesa first layer
`
`
`
`
`
`
`
`
`
`of TaN,, which is applied directly over the substrate, fol-
`
`
`
`
`
`
`
`
`
`lowed by a second layer of Ta. The TaN,/Ta barrier layer
`
`
`
`
`
`
`
`structure provides both a barrier to the diffusion of a copper
`
`
`
`
`
`
`
`
`layer deposited thereover, and enables the formation of a
`
`
`
`
`
`
`
`copper layer having a high <111> crystallographic content
`
`
`
`
`
`
`
`
`so that
`the electromigration resistance of the copper is
`
`
`
`
`
`
`
`
`
`increased. The TaN, layer, where x ranges from about 0.1 to
`
`
`
`
`
`
`
`about 1.5, is sufficiently amorphousto preventthe diffusion
`
`
`
`
`
`
`
`
`of copper into the underlying substrate, which is typically
`silicon or a dielectric such as silicon dioxide. The thickness
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`of the TaN,, and Ta layers used for an interconnect depend on
`
`
`
`
`
`
`
`
`
`
`the feature size and aspect ratio; typically, the TaN,, layer
`
`
`
`
`
`
`
`thickness ranges from about 50 A to about 1,000 A while
`
`
`
`
`
`
`
`
`the ‘la layer thickness ranges from about 20 A to about 500
`
`
`
`
`
`
`
`
`
`A. For a contact via, the permissible layer thickness on the
`
`
`
`
`
`
`
`
`via walls must be even more carefully controlled based on
`
`
`
`
`
`
`
`
`
`feature size and aspect ratio;
`typically,
`the TaN,
`layer
`
`
`
`
`
`
`
`
`thickness ranges from about 10 Ato about 300 A,while the
`Ta layer thickness ranges from about 5 A to about 300 A.
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`The copperlayer is deposited at the thickness desired to suit
`
`
`
`
`
`
`
`
`
`the needs of the device. The copper layer may be deposited
`
`
`
`
`
`
`
`
`using, any of the preferred techniques knownin the art.
`
`
`
`
`
`
`
`
`Preferably, the entire copper layer, or at least a “seed” layer
`
`
`
`
`
`
`
`is deposited using physical vapor deposition
`of copper,
`
`
`
`
`
`techniques such as sputtering or evaporation, as opposed to
`
`
`
`
`
`
`
`
`CVDorelectroplating. Since the crystal orientation of the
`
`
`
`
`
`
`
`copper is sensitive to deposition temperature, and since the
`
`
`
`
`
`
`
`
`copper may tend to dewet/delaminate from the barrier layer
`
`
`
`
`
`
`
`
`
`
`if the temperature is too high,it is important that the copper
`
`
`
`
`
`
`
`be deposited and/or annealed at a temperature of less than
`
`
`
`
`
`
`
`
`about 500° C., and preferably at a temperature of less than
`about 300° C.
`
`
`
`
`
`
`7 Claims, 2 Drawing Sheets
`
`
`
`Page 1 of 9
`
`TSMC Exhibit 1005
`
`TSMC Exhibit 1005
`
`Page 1 of 9
`
`
`
`
`U.S. Patent
`
`
`
`
`May 3, 2005
`
`
`
`
`
`Sheet 1 of 2
`
`
`
`US 6,887,353 B1
`
`
`
`FANteaWAASWENWAENWLSSSWANANSSOUSNUSSSENNNEA_ASSESSESASNSSRSs
`
`
`
`
`
`
`
`
`
`
`
`
`
`Page 2 of 9
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`Page 2 of 9
`
`
`
`
`
`May 3, 2005
`
`
`
`WHM4(HEIND
`
`Sheet 2 of 2
`
`US 6,887,353 B1
`
`
`
` Ayisuajuy0ott00002yeag
`
`812
`
`0
`
`000S|
`
`0000!
