`4,638,347
`19)
`United States Patent
`
`
`
`
`
`
`
`Patent Number:
`Date of Patent:
`
`
`
`Jan. 20, 1987
`
`
`
`
`[45]
`Tyer
`
`[11]
`
`
`
`
`GATE ELECTRODE SIDEWALL ISOLATION
`SPACER FOR FIELD EFFECT
`
`
`
`
`TRANSISTORS
`
`SubramanianS. Iyer, Mt. Kisco, N.Y.
`
`
`
`
`International Business Machines
`
`
`
`
`
`
`Corporation, Armonk, N.Y.
`763,897
`
`Aug. 9, 1985
`
`
`Inventor:
`
`
`Assignee:
`
`
`
`Appl. No.:
`Filed:
`
`
`
`
`
`
`
`
`[54]
`
`
`
`[75]
`
`[73]
`
`[21]
`
`[22]
`
`
`
`
`
`
`
`[63]
`
`
`
`[51]
`[52]
`
`
`
`
`[58]
`
`
`
`[56]
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`4,109,372
`8/1978 Geffken ose29/571
`
`
`
`
`
`
`4,227,944 10/1980 Brownetal.
` 148/6
`
`
`
`
`
`
`
`4,252,840 2/1981 Minami........
`. 357/54
`
`
`
`
`6/1982 Ikeda et al. w.sess-secsecsrecnseerees 357/54
`4,337,115
`OTHER PUBLICATIONS
`
`
`IBM Tech. Discl. Bulletin, vol. 24, No. £A, Jun. 1981,
`
`
`
`
`
`
`
`
`
`
`pp. 57-60, vol. 21, No. 3, Aug. 1978, pp. 1250-1251, vol.
`
`
`
`
`
`
`
`
`
`
`24, No. 7A, Dec. 1981, pp. 3415-3416.
`
`
`
`
`
`
`
`
`
`
`Primary Examiner—Martin H. Edlow
`Assistant Examiner—Charles S. Small, Jr.
`
`
`
`
`Attorney, Agent, or Firm—Pollock, Vande Sande &
`
`
`
`
`
`
`
`Priddy
`
`
`ABSTRACT
`[57]
`A sidewall isolation structure for field effect transistor
`
`
`
`
`
`
`
`
`which includes a first electrical insulating layer and a
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`second electrical insulating layer contiguous with the
`first layer. The second electrical insulating material is
`
`
`
`
`
`
`
`etched above or below the surface level of the first
`
`
`
`
`
`
`
`
`
`insulating layer to provide recesses in the sidewallisola-
`
`
`
`
`
`
`
`tion structure, and method for the preparation thereof.
`
`
`
`
`
`
`
`
`Related U.S. Application Data
`
`
`
`
`Continuation of Ser. No. 447,543, Dec. 7, 1982, aban-
`
`
`
`
`
`
`
`doned.
`
`Int, CL! ooceeseeeseeseescoees HO1L 29/94; HOLL 29/78
`
`
`
`
`
`
`
`
`WLS. Cl, wccccesssereecseeteseenreneanseser 357/54; 357/23.3;
`
`
`
`
`
`
`
`
`357/23.9; 357/59; 357/23.1
`Field of Search ...........--.0 357/54, 59, 23.3, 23.9,
`
`
`
`
`
`
`
`357/23.1
`
`
`References Cited
`
`
`U.S. PATENT DOCUMENTS
`
`
`
`5/1977 Richman ........-2secceeeenerseees 198/399
`
`
`
`
`
`
`4,023,195
`
`
`
`
`
`
`11 Claims, 8 Drawing Figures
`
`
`
`
`
`
`
`
`
`
`
`
`Page 1 of 7
`
`TSMC Exhibit 1018
`
`TSMC Exhibit 1018
`
`Page 1 of 7
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`Se
`
`G.
`
`de
`
`
`
`Page 2 of 7
`
`
`
`|
`
`LZ
`
`
`
`Jan. 20, 1987
`
`
`
`
`
`
`U.S. Patent
`
`|
`
`Sheet 2 of 3
`
`FIG. 4
`
`4,638,347
`
`
`
`
`
`LZNW atVIL.
