`United States Patent
`4,957,590
`
`Patent Number:
`
`[11]
`
`
`
`
`Sep. 18, 1990
`Date of Patent:
`Douglas
`[45]
`
`
`
`
`
`
`
`
`
`
`
`
`
`VLSI Applications”, J. Electrochem. Soc.: Solid-State
`
`
`
`
`
`
`Science and Technol, vol.
`131, No.
`10, 1984, pp.
`
`
`
`
`
`
`
`
`
`2325-2335.
`
`Donnellyet al., “Anisotropic Etching in Chlorine-Con-
`
`
`
`
`
`
`taining Plasmas”, Solid-State Techol., vol. 24, No. 4,
`
`
`
`
`
`
`
`1981, pp. 161-166.
`
`
`
`Shah, “Refractory Metal Gate Processes for VLSI
`
`
`
`
`
`
`Applications”, ZEEE Trans. on Electron Devices, vol.
`
`
`
`
`
`
`ED-26, No. 4, Apr. 1979, pp. 631-640.
`
`
`
`
`
`
`Primary Examiner—William A. Powell
`
`
`
`
`Attorney, Agent, or Firm—Rodney M. Anderson
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`ABSTRACT
`[57]
`
`
`A method for etching titanium nitride local intercon-
`
`
`
`
`
`
`
`nects is disclosed. A layer of titaniun nitride is either
`
`
`
`
`
`
`
`
`
`formed as a by-product of the formation of titanium
`
`
`
`
`
`
`
`
`silicide by direct reaction or by deposition. The location
`
`
`
`
`
`
`
`
`of the interconnects is defined by patterning photoresist
`
`
`
`
`
`
`
`at the desired locations. A plasma etch using a chlorine-
`
`
`
`
`
`
`
`
`bearing agent such as CCl4 as the etchant etches the
`
`
`
`
`
`
`
`
`
`titanium nitride anisotropically at those locations cov-
`
`
`
`
`
`
`ered by photoresist, and isotropically elsewhere, so that
`
`
`
`
`
`
`
`
`filaments of the titanium nitride are removed without
`
`
`
`
`
`
`
`
`undercutting the photoresist mask. The etch is selective
`
`
`
`
`
`
`
`
`relative to the underlying material, such as a refractory
`
`
`
`
`
`
`
`
`
`metal silicide, refractory metals, or silicon, due to the
`
`
`
`
`
`
`
`
`
`passivation of the underlying material by the carbon
`
`
`
`
`
`
`
`
`atoms of the CCl4. The selectivity, together with the
`
`
`
`
`
`
`
`
`
`selective anisotropy, even allowssignificant overetch of
`
`
`
`
`
`
`
`the material to removethe filaments without undercut-
`
`
`
`
`
`
`
`ting the masked interconnect material.
`
`
`
`
`
`
`
`
`Sep. 5, 1989
`
`
`Related U.S. Application Data
`
`
`
`
`Continuation-in-part of Ser. No. 273,287, Nov. 17,
`
`
`
`
`
`
`
`1988, Pat. No. 4,863,559, which is a continuation of
`
`
`
`
`
`
`
`
`
`Ser. No. 159,282, Feb. 22, 1988, Pat. No. 4,793,896.
`
`
`
`
`
`
`
`
`
`Int, CLS ceeeeccccsccsssssssseee B44C 1/22; CO3C 15/00;
`
`
`
`
`
`
`C03C 25/06; C23F 1/02
`
`
`
`US. Cle seesecssesssssesssessssssssssessen 156/643; 156/646;
`
`
`
`
`156/662; 156/659.1; 204/192.35
`
`
`Field of Search 0... 156/643, 646, 652, 653,
`
`
`
`
`
`
`
`156/655, 656, 657, 659.1, 662, 667; 204/192.32,
`
`
`
`
`
`
`192.35, 192.37; 357/23.1, 65, 67; 437/180, 200,
`
`
`
`
`
`
`228; 252/79.1
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`[54] METHOD FOR FORMING LOCAL
`
`
`
`
`
`INTERCONNECTS USING SELECTIVE
`
`
`ANISOTROPY
`
`
`
`Inventor:
`
`
`Assignee:
`
`
`
`Appl. No.:
`
`Filed:
`
`
`
`
`
`Monte A. Douglas, Coppell, Tex.