`
`000S
`
`SeilnO/(¥r11)01/NoLanset|
`
`
`
`
`
`N9/(v9Sr)1/NOLM9/(YOL1)°1/NoLn9/(y2s)01/NOL¢Uld
`
`U.S. Patent
`
`soz¢}00007
`
`602
`
`002
`
`
`
`AJERSANGEL/ANELUOGt}NDJOCUX
`
`Page 3 of 9
`
`Page 3 of 9
`
`
`
`
`
`
`US 6,887,353 B1
`
`
`1
`TAILORED BARRIER LAYER WHICH
`
`
`
`
`PROVIDES IMPROVED COPPER
`
`
`
`
`INTERCONNECT ELECTROMIGRATION
`
`RESISTANCE
`
`
`
`BACKGROUND OF THE INVENTION
`
`
`
`
`1. Field of the Invention
`
`
`
`
`
`
`
`
`
`
`
`The present invention pertains to a particular TaN,/Ta
`
`
`
`
`
`
`
`barrier/wetting layer structure which increases the degree of
`
`
`
`
`
`
`
`
`{111} crystal orientation in an overlying copper layer,
`
`
`
`
`
`
`thereby providing improved electromigration resistance of
`
`
`the copper.
`
`
`
`
`
`
`2. Brief Description of the Background Art
`
`
`
`
`
`As microelectronics continue to miniaturize, interconnec-
`
`
`
`
`
`
`
`tion performance, reliability, and power consumption has
`
`
`
`
`
`
`
`become increasingly important, and interest has grown in
`
`
`
`
`
`
`
`replacing aluminum alloys with lower-resistivity and higher-
`
`
`
`
`
`
`reliability metals. Copper offers a significant improvement
`over aluminum as a contact and interconnect material. For
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`example, the resistivity of copper is about 1.67 wQQ2cm, which
`
`
`
`
`
`
`
`
`is only about half of the resistivity of aluminum.
`
`
`
`
`
`
`
`There are two principal competing technologies under
`
`
`
`
`
`
`evaluation by material and process developers working to
`
`
`
`
`
`
`
`
`enable the use of copper. The first technology is known as
`
`
`
`
`
`
`damascene technology.In this technology, a typical process
`
`
`
`
`
`
`
`for producing a multilevel structure having feature sizes
`(i.e., width of the aperture) in the range of 0.5 micron (um)
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`or less would include: blanket deposition of a dielectric
`
`
`
`
`
`
`
`material; patterning of the dielectric material to form open-
`
`
`
`
`
`
`
`ings; deposition of a diffusion barrier layer and, optionally,
`
`
`
`
`
`
`
`
`a wetting layer to line the openings; deposition of a copper
`
`
`
`
`
`
`
`
`
`layer onto the substrate in sufficient thickness to fill the
`
`
`
`
`
`
`
`openings; and removal of excessive conductive material
`
`
`
`
`
`
`
`from the substrate surface using chemical-mechanical pol-
`
`
`
`
`
`
`
`ishing (CMP)
`techniques. The damascene process is
`
`
`
`
`
`
`
`
`described in detail by C. Steinbruchel in “Patterning of
`
`
`
`
`
`
`
`
`copper for multilevel metallization: reactive ion etching and
`
`
`
`
`
`chemical-mechanical polishing”, Applied Surface Science
`
`
`91 (1995)139-146.
`
`
`
`
`
`
`
`The competing technology is one which involves the
`
`
`
`
`
`
`
`patterned etch of a copper layer.In this technology, a typical
`
`
`
`
`
`
`
`
`process would include deposition of a copper layer on a
`
`
`
`
`
`
`desired substrate (typically a dielectric material having a
`
`
`
`
`
`
`barrier layer on its surface); application of a patterned hard
`
`
`
`
`
`
`
`
`maskor photoresist over the copper layer; pattern etching of
`
`
`
`
`
`
`
`
`
`the copper layer using wet or dry etch techniques; and
`
`
`
`
`
`
`
`
`
`deposition of a dielectric material over the surface of the
`
`
`
`
`
`
`
`
`patterned copper layer, to provide isolation of conductive
`
`
`
`
`
`
`
`
`lines and contacts which comprise various integrated cir-
`cuits.
`
`
`
`
`
`
`
`
`
`
`
`
`Typically, the copper layer can be applied using sputtering
`
`
`
`
`
`
`
`
`techniques well knownin the art. The sputtering of copper
`
`
`
`
`
`
`
`provides a much higher deposition rate than evaporation or
`
`
`
`
`
`
`
`CVD (chemical vapor deposition) and provides a purer
`
`
`
`
`copper film than CVD.
`
`
`
`
`
`
`
`In integrated circuit interconnect structures where copper
`
`
`
`
`
`
`
`
`
`is the material used to form conductive lines and contacts,it
`
`
`
`
`
`
`
`
`is recognized that copper diffuses rapidly into adjacent
`
`
`
`
`
`
`
`
`
`layers of SiO, and silicon and needs to be encapsulated.