`afase
`WASYi
`Z Gil
`
`
`
`Page 3 of 7
`
`
`
`U.S. Patent
`
`
`
`Jan. 20, 1987
`
`
`
`
`Sheet30f3
`
`
`
`
`4,638,347
`
`
`
`A 81WA |
`
`ZKNL eM
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`Page 4 of 7 —
`
`|
`
`Page 4 of 7
`
`
`
`1
`
`
`
`4,638,347
`
`
`
`2
`cal
`the present invention
`leakage across the spacer,
`
`
`
`
`
`
`
`
`provides a discontinuous metal film over the sidewall
`
`
`
`
`
`
`
`isolation Jayer rather than a continuous metal film as
`
`
`
`
`
`
`
`obtained in accordance with the above discussed tech-
`
`
`
`
`
`
`
`
`nique.
`Providing a discontinuous film over the sidewall
`
`
`
`
`
`
`isolation spacer prevents the formation of a continuous
`
`
`
`
`
`
`silicon diffusion path over the spacer. This prevents the
`
`
`
`
`
`
`
`
`
`formation of a continuoussilicide film over the spacer
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`and thereby precludes electrical
`leakage across the
`spacer after the unreacted metal has been selectively
`
`
`
`
`
`
`
`
`
`
`etched away.
`
`
`
`
`
`
`
`This discontinuous path is created by recessing the
`
`
`
`
`
`
`
`sidewall isolation layer so that metal deposited thereon
`would be discontinuous over the isolation region. In
`
`
`
`
`
`
`
`particular, the sidewall isolation is fabricated of at least
`
`
`
`
`
`
`two different materials and the composite isolation re-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`gionis then selectively etched in order to create a recess
`therein.
`
`In particular, the present invention is concerned with
`
`
`
`
`
`
`
`a sidewall isolation structure for field effect transistors
`
`
`
`
`
`
`
`
`which structure comprises a first electrical insulating
`
`
`
`
`
`
`material and a second anddifferentelectrical insulating
`
`
`
`
`
`
`
`material. The second electrical insulating material is
`
`
`
`
`
`
`contiguous with and preferably embedded in thefirst -
`
`
`
`
`
`
`
`
`
`
`
`
`
`insulating material. Moreover,
`the second
`electrical
`electrical insulating material is etched aboveor prefera-
`
`
`
`
`
`
`bly below the surface levelofthe first electrical insulat-
`
`
`
`
`
`
`
`
`
`ing material to provide a recess in the sidewall isolation
`
`
`
`
`
`
`
`structure. This,
`in turn, prevents the formation of a
`
`
`
`
`
`
`
`
`continuous metal film over the sidewall isolation struc-
`
`
`
`
`
`
`
`
`ture.
`
`Another aspect of the present invention is a process
`
`
`
`
`
`
`for preparing sidewall isolation for field effect transis-
`
`
`
`
`
`
`
`
`tors. The process comprises providing a first electrical
`
`
`
`
`
`
`
`insulating layer over at least the sidewalls of an electri-
`
`
`
`
`
`
`
`cally conductive region. A second and different electri-
`
`
`
`
`
`
`
`cal insulating layer is provided adjacentthefirst electri-
`
`
`
`
`
`
`
`
`cal insulating layer on at least the sidewalls of the con-
`
`
`
`
`
`
`
`
`
`
`ductive region.