`
`
`
`
`Texas Instruments Incorporated,
`
`
`Dallas, Tex.
`
`402,944
`
`
`
`
`
`
`
`
`
`[75]
`
`[73]
`
`
`
`[21]
`
`
`[22]
`
`
`[63]
`
`
`
`[51]
`
`[52]
`
`
`
`[58]
`
`
`
`[56]
`
`
`
`References Cited
`
`
`U.S. PATENT DOCUMENTS
`
`
`
`4,574,177
`3/1986 Wang ....scssccserseresecereteeee 219/121 PE
`
`
`
`
`
`4,657,628 4/1987
`
`
`
`
`4,676,866 6/1987
`
`
`
`
`
`
`4,690,730 9/1987
`
`
`
`
`
`
`4,784,973 11/1988
`
`
`
`
`
`
`
`
`4,793,896 12/1988 Douglas ......sccsssssereerererse 156/643
`
`
`
`
`OTHER PUBLICATIONS
`
`
`Chowetal., “Plasma Etching of Refractory Gates for
`
`
`
`
`
`
`
`
`
`
`
`29 Claims, 4 Drawing Sheets
`
`
`
`
`
`
`
`Page 1 of 10
`
`TSMC Exhibit 1011
`
`TSMC Exhibit 1011
`
`Page 1 of 10
`
`
`
`
`US. Patent—Sep. 18, 1990 Sheetlof2 4,957,590
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`44
`
`38
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`SS
`
`rzeree
`Lip nd
`UPIESSESS
`
`<LALMGy
`
`NAKnH7r
`
`
`
`
`i,
`
`
`
`
`<
`
`
`
`
`
`
`
`
`
`3 WrzLp
`y SASSIZ
`iLilliteiels.
`
`
`
`
`SSS
`
`
`
`
`
`
`
`
`Page 2 of 10
`
`Page 2 of 10
`
`
`
`US. Patent—Sep. 18, 1990 Sheet 2 of 2 4,957,590
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`OX
`
`
`2b
`
`
`
`26
`
`
`
`
`
`
`
`Page 3 of 10
`
`Page 3 of 10
`
`
`
`1
`
`4,957,590
`
`
`
`
`
`10
`
`
`
`15
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`20
`
`25
`
`
`
`
`
`30
`
`
`
`
`
`
`
`45
`
`
`
`50
`
`
`
`
`
`
`
`
`60
`
`
`65
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`METHOD FOR FORMING LOCAL
`
`
`
`
`INTERCONNECTS USING SELECTIVE
`
`
`ANISOTROPY
`
`This application is a continuation-in-part of applica-
`
`
`
`
`
`
`tion S.N. 273,287 filed Nov. 17, 1988, now U.S. Pat. No.
`
`
`
`
`
`
`
`
`
`
`
`4,863,559, which is a continuation of application S.N.
`
`
`
`
`
`
`
`
`159,282 filed Feb. 22, 1988, now U.S. Pat. No. 4,793,896
`
`
`
`
`
`
`
`
`
`
`issued Dec. 27, 1988.
`
`
`
`
`This invention relates in general to semiconductor
`
`
`
`
`
`
`devices, and in particular to an improved method for
`
`
`
`
`
`
`
`
`forming local
`interconnects using chlorine bearing
`
`
`
`
`agents.
`
`
`2
`
`with the n-type dopant through thesilicide intercon-
`
`
`
`
`
`
`
`nect.