`
`
`
`
`
`
`
`Gang Bai et al.
`in “Copper Interconnection Deposition
`
`
`
`
`
`
`Techniques and Integration”, 1996 Symposium on VLSI
`
`
`
`
`
`
`Technology, Digests of Technical Papers (0-7803-3342-X/
`
`
`
`
`
`
`
`96, IEEE), describe the effectiveness of Ta, TiN, W and Mo
`
`
`
`
`
`
`
`
`
`
`as barrier layers for use with copper. They concluded that Ta
`
`10
`
`
`
`15
`
`
`
`20
`
`
`
`25
`
`
`
`30
`
`
`
`35
`
`
`
`45
`
`
`
`50
`
`
`
`55
`
`
`
`60
`
`
`
`65
`
`
`
`
`2
`
`
`
`
`
`
`
`
`annealed in UHV(ultra high vacuum) after copper deposi-
`
`
`
`
`
`
`
`
`tion provided the best barrier layer. Sputtered copper
`
`
`
`
`
`
`
`
`
`appeared to be preferable over CVD copper and over elec-
`
`
`
`
`
`
`
`
`troplated copper, although all
`the data for electroplated
`
`
`
`
`
`
`
`
`copper was not available at the time of presentation of the
`
`paper.
`
`
`
`
`
`
`
`
`USS. Pat. No. 4,319,264 of Gangulee et al., issued Mar.9,
`
`
`
`
`
`
`
`1982 and titled “Nickel-gold-nickel Conductors For Solid
`
`
`
`
`
`
`State Devices” discusses the problem of electromigration in
`
`
`
`
`
`
`
`
`
`solid state devices. In particular, the patent discusses the
`
`
`
`
`
`
`
`application of direct current over particular current density
`
`
`
`
`
`
`
`
`ranges which induces motion of the atoms comprising the
`
`
`
`
`
`
`
`thin film conductor, the effect known as electromigration.
`
`
`
`
`
`
`Electromigration is said to induce crack or void formation in
`
`
`
`
`
`
`
`
`
`
`the conductor which, over a period of time, can result in
`
`
`
`
`
`
`
`conductor failure. The rate of electromigration is said to be
`
`
`
`
`
`
`
`dependent on the current density imposed on the conductor,
`
`
`
`
`
`
`
`
`
`the conductor temperature, and the properties of the con-
`
`
`
`
`
`
`
`ductor material. In high current density applications, poten-
`
`
`
`
`
`
`
`tial conductor failure due to electromigration is said to
`
`
`
`
`
`
`
`
`
`severely limit the reliability of the circuit. In discussing the
`
`
`
`
`
`
`
`various factors affecting performance of the conductive
`
`
`
`
`
`
`materials, grain structure is mentioned as being important.
`
`
`
`
`
`
`
`
`(In order to obtain adequate lithographic line width
`
`
`
`
`
`
`
`
`resolution,it is recommendedthatthe film be small grained,
`
`
`
`
`
`
`
`
`
`with a grain size not exceeding about one-third of the
`
`
`
`
`
`
`
`
`required line width.) Uniformity of grain size and preferred
`
`
`
`
`
`
`
`
`crystallographic orientation of the grains are also said to be
`
`
`
`
`
`
`factors which promote longer (electromigration limited)
`
`
`
`
`
`
`
`conductor lifetimes. Fine grained films are also described as
`
`
`
`
`
`
`being smoother, which is a desirable quality in semiconduc-
`
`
`
`
`
`
`
`tor applications, to lessen difficulties associated with cov-
`
`
`
`
`
`ering the conductor with an overlayer.