`Although the present invention can be practiced with
`
`
`
`
`
`
`
`only twolayers, it is preferred to providea third electri-
`
`
`
`
`
`
`
`cal insulating layer adjacent the second and different
`
`
`
`
`
`
`
`
`insulating layer on at least the sidewalls. The third elec-
`
`
`
`
`
`
`
`
`trical insulating layer, if provided, can have substan-
`
`
`
`
`
`
`
`
`tially the sameora different etch rate as does the second
`
`
`
`
`
`
`
`
`
`insulating layer orthefirst insulating layer. However,it
`
`
`
`
`
`
`
`is preferred that such a third layer have an etch rate
`
`
`
`
`
`
`
`
`
`substantially the sameas that ofthefirst electrical insu-
`
`
`
`
`
`
`
`
`lating layer. The layers are then etched whereby the
`
`
`
`
`
`
`
`
`
`secondlayer is etched at a rate different than the first
`
`
`
`
`
`
`
`
`layer to thereby provide recesses in the sidewall isola-
`
`
`
`
`
`
`
`tion. Preferably the second layer is etched at a rate
`
`
`
`
`
`
`
`faster than the first layer and third layer, if present,
`
`
`
`
`
`
`
`
`
`
`resulting in a recess below the surface level of the first
`
`
`
`
`
`
`
`
`
`
`
`and third layers.
`BRIEF DESCRIPTION OF DRAWINGS
`
`
`
`FIGS. 1-8 are. cross-sectional views of a simplified
`
`
`
`
`field effect transistor in various stages of fabrication
`
`
`
`
`
`
`
`according to the present invention.
`
`
`
`
`BEST AND VARIOUS MODES FOR CARRYING
`
`
`
`
`
`OUT INVENTION
`
`
`For convenience, the discussion of the fabrication
`
`
`
`
`
`
`
`steps is directed to the preferred aspect of employing a
`
`
`
`
`
`
`p-type silicon substrate as the semiconductive substrate
`
`
`
`
`
`
`and n-type impurities. This leads to the n-channel FET
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`GATE ELECTRODE SIDEWALL ISOLATION
`
`
`
`
`SPACER FOR FIELD EFFECT TRANSISTORS
`
`
`
`
`
`
`This application is a continuation of application Ser.
`
`
`
`
`
`No. 447,543,filed Dec. 7, 1982, now abandoned.
`
`
`
`
`
`
`
`DESCRIPTION
`
`
`1. Technical Field
`
`
`
`Thepresentinvention is concerned with certain side-
`
`
`
`
`
`
`
`wall isolation structures for field effect transistors. In
`
`
`
`
`
`
`
`
`particular, the present invention is concerned with a
`
`
`
`
`
`
`sidewall isolation structure for field effect transistors
`
`
`
`
`
`
`
`whichstructure contains a plurality of electrical insulat-
`
`
`
`
`
`
`ing materials. The present invention is also concerned
`
`
`
`
`
`
`
`with a process for fabricating the sidewall
`isolation
`
`
`
`
`
`
`
`structure and, particularly, for fabricating a sidewall
`
`
`
`
`
`
`isolation structure having a plurality of insulating mate-
`
`
`
`
`
`
`rials.
`
`
`
`
`2. Background Art
`The metallic type electrical connections to the
`
`
`
`
`
`
`
`source, drain, and gate regionsofa field effect transistor
`
`
`
`
`
`
`
`
`can be achieved by various processes. One such proce-
`
`
`
`
`
`
`
`dure involves the selective reaction of a metal such as
`
`
`
`
`
`
`
`titanium, cobalt, palladium, or nickel with exposedsili-
`
`
`
`
`
`
`
`con to obtain self-aligned contacts to the source, drain,
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`and gate regions of the device. Achieving self-align-
`mentis significant in the fabrication offield effect tran-
`
`
`
`
`
`
`
`sistors since one of the most crucial steps in preparing
`
`
`
`
`
`
`
`
`FETdevices is a lithographic masking step which re-
`
`
`
`
`
`
`
`
`
`
`
`
`
`quires high precision in registration (i.e., relative mask-
`to-mask alignment) and extreme care in execution.