`
`Another known method uses molybdenum metalas a
`
`
`
`
`
`
`
`interconnect material. Molybdenum, however,
`local
`
`
`
`
`
`also acts as a diffusion conduit through which phospho-
`
`
`
`
`
`
`
`rus, used to dope n-type regions of the semiconductor
`
`
`
`
`
`
`
`
`device, can diffuse. The molybdenum interconnect
`
`
`
`
`
`therefore is not an effective local interconnect between
`
`
`
`
`
`
`
`n-type and p-type regions, as the p-type regions can be
`
`
`
`
`
`
`
`
`
`undesirably counterdoped by the phosphorousdiffusing
`
`
`
`
`
`through the molybdenum,similarly as the silicide strap
`
`
`
`
`
`
`
`interconnect.
`
`Anotherlocal interconnection method is disclosed in
`
`
`
`
`
`
`
`U.S. Pat. No. 4,675,073, issued to me on June 23, 1987,
`
`
`
`
`
`
`
`
`
`
`
`
`and assigned to Texas Instruments Incorporated, incor-
`
`
`BACKGROUND OF THE INVENTION
`
`
`
`
`porated herein by this reference. As disclosed therein,
`
`
`
`
`
`
`
`
`
`
`
`the desired local interconnect is formed by patterning
`Increasing the number of levels of interconnects
`
`
`
`
`
`
`
`
`
`
`
`
`
`the residual titanium compound, for example titanium
`(both intra-level and inter-level) in integrated circuits
`
`
`
`
`
`
`
`
`
`
`
`
`nitride, from the direct reaction forming titanium sili-
`provides additional routing capability, more compact
`
`
`
`
`
`
`
`
`
`
`
`
`cide cladding of the diffusions and polysilicon gates.
`layouts, better circuit performance and greater use of
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`Thetitanium nitride is sufficiently conductive so thatit
`circuit design within a given integrated circuit surface
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`is useful to make local interconnections between neigh-
`area. A particularly useful level of connection is com-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`monly called local interconnection, where neighboring
`boring regions. The disclosed process uses carbontetra-
`
`
`
`
`
`
`
`
`
`
`
`
`diffused areas are connected to one another, and to
`fluoride (CF4) as the reactant in a plasma etch to re-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`move the undesired titanium nitride faster than titanium
`neighboring polysilicon and metal lines.
`
`
`
`
`
`
`
`
`
`
`
`
`silicide. This plasma etch using carbon tetrafluoride
`For example, a conventional method for creating
`
`
`
`
`
`
`
`
`
`
`
`
`local interconnects uses metal interconnection of dif-
`etches titanium nitride or titanium oxide at approxi-
`
`
`
`
`
`
`
`
`
`
`
`
`
`mately twice the rate it removes titanium silicide. This
`fused regions to one another, as well as to other layers.
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`technique also etches silicon oxides at twice the rate,
`The metal interconnection is formed by etching vias
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`through a thick oxide layer to the locations to be inter-
`and photoresist at five times the rate, as it etches tita-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`connected. A conductor is then formedto fill the vias
`nium nitride or titanium oxide. Additionally, products
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`of the etching process include solids that tend to adhere
`and make the connection. This method is limited, for
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`to the etching device. This requires extra maintenance
`purposesof reducing the area required for such connec-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`and cleanup time that is nonproductive. Thus, a need
`tion, by the state of the technology of etching contact
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`has arisen for a method for producing a local intercon-
`holes and the planarization of interlevel dielectrics.
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`nect with increased selectivity to the refractory metal
`These limitations include the alignment tolerance of the
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`compound ofthe local interconnect(e.g., titanium ni-
`vias to the underlying region to be connected, the size
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`tride or titanium oxide) relative to silicides, silicon ox-
`of the via required (and accordingly the size of the
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`ides and photoresist, so that an additional layer of inter-
`contact area in the underlying region) which can be
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`connection may be more consistently manufactured
`reliably etched, and the step coverage of the conductor
`
`
`
`
`
`
`
`
`
`
`
`
`
`with precisely located interconnects and improved pla-
`in filling the via and making good ohmic contact to the
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`narization compatible with sub-micron technology.