`
`
`
`
`
`
`
`
`U.S. Pat. No. 5,571,752 to Chen et al., issued Nov. 5,
`
`
`
`
`
`
`
`1996, discloses a method for patterning a submicron semi-
`
`
`
`
`
`
`
`conductor layer of an integrated circuit. In one embodiment
`
`
`
`
`
`
`describing an aluminum contact, titanium or titanium nitride
`
`
`
`
`
`
`
`having a thickness of between approximately 300 and 2,000
`
`
`
`
`
`
`
`A is formed by sputter deposition to reach the bottom of a
`
`
`
`
`
`
`
`contact opening. Finally, a second conductive layer, typi-
`
`
`
`
`
`
`
`
`cally aluminum,is applied over the surface of the conformal
`
`
`
`
`
`
`
`conductive layer. The aluminum is sputtered on, preferably
`
`
`
`
`
`
`
`at a temperature ranging between approximately 100° C. and
`
`
`
`
`
`
`
`
`400° C. This method is said to make possible the filling of
`
`
`
`
`
`
`
`contact openings having smaller device geometry design
`
`
`
`
`
`
`
`requirements by avoiding the formation of fairly large grain
`sizes in the aluminum film.
`
`
`
`
`
`
`
`
`
`
`
`
`As described in U.S. patent application Ser. No. 08/824,
`
`
`
`
`
`
`
`
`
`
`911, of Ngan et al., filed Mar. 27, 1997 and commonly
`
`
`
`
`
`
`
`
`
`assigned with the present invention, efforts have been made
`
`
`
`
`
`
`
`to increase the <111> crystallographic content of aluminum
`
`
`
`
`
`as a means of improving electromigration of aluminum. In
`
`
`
`
`
`
`
`
`
`particular,
`the <111> content of an aluminum layer was
`
`
`
`
`
`
`
`
`controlled by controlling the thickness of various barrier
`
`
`
`
`
`
`
`
`layers underlying the aluminum layer. The underlying bar-
`
`
`
`
`
`
`
`
`rier layer structure was Ti/TiN/TiN,, which enabled alumi-
`
`
`
`
`
`
`
`
`num filling of high aspect vias while providing an aluminum
`
`
`
`
`
`
`
`
`fill exhibiting the high degree of aluminum <111> crystal
`
`
`
`
`
`
`
`orientation. The Ti/TiN/TiN,, barrier layer was deposited
`
`
`
`
`
`
`
`
`
`using IMP (ion metal plasma) techniques, and the barrier
`
`
`
`
`
`
`
`
`layer thicknesses were as follows. The thickness ofthe first
`
`
`
`
`
`
`
`
`
`layer of Ti ranges from greater than about 100 A to about
`
`
`
`
`
`
`
`500 A (the feature geometry controls the upper thickness
`
`
`
`
`
`
`
`
`
`
`limit). The thickness of the TiN second layer ranges from
`
`
`
`
`
`
`
`
`greater than about 100 A to less than about 800 A
`
`
`
`
`
`
`
`
`
`
`(preferably, less than about 600 A). And,the TiN,, third layer
`
`
`
`
`
`
`
`(having a Ti content ranging from about 50 atomic percent
`
`Page 4 of 9
`
`Page 4 of 9
`
`
`
`
`
`US 6,887,353 B1
`
`
`3
`
`
`
`
`
`
`
`
`titanium toabout 100 atomic percent titanium) ranges from
`
`
`
`
`
`
`
`
`about 15 A to about 500 A. A Ti/TiN/TIN,, barrier layer
`
`
`
`
`
`
`
`
`having this structure, used to line a contact via, is described
`
`
`
`
`
`
`
`
`
`as enabling complete filling of via with sputtered warm
`
`
`
`
`
`
`
`
`
`aluminum, where the feature size of the via or aperture is
`
`
`
`
`
`
`
`
`
`
`about 0.25 micron or less and the aspect ratio ranges from
`
`
`
`
`
`
`about 5:1 to as high as about 6:1.
`
`
`
`
`
`
`
`Subsequently, in U.S. Pat. No. 5,882,399, of Nganet al.,
`
`
`
`
`
`
`
`
`
`issued Mar. 16, 1999, the inventors disclose that to maintain
`
`
`
`
`
`
`
`a consistently high aluminum <111> crystal orientation
`
`
`
`
`
`
`content of an interconnect during the processing of a series
`
`
`
`
`
`
`of semiconductor substrates in a given process chamber,it is
`
`
`
`
`
`
`
`
`necessary to form thefirst deposited layer of the barrier layer
`
`
`
`
`
`
`
`to a minimalthickness of at least about 150 A,to compen-
`
`
`
`
`
`
`
`
`sate for irregularities in the crystal orientation which may be
`
`
`
`
`
`
`
`
`present during the initial deposition of this layer when the
`
`
`
`
`
`
`
`
`process chamberis initially started up (and continuing for
`
`
`
`
`
`
`
`
`
`
`the first 7-8 wafers processed). Ngan etal. teach that in the
`
`
`
`
`
`
`
`case of a copper conductive layer, it may also be necessary
`
`
`
`
`
`
`
`
`
`that the first layer of a barrier layer structure underlying the
`
`
`
`
`
`
`
`
`copper layer have a minimalthicknessofat least about 150
`
`
`
`
`
`
`
`to enable a consistent crystal orientation within the
`A,
`
`
`
`
`
`
`
`copper layer during the processing of a series of wafers in a
`semiconductor chamber.