`
`
`
`
`
`
`With respect to the above procedure for achieving
`
`
`
`
`
`
`
`self-alignment of metallic type contacts to the source,
`
`
`
`
`
`
`
`drain, and gate regions of a FET device,it is important
`
`
`
`
`
`
`
`
`to maintain the electrical isolation of the gate from the
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`source and drain regions. This is accomplished by pro-
`viding an isolation or electrical insulation layer on the
`
`
`
`
`
`
`sidewalls of the gate (which can be referred to as
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`“spacer”) and between the gate and semiconductor
`substrate. To obtain self-aligned contacts, a metal is
`
`
`
`
`
`
`deposited over the entire region (the source, drain, gate,
`
`
`
`
`
`
`
`
`
`and overthe sidewall isolation between the gate and the
`
`
`
`
`
`
`
`
`
`
`source and drain regions). Subsequentto this, the metal
`
`
`
`
`
`
`
`
`is reacted with the available exposed silicon which it
`
`
`
`
`
`
`
`
`contacts to form a metallic silicide. Since the sidewalls
`
`
`
`
`
`
`
`are of an isolation material such as an oxide ornitride,
`
`
`
`
`
`
`reaction between the metal and the sidewall should not
`
`
`
`
`
`
`
`
`
`occurto form silicide. Subsequentto this, the unreacted
`
`
`
`
`
`
`
`metal on the sidewall isolation can then be selectively
`
`
`
`
`
`
`
`etched away.
`
`
`However,it has been observed in attempting to pre-
`
`
`
`
`
`
`pare devices by the procedure discussed above, that
`
`
`
`
`
`
`
`
`although free silicon is not present on the sidewalls,
`
`
`
`
`
`
`
`
`nonetheless, metallic silicides have formed thereon.
`
`
`
`
`
`
`in turn, causes electrical
`leakage between the
`This,
`
`
`
`
`
`
`
`
`source, drain, and gate areas across the spacer paths.It
`
`
`
`
`
`
`
`
`
`is not entirely understood as to what causesthesilicide
`
`
`
`
`
`
`
`
`formation on the sidewalls, but it is believed that possi-
`
`
`
`
`
`
`
`bly silicon is diffused through the metal on the sidewall
`
`
`
`
`
`
`
`
`due to the temperatureofthe silicide formation and this
`
`
`
`
`
`
`
`
`leads to silicide formation there. This is particularly
`
`
`
`
`
`
`
`noticeable when employing metals such as cobalt and
`
`
`
`
`
`
`
`titanium to form thesilicide.
`
`
`
`
`DISCLOSURE OF INVENTION
`
`
`In order to prevent possible diffusion paths on the
`
`
`
`
`
`
`
`
`silicon over the spacer and thereby eliminating electri-
`
`
`
`
`
`
`
`
`
`20
`
`25
`
`
`
`30
`
`35
`
`
`
`40
`
`
`
`45
`
`
`
`50
`
`35
`
`
`
`
`
`65
`
`
`
`Page 5 of 7
`
`Page 5 of 7
`
`
`
`4,638,347
`
`15
`
`
`
`20
`
`
`
`25
`
`
`
`30
`
`
`35
`
`
`
`
`45
`
`
`30
`
`55
`
`
`
`3
`
`
`
`
`
`
`technology. Accordingly,it is understood that a n-type
`
`
`
`
`
`
`
`substrate and a p-type diffused or implanted dopant
`
`
`
`
`
`
`
`impurity can be employed according to the present
`
`
`
`
`invention in p-channe] FET technology.
`It is understood that when the discussion refers to
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`n-type impurities, the process steps are applicable to
`
`
`
`
`
`
`
`
`p-type impurities and vice versa. Also, when reference
`
`
`
`
`
`
`
`
`is made to impuritiesof the ‘‘first type” and to impurities
`
`
`
`
`
`
`
`
`of a “second type”, it is understood that the “first type”
`
`
`
`
`
`
`
`
`refers to the opposite conductivity. Thatis, if the “first
`
`
`
`
`
`
`
`
`
`
`type”is p, then the “second type”is n. If the “first type”
`
`
`
`
`
`
`
`is n, then the “second type”is p.
`
`
`
`
`
`
`Although the fabrication process is described em-
`
`
`
`
`
`
`ploying the preferred material, polycrystalline silicon,
`
`
`
`
`
`other suitable materials can be employed.