`underlying region. Also, the additional layer of a metal-
`
`
`
`
`
`
`
`
`
`
`
`
`For purposes of forming such smail feature sizes for
`lic conductor across the dielectric contributes to a loss
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`the interconnect,it is well knownthat etches which are
`of planarization in subsequentlevels.
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`substantially anisotropic (i.e., directional) are preferred.
`An alternative methed developed by Hewlett Pack-
`
`
`
`
`
`
`
`
`
`
`
`
`Anisotropic etches provide improved control in fabri-
`ard and published at page 118 of the 1984 [EDM Pro-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`cation, since the patterned masking material more
`ceedings uses additional patterned silicon to provide
`
`
`
`
`
`
`
`
`
`
`
`
`
`closely defines the feature to remain after the etch;
`conductive silicide regions extending over the field
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`etches which are more isotropic tend, of course,
`to
`oxide as desired. A layer of titanium is deposited over
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`undercut the mask, requiring that the size of the pat-
`the substrate and, prior to the direct reaction of the
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`terned masking material be made larger than that of the
`titanium with the underlyingsilicon to form thesilicide,
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`desired feature in order to compensate for the line width
`a thin layerof silicon is patterned on top ofthe titanium
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`loss resulting from the undercut.
`metal to define an interconnect extending overasilicon
`
`
`
`
`
`
`
`
`
`
`
`
`
`However, substantially anisotropic etches can leave
`dioxide region separating the two regions to be inter-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`filaments of the material being etched. Such filaments
`connected. Wherethis silicon layer remains,a silicide is
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`tend to occur at locations where the etched material
`formed during the reaction process extending over the
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`makesa step over surface topography.In the case of the
`oxides. This method requires the deposition and pat-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`local interconnect discussed above, such filaments can
`terning of the additional layer ofsilicon to define the
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`create a short circuit between conductive structures at
`local interconnection. In addition, the resulting silicide
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`the top of, and at the bottom of, a step where no such
`strap provides a conduit through which typical n-type
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`connection is desired. In addition, filaments may be
`dopants such as phosphorouscan diffuse, since titanium
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`present
`laterally, connecting two otherwise uncon-
`silicide is a very poor diffusion barrier to conventional
`
`
`
`
`
`
`
`
`
`
`
`
`
`nected structures.
`semiconductor dopants. If a silicide strap is used to
`
`
`
`
`
`
`
`
`
`It should also be noted that the titanium nitride may
`connect n-type regions to p-type regions, for example
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`be used as a gate material, especially in the case where
`n-doped polysilicon to p-type diffusion, subsequent
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`it is deposited. Similar problems concerning the etch as
`processing must be doneatrelatively low temperatures
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`described above will also affect the etch of such tita-
`to minimize the counterdoping of the p-type region
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`Page 4 of 10
`
`Page 4 of 10
`
`
`
`3
`
`nium gate electrodes, as well as other structures for
`
`
`
`
`
`
`
`
`which a conductive titanium compound may be used.
`
`
`
`
`
`
`
`It is therefore an object of this invention to provide
`
`
`
`
`
`
`
`
`
`
`an etch for the residual material over insulating layers
`
`
`
`
`
`
`
`
`
`remaining from the direct react silicidation which is
`
`
`
`
`
`
`
`
`anisotropic at the locations where the masking layeris
`
`
`
`
`
`
`
`
`
`in place to define the interconnect, but which is iso-
`
`
`
`
`
`
`
`
`
`tropic elsewhere so that filaments of the interconnect
`
`
`
`
`
`
`
`material are removed.
`
`
`
`It is a further object of this invention to provide such
`
`
`
`
`
`
`
`
`
`
`
`an etch which also has improvedetch selectivity (i.e.,
`
`
`
`
`
`
`
`
`
`an increased etch rate ratio) of the interconnectrelative
`
`
`
`
`
`
`
`
`
`to underlying conducting layers.