`
`
`
`
`4
`
`
`
`
`
`
`
`temperature of the copper either during deposition or during
`
`
`
`
`
`
`
`
`subsequent annealing processes not be higher than about
`
`
`
`
`
`
`
`500° C. Preferably, the maximum temperature is about 300°
`C.
`
`
`
`
`
`
`
`
`We havealso developed a method of producing a copper
`
`
`
`
`
`
`interconnect structure comprising a copper layer deposited
`
`
`
`
`
`
`
`
`
`over a barrier layer structure of the kind described above,
`
`
`
`
`
`
`
`comprising a Ta layer overlying a TaN, layer, where the Cu
`
`
`
`
`
`
`
`
`<111> crystallographic content is at least 70% of the Cu
`
`
`
`
`
`
`
`<111> crystallographic content which can be obtained by
`
`
`
`
`
`
`
`
`
`depositing the copper layer over a pure Ta barrier layer
`
`
`
`
`
`
`
`
`
`whichis about 500 A thick. The method comprises the steps
`of:
`
`
`
`
`
`
`
`
`
`a) depositing a first layer of TaN, having a thickness
`
`
`
`
`
`
`
`ranging from greater than about 50 A to about 1,000 A;
`
`
`
`
`
`
`
`b) depositing a second layer of Ta having a thickness
`
`
`
`
`
`
`
`ranging from about 5 A to about 500 A over the surface
`
`
`
`
`
`
`of the first layer of TaN,; and
`c) depositing a third layer ofcopperoverthe surface of the
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`second layer of Ta, wherein at least a portion of the
`
`
`
`
`
`
`
`third layer of copperis deposited using a physical vapor
`
`
`
`
`
`
`
`deposition technique, and wherein the substrate tem-
`
`
`
`
`
`
`
`perature at which the third layer of copper is deposited
`is less than about 500° C
`
`
`
`
`
`
`
`
`
`
`
`Further, we have developed a method of producing a
`
`
`
`
`
`
`copper-comprising contact via structure comprising a copper
`
`
`
`
`
`
`
`
`
`layer deposited over a barrier layer structure of the kind
`
`
`
`
`
`
`
`described above, comprising a Ta layer overlying a TaN,,
`
`
`
`
`
`
`
`
`layer; wherein the Cu <111> crystallographic content is at
`
`
`
`
`
`
`
`
`least 70% of the Cu <111> crystallographic content which
`
`
`
`
`
`
`
`
`can be obtained by depositing said copper layer over a pure
`
`
`
`
`
`
`
`
`
`Ta barrier layer which is about 300 A thick. The method
`
`
`
`
`comprises the steps of:
`
`
`
`
`
`
`
`
`a) depositing a first layer of TaN, having a thickness
`
`
`
`
`
`
`
`ranging from greater than about 10 A to about 300 A;
`
`
`
`
`
`
`
`b) depositing a second layer of Ta having a thickness
`
`
`
`
`
`
`
`ranging from about 5 A to about 300 A over the surface
`
`
`
`
`
`
`of said first layer of TaN,; and
`
`
`
`
`
`
`
`
`
`c) depositing a third layer of copper overthe surface ofthe
`
`
`
`
`
`
`
`
`
`second layer of Ta, wherein at least a portion of the
`
`
`
`
`
`
`
`third layer of copperis deposited using a physical vapor
`
`
`
`
`
`
`
`deposition technique, and wherein the substrate tem-
`
`
`
`
`
`
`
`perature at which the third layer of copper is deposited
`is less than about 500° C
`
`
`
`
`
`
`
`
`
`
`
`In the method of producing a copper-comprising contact
`
`
`
`
`
`
`
`
`structure described above, a least a portion of the first layer
`
`
`
`
`
`
`
`
`
`
`of TaN,,, or the second layer of Ta, or the third layer of Cu,
`
`
`
`
`
`
`
`
`
`or at least a portion of more than one of these three layers
`
`
`
`
`
`
`may be deposited using ion-deposition sputtering, where at
`
`
`
`
`
`
`
`
`least a portion of the sputtered emissionis in the form of ions
`
`
`
`
`
`
`
`
`
`
`at the time the emission reaches the substrate surface, and
`
`
`
`
`
`
`
`where, typically 10% or more of the sputtered emissionis in
`the form of ions at
`the time the emission reaches the
`
`
`
`
`
`
`
`
`
`
`
`substrate surface.