`
`
`
`
`
`
`Referring to FIG. 1, there is shown a p-type silicon
`
`
`
`
`
`
`
`substrate 2 having any desired crystal orientation (e.g.,
`
`
`
`
`
`
`
`
`<100>). Such can be preparedbyslicing and polishing
`a p-type boule grown in the presence of a p-type dop-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`ant, such as boron ‘following conventional crystal
`
`
`
`
`
`
`
`growth techniques. Other p-type dopants for silicon
`
`
`
`
`
`include aluminum, gallium, and indium.
`Field oxide isolation 12 can be fabricated by any of
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`the several known procedures including thermal oxida-
`
`
`
`
`
`tion of the semiconductor substrate or by well-known
`
`
`
`
`
`
`vacuum vapor deposition techniques. Furthermore, the
`field oxide 12 may be formed above the semiconductor
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`surface or it may be partially or fully recessed into the
`semiconductor substrate. An example of one such pro-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`cedure is the fully recessed oxide isolation technique
`disclosed in U.S. Pat. No. 3,899,363, disclosure of which
`
`
`
`
`
`
`
`
`
`
`
`is incorporated herein by reference.
`
`
`
`
`
`
`
`For the purposesofillustration of the procedure of
`the present
`invention, a non-recessed field isolation
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`oxide 12 will be used. The field isolation regions are
`
`
`
`
`
`
`
`generally about 4,000 to about 10,000 angstromsthick.
`
`
`
`
`
`
`
`
`
`Thefield oxide regions 12 and the regions under which
`source and drain regions 4 and 5 are formedare delin-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`eated by employing a lithographic mask. The maskis of
`40
`a transparent material having opaque portions in a pre-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`determined pattern. Next, source and drain regions 4
`
`
`
`
`
`
`
`and 5 are formedin the p-silicon substrate 2, such as by
`thermal diffusion or ion-implantation of an impurity of
`
`
`
`
`
`
`
`
`
`
`
`the n-type. Examples of some n-type impurities for
`
`
`
`
`
`
`
`silicon substrates include arsenic, phosphorus, and anti-
`mony.
`
`
`
`
`
`
`
`
`The field oxide 12 using a photolithographic tech-
`nique is etched from that area where a thin gate oxide
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`insulator layer 3 is to be subsequently grown.
`
`
`
`
`
`
`
`
`A relatively thin gate insulator layer of silicon diox-
`ide 3 (see FIG. 2) is grown on or deposited onto the
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`silicon substrate 2. This gate insulator, which is usually
`about 100 to about 1,000 angstromsthick, can be formed
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`by thermal oxidation of the silicon substrate at about
`800°-1000° C. in the presence of oxygen.
`
`
`
`
`
`
`
`
`
`
`
`
`Next, the gate 6 of the FET is deposited and delin-
`
`
`
`
`
`
`eated by known photolithographic technique. The gate
`
`
`
`
`
`
`
`6 of the FETis of preferably polycrystalline silicon and
`is generally doped to the same conductive type as the
`
`
`
`
`
`
`
`
`source and drain.
`
`
`
`
`
`
`
`
`
`
`Next, a layer 7,ofsilicon dioxide is provided over the
`
`
`
`
`
`
`entire structure including the polycrystalline silicon
`
`
`
`
`
`
`
`
`gate 6 (see FIG. 4). This silicon dioxide layer can be
`grownon or deposited on to the substrate and the gate
`
`
`
`
`
`
`
`65
`
`
`
`
`
`
`
`
`
`6. This layer is usually about 500 to about 1,500 ang-
`stroms thick and can be formed by thermaloxidation of
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`the silicon surface and polycrystalline silicon surface at
`about 800°-1000° C. in the presence of oxygen.
`
`
`
`
`
`
`
`
`
`
`
`4
`
`
`
`
`
`Next, a layer 8 of an electrically insulating material,
`
`
`
`
`
`
`
`
`different from the silicon dioxide, is provided over the
`silicon dioxide. An example of such a materialis silicon
`
`
`
`
`
`
`nitride. Other materials which can be used as layer 7 or
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`layer 8 include oxides such as aluminum oxide and mag-
`nesium oxide.