`
`
`BRIEF DESCRIPTION OF THE DRAWINGS
`
`
`
`
`FIG. 1 shows a schematic of a cross sectional view of a
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`sputtering chamberof the kind which can be used to deposit
`
`
`
`
`
`
`the barrier layer of the present invention.
`
`
`
`
`
`
`FIG. 2 showsa graph representative of the copper <111>
`
`
`
`
`
`crystal orientation on a TaN,,/Ta barrier layer as a function
`
`
`
`
`
`
`
`
`
`
`
`of the thickness of the Ta layer, with the TaN,, layer held
`constant at about 500 A.
`
`
`
`
`
`
`
`
`DETAILED DESCRIPTION OF THE
`
`
`PREFERRED EMBODIMENTS
`
`
`
`
`
`
`
`
`
`
`The present disclosure pertains to a TaN,/Ta/Cu structure
`
`
`
`
`
`
`
`and a methodof creating that structure. The TaN,/Ta barrier
`
`
`
`
`10
`
`
`
`15
`
`
`
`20
`
`
`
`25
`
`
`
`30
`
`
`
`35
`
`
`
`40
`
`
`
`45
`
`
`
`50
`
`
`
`55
`
`
`
`60
`
`
`
`65
`
`
`
`SUMMARYOF THE INVENTION
`
`
`
`
`
`
`
`
`
`
`
`
`is a
`We have discovered that tantalum nitride (TaN,)
`
`
`
`
`
`
`
`
`
`better barrier layer for copper than tantalum (Ta). However,
`
`
`
`
`
`
`
`
`copper deposited directly over TaN, does not exhibit a
`
`
`
`
`
`
`
`
`sufficiently high degree of <111> crystal orientation to
`
`
`
`
`
`
`provide the desired copper electromigration characteristics.
`
`
`
`
`
`
`
`We have developed a barrier layer structure comprising a
`
`
`
`
`
`
`
`layer of Ta overlying a layer of TaN,, which provides both a
`
`
`
`
`
`
`
`barrier to the diffusion of a copper layer deposited thereover,
`
`
`
`
`
`
`
`
`and enables the formation of a copper layer having a high
`
`
`
`
`
`
`
`<111> crystallographic content, so that copper electromi-
`
`
`
`gration resistance is increased.
`
`
`
`
`
`
`
`
`
`The TaN,, layer, where x ranges from about 0.1 to about
`
`
`
`
`
`
`
`
`1.5, is sufficiently amorphous to prevent the diffusion of
`
`
`
`
`
`
`
`
`copper into underlyingsilicon orsilicon oxide surfaces. The
`
`
`
`
`
`
`
`
`
`desired thickness for the TaN, layer is dependent on the
`
`
`
`
`
`
`
`
`device structure. For a typical interconnect, the TaN,, layer
`
`
`
`
`
`
`
`thickness ranges from about 50 A to about 1,000 A. For a
`
`
`
`
`
`
`
`
`contact, the TaN,, layer, the thickness on the wall of a contact
`via ranges from“about 10 A to about 300 A, depending on
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`the feature size. The TaN,, layer is preferably deposited using
`
`
`
`
`
`
`standard reactive ion sputtering techniques at a substrate
`
`
`
`
`
`
`
`
`
`temperature ranging from about 20° C. to about 500° C.
`
`
`
`
`
`
`
`However, ion deposition sputtering techniques may be used
`
`
`
`
`to deposit this layer.
`
`
`
`
`
`
`
`
`
`The Ta layer deposited over the TaN, layer has a desired
`thickness ranging from about 5 Ato about 500 A, wherein
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`the thickness is preferably greater than about 20 A, depend-
`
`
`
`
`
`
`
`
`ing on the feature size. The Ta layer is preferably deposited
`
`
`
`
`
`
`
`using standard ion sputtering techniques at a substrate
`
`
`
`
`
`
`
`
`
`temperature ranging from about 20° C. to about 500° C.
`
`
`
`
`
`
`
`However, ion deposition sputtering techniques may be used
`
`
`
`
`to deposit this layer.
`
`
`
`
`
`
`
`The copper layer is deposited at the thickness desired to
`
`
`
`
`
`
`
`
`
`
`the needs of the device. The copper layer may be
`suit
`
`
`
`
`
`
`
`
`deposited using any of the preferred techniques knownin the
`
`
`
`
`
`
`
`
`
`art. Preferably, the entire copper layer or at least a “seed”
`
`
`
`
`
`
`
`layer of copper is deposited using physical vapor deposition
`
`
`
`
`
`techniques such as sputtering or evaporation, as opposed to
`
`
`
`
`
`
`
`
`CVD. Since the crystal orientation of the copperis sensitive
`
`
`
`
`
`
`
`
`to deposition temperature, it is important that the maximum
`
`Page 5 of 9
`
`Page 5 of 9
`
`
`
`
`
`US 6,887,353 B1
`
`
`5
`
`
`
`
`
`
`
`layer structure enables the deposition of an overlying copper
`
`
`
`
`
`
`
`layer having a high <111> crystallographic content, so that
`
`
`
`
`
`
`electromigration resistance of the copper is increased.
`
`I. Definitions
`
`
`
`
`
`
`
`
`
`
`As a preface to the detailed description, it should be noted
`
`
`
`
`
`
`
`
`
`that, as used in this specification and the appended claims,
`
`
`
`
`
`
`
`
`
`the singular forms “a”, “an”, and “the” include plural
`
`
`
`
`
`
`
`
`referents, unless the context clearly dictates otherwise. Thus,
`
`
`
`
`
`
`
`for example, the term “a semiconductor” includes a variety
`of different materials which are known to have the behav-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`ioral characteristics of a semiconductor, reference to a
`
`
`
`
`
`
`“plasma” includes a gas or gas reactants activated by an RF
`
`
`
`
`
`
`
`glow discharge, reference to “the contact material”or“inter-
`
`
`
`
`
`
`
`
`connect material” includes copper and copper alloys, and
`
`
`
`
`
`
`
`other conductive materials which have a melting point
`
`
`
`
`
`
`
`
`enabling them to be sputtered over the temperature range
`described herein.
`
`
`
`
`
`
`
`
`
`Specific terminology of particular importance to the
`
`
`
`
`
`
`description of the present invention is defined below.
`
`
`
`
`
`
`
`
`
`
`
`The term “aspect ratio” refers to the ratio of the height
`
`
`
`
`
`
`dimension to the width dimension of particular openings
`
`
`
`
`
`
`
`into which an electrical contact is to be placed. For example,
`
`
`
`
`
`
`
`
`a via opening which typically extends in a tubular form
`
`
`
`
`
`
`
`
`
`through multiple layers has a height and a diameter, and the
`
`
`
`
`
`
`
`
`aspect ratio would be the height of the tubular divided by the
`
`
`
`
`
`
`
`
`diameter. The aspect ratio of a trench would be the height of
`
`
`
`
`
`
`
`
`the trench divided by the minimal travel width of the trench
`at its base.
`
`
`
`The term “contact via” or “via” refers to an electrical
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`contact having an aspect ratio which is typically greater than
`
`
`
`
`
`
`
`
`1:1. Acontact via most frequently extends through multiple
`
`
`
`
`
`
`
`layers of material to connect one electrically conductive
`element with another.
`
`
`
`
`
`
`
`
`
`
`
`The term “copper” includes alloys of copper of the kind
`
`
`
`
`
`
`
`typically used in the semiconductor industry. The preferred
`
`
`
`
`
`
`
`embodiments described herein were for a copper alloy
`
`
`
`
`
`comprising about 98% by weight copper.
`
`
`
`
`
`
`
`
`The term “feature” refers to contacts, vias, trenches, and
`
`
`
`
`
`
`
`
`
`other structures which make up the topography of the
`substrate surface.