`
`
`
`
`
`
`
`
`Thesilicon nitride can be formed by chemical vapor
`
`
`
`
`
`
`deposition and is usually about 100 to 1,000 angstroms
`thick.
`
`
`
`
`
`
`
`
`An additionallayer 9 of silicon dioxide is then depos-
`
`
`
`
`
`
`
`ited. The silicon dioxide layer is approximately 500 to
`
`
`
`
`
`
`
`1,500 angstroms thick and may be formed by chemical
`
`
`vapor deposition.
`
`
`
`
`
`
`Throughvertically directional reactive ion etching,
`
`
`
`
`
`
`
`
`silicon dioxide layer 7, silicon nitride layer 8, and silicon
`oxide layer 9 are etchedso thatas to obtain the structure
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`shownin FIG.5. Since the rates of etching ofthesilicon
`
`
`
`
`
`
`
`
`oxide andsilicon nitride employing reactive ion etching
`are substantially the same, no depressions or recesses
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`are formed in the isolation structure employing the
`
`
`
`
`
`
`
`reactive ion etching technique. Typical conditions of
`
`
`
`
`
`
`
`reactive ion etching include using a CF4 gas at about 25
`micronsof prespureat a gas flow rate of about 40 stan-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`dard cubic centimeters per minute and employing about
`20 watts of power, which is equivalent to a power den-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`sity of about 0.073 watts per cm2. These particular pa-
`rameters provide for an etch rate of about 160 ang-
`
`
`
`
`
`
`
`
`
`
`stroms per minute.
`:
`
`
`
`
`The sidewall spacer so formed is about 2000 A wide
`
`
`
`
`
`
`
`at the base. Also, in this process, the source and drain
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`regions are exposed. Source and drain may be formed,
`
`
`
`
`
`
`
`for example, by ion-implantation of n-type dopant at
`
`
`this stage.
`
`
`
`
`
`
`
`Next, the remaining silicon dioxide layer 7, silicon
`nitride layer 8, and silicon dioxide 9 are subjected to a
`
`
`
`
`
`
`
`chemical etch to thereby form recess in the sidewall
`
`
`
`
`
`
`
`isolation as illustrated in FIG. 6. A typical etch em-
`
`
`
`
`
`
`
`
`ployed is phosphoric acid solution at about 180° C. The
`
`
`
`
`
`
`
`silicon nitride is etched to a much greater extent than
`
`
`
`
`
`
`
`the silicon dioxide in the presence of the phosphoric
`
`
`
`
`
`
`
`acid. Accordingly, recess in the sidewall isolation is
`
`
`
`
`
`
`achieved asillustrated in FIG. 6. Generally, the etch
`
`
`
`
`
`
`
`rate ratio oflayer 8 to layers 7 and 9 is at least about 10:1
`
`
`
`
`
`
`
`
`
`
`
`
`
`and, preferably, at least about 100:1.
`Theetching is carried out for about 2-10 minutesto
`
`
`
`
`
`
`
`
`cause a 200-1000 A recess in the sidewall isolation.
`
`
`
`
`
`
`Next, a metal
`layer 10, such as cobalt,
`titanium,
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`nickel, and platinum series metals is deposited over the
`structure such as by sputtering or, preferably, evapora-
`
`
`
`
`
`
`tion. The recesses prevent a continuous metallic film
`
`
`
`
`
`
`
`from forming on the sidewalls ofthe gate, as illustrated
`
`
`
`
`
`
`
`in FIG.7.
`
`
`Next, the metal is reacted with thesilicon at elevated
`
`
`
`
`
`
`
`
`temperature such as about 400° to about 800° C. to
`
`
`
`
`
`
`
`
`
`provide a metallic silicide 11. The preferred metals
`
`
`
`
`
`
`
`employed are cobalt and titanium. The temperatures
`
`
`
`
`
`
`
`employed for the cobalt and titanium are at least about
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`550° C., while those for the platinum type metals are
`about 400° to about 500° C.