`
`
`
`
`
`
`
`
`
`The term “interconnect” generally refers to conductive
`
`
`
`
`
`
`structures within a semiconductive device. For purposes of
`
`
`
`
`
`
`
`this patent application, electrical contacts in the form of a
`
`
`
`
`
`
`
`
`
`“contact via” or “via” (which has a higher aspect ratio than
`
`
`
`
`
`
`
`conductive lines in trenches, for example) is distinguished
`from other conductive structures which form interconnects.
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`The term “ion-deposition sputtered” and the term “reac-
`
`
`
`
`
`
`
`
`
`tive ion metal plasma (IMP)” refer to sputter deposition
`
`
`
`
`
`
`
`using a particular technique, wherein a high density, induc-
`
`
`
`
`
`
`
`tively coupled RF plasmais positioned between the sput-
`
`
`
`
`
`
`
`
`tering cathode and the substrate support electrode, whereby
`
`
`
`
`
`
`
`
`at least a portion of the sputtered emission is in the form of
`
`
`
`
`
`
`
`
`ions at the time it reaches the substrate surface. Typically,
`
`
`
`
`
`
`
`
`10% or more of the sputtered emission is in the form of ions
`at the time it reaches the substrate surface.
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`The term “traditional sputtering” refers to a method of
`
`
`
`
`
`
`
`
`forming a film layer on a substrate wherein a target is
`
`
`
`
`
`
`
`
`
`sputtered and the material sputtered from the target passes
`
`
`
`
`
`
`
`
`
`between the target and the substrate to form a film layer on
`
`
`
`
`
`
`
`the substrate, and no meansis provided to ionize a substan-
`
`
`
`
`
`
`
`
`
`tial portion of the target material sputtered from the target
`
`
`
`
`
`
`
`before it reaches the substrate. One apparatus configured to
`
`
`
`
`
`
`
`provide traditional sputtering is disclosed in U.S. Pat. No.
`
`
`
`
`
`
`5,320,728, the disclosure of which is incorporated herein by
`
`10
`
`
`
`20
`
`
`
`25
`
`
`
`30
`
`
`
`35
`
`
`
`40
`
`
`
`45
`
`
`
`50
`
`
`
`55
`
`
`
`60
`
`
`
`65
`
`
`
`Page6 of 9
`
`
`6
`
`
`
`
`
`
`reference. In such a traditional sputtering configuration, the
`
`
`
`
`
`
`
`
`percentage of target material which is ionized is less than
`
`
`
`
`
`
`
`
`
`
`10%, more typically less than 1%, of that sputtered from the
`
`target.
`
`
`
`
`
`
`
`The term “XRD”(X-ray Diffraction) refers to a technique
`
`
`
`
`
`
`commonly used to measure crystalline orientation, wherein
`
`
`
`
`
`
`
`radiation over particular wavelengths is passed through the
`
`
`
`
`
`
`
`
`
`to be characterized, and the diffraction of the
`material
`
`
`
`
`
`
`radiation, caused by the material through whichit passes,is
`
`
`
`
`
`
`measured. A map is created which showsthe diffraction
`
`
`
`
`
`
`
`
`pattern,and the crystal orientation is calculated based on this
`
`map.
`
`
`
`
`
`A “traditionally sputtered” tantalum nitride-comprising
`
`
`
`
`
`
`
`film or layer is deposited on a substrate by contacting a
`
`
`
`
`
`
`
`
`
`tantalum target with a plasmacreated from an inert gas such
`
`
`
`
`
`
`
`
`as argon in combination with nitrogen gas. A portion of the
`
`
`
`
`
`
`
`
`
`tantalum sputtered from the target reacts with nitrogen gas
`
`
`
`
`
`
`
`which has been activated by the plasma to produce tantalum
`
`
`
`
`
`
`
`
`
`nitride, and the gas phase mixture contacts the substrate to
`
`
`
`
`form a layer on the substrate.
`
`
`
`
`
`
`
`
`
`II. An Apparatus for Practicing the Invention
`
`
`
`
`
`
`
`
`A process system in which the method of the present
`
`
`
`
`
`
`
`
`invention maybecarried out is the Applied Materials, Inc.
`
`
`
`
`
`
`
`(Santa Clara, Calif.) Endura® Integrated Processing System.
`
`
`
`
`
`
`
`
`This process system is not specifically shown in the Figures.
`
`
`
`
`
`
`
`However, the system is generally known in the semicon-
`
`
`
`
`
`
`
`ductor processing industry and is shown and described in
`
`
`