`
`
`
`
`
`After formation of the silicide, the unreacted metal
`
`
`
`
`
`
`
`can be removed from thestructure by etching in a mate-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`rial which will not effect thesilicide, but will selectively
`remove the unreacted metal. For instance, with tita-
`
`
`
`
`
`
`
`
`nium, the etch employed can be a solution of 1:1:5 vol-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`umeratio of ammonium hydroxide, hydrogen peroxide,
`
`
`
`
`and water (see FIG.8).
`Whatis claimed is:
`
`
`
`60
`
`
`
`
`
`Page 6 of 7
`
`Page 6 of 7
`
`
`
`
`
`6
`5. The sidewall isolation structure of claim 1 which
`
`
`
`
`
`
`further includes a third electrical insulating material
`
`
`
`
`
`
`
`
`
`
`
`adjacent said second anddifferent electrical insulating
`material.
`
`6. The sidewall isolation structure of claim 5 wherein
`
`
`
`
`
`
`
`said third electrical insulating material has an etch rate
`
`
`
`
`
`
`
`
`different from the etch rate of said second and different
`
`
`
`
`
`
`
`
`
`
`
`
`electrical insulating material.
`7. The sidewall isolation structure of claim 5 wherein
`
`
`
`
`
`
`
`said third electrical insulating material has an etch rate
`
`
`
`
`
`
`
`
`substantially the same as the etch rate ofsaid first elec-
`
`
`
`
`
`
`
`
`
`
`
`
`trical insulating material.
`8. The structure of claim 5 wherein saidfirst electri-
`
`
`
`
`
`
`
`
`
`
`
`
`
`cal insulating material is silicon dioxide.
`9. The structure of claim 8 wherein said second elec-
`
`
`
`
`
`
`
`
`
`
`
`
`
`trical insulating materialis silicon nitride.
`10. The structure of claim 5 wherein said second
`
`
`
`
`
`
`
`
`
`
`
`
`electrical insulating materialis silicon nitride.
`11. The structure of claim 8 whereinsaid third electri-
`
`
`
`
`
`
`
`
`
`
`
`
`
`cal insulating material is silicon dioxide.
`*
`*
`*
`*
`*
`
`
`
`
`
`
`
`
`
`
`
`
`4,638,347
`
`
`5
`1. A sidewall isolation structure for the gate electrode
`
`
`
`
`
`
`
`
`of an insulated gate field effect transistor which com-
`
`
`
`
`
`
`
`
`prises a first electrical insulating material and a second
`
`
`
`
`
`
`
`
`
`
`
`
`
`and different electrical insulating material contiguous
`with said first electrical insulating material, and wherein
`
`
`
`
`
`
`
`
`said second and different electrical insulating material
`
`
`
`
`
`
`
`being etched below the surface levelofsaid first electri-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`cal insulating material and being etched to a greater
`extent than and at a rate faster than said first electrical
`
`
`
`
`
`
`
`
`
`insulating material to provide a recess in said sidewall
`
`
`
`
`
`
`isolation structure wherein said recess is such as to
`
`
`
`
`
`
`
`prevent the formation of a continuous metal film over
`
`
`
`
`
`
`
`the sidewall isolation.
`
`
`
`2. The structure of claim 1 wherein saidfirst electri-
`
`
`
`
`
`
`
`
`
`
`
`
`
`cal insulating material is silicon dioxide.
`3. The structure of claim 2 wherein said second elec-
`
`
`
`
`
`
`
`
`trical insulating material is silicon nitride.
`
`
`
`
`
`4. Thestructure of claim 1 wherein said second elec-
`
`
`
`
`
`
`
`
`trical insulating material is silicon nitride.
`
`
`
`
`
`
`
`
`20
`
`
`
`25
`
`
`
`30
`
`
`
`35
`
`
`
`45
`
`
`
`50
`
`
`
`35
`
`
`
`60
`
`
`
`65
`
`
`
`Page 7 of 7
`