`
`
`
`
`It is a further object of the present invention to pro-
`
`
`
`
`
`
`
`
`
`vide such an etch with improvedselectivity to titanium
`
`
`
`
`
`
`
`
`nitride or titanium oxide with respect to titanium sili-
`
`
`
`
`
`
`
`
`cide, silicon dioxide and photoresist.
`
`
`
`
`
`It is a further object of the present invention to pro-
`
`
`
`
`
`
`
`
`
`vide such an etch which reduces the preventative main-
`
`
`
`
`
`
`
`
`tenance and cleanup schedules and procedures by the
`
`
`
`
`
`
`
`use of a chlorine bearing agent as opposed to a flourine
`
`
`
`
`
`
`
`
`agent.
`
`Other objects and advantages of the invention will
`
`
`
`
`
`
`
`become apparent to those of ordinary skill in the art
`
`
`
`
`
`
`
`
`
`having reference to the following specification in con-
`
`
`
`
`
`
`
`junction with the drawings.
`
`
`
`
`SUMMARYOF THE INVENTION
`
`
`
`
`The invention may be incorporated into a method for
`
`
`
`
`
`
`
`forming a local interconnect on a semiconductorsur-
`
`
`
`
`
`
`
`face. A dielectric layer of a prefabricated integrated
`
`
`
`
`
`
`circuit is covered with a conductive chemical com-
`
`
`
`
`
`
`
`pound ofa refractory metal, such as titanium. The com-
`
`
`
`
`
`
`
`
`pound may be formed by deposition, or as a by-product
`
`
`
`
`
`
`
`
`of the silicidation of the refractory metal at locations
`
`
`
`
`
`
`
`
`whereit is in contact with the underlying semiconduc-
`
`
`
`
`
`
`
`
`tor. Photoresist is placed over this chemical compound
`
`
`
`
`
`
`
`
`layer to protect a specific portion thereof which will
`
`
`
`
`
`
`
`
`
`serve as an interconnect. A chlorine bearing agentis
`
`
`
`
`
`
`
`
`
`used to etch the exposed conductive chemical com-
`
`
`
`
`
`
`
`pound layer, which occurs in substantially an aniso-
`
`
`
`
`
`
`
`tropic manner at those locations where the photoresist
`
`
`
`
`
`
`
`
`is in place. At those locations where the photoresistis
`
`
`
`
`
`
`
`
`
`
`absent, the etch is substantially isotropic. Accordingly,
`
`
`
`
`
`
`
`the etch removes filaments which may otherwise re-
`
`
`
`
`
`
`
`main upon clearing of the surfaces, without undercut-
`
`
`
`
`
`
`
`ting the photoresist mask. The chlorine bearing agent
`
`
`
`
`
`
`
`etches the conductive chemical compound at a greater
`
`
`
`
`
`
`rate than the underlyingsilicide, or other material used
`
`
`
`
`
`
`
`
`as a conductor.
`
`
`
`BRIEF DESCRIPTION OF THE DRAWINGS
`
`
`
`
`
`For a more complete understanding of the present
`
`
`
`
`
`
`
`invention, and for further advantages thereof, reference
`
`
`
`
`
`
`is now madeto the following description taken in con-
`
`
`
`
`
`
`
`
`
`junction with the accompanying drawings in which:
`
`
`
`
`
`
`
`FIG. 1 is a cross-sectional view of a partially fabri-
`
`
`
`
`
`
`
`
`cated integrated circuit with a titanium chemical com-
`
`
`
`
`
`
`
`pound formed over the entire surface;
`
`
`
`
`
`
`FIG.2 is a cross-sectional view of the device of FIG.
`
`
`
`
`
`
`
`
`1 with patterned masking material added over the area
`
`
`
`
`
`
`
`
`to be protected;
`
`
`
`FIG.3 is a cross-sectional view of an integrated cir-
`
`
`
`
`
`
`
`
`
`cuit with a local interconnect formed in accordance
`
`
`
`
`
`
`
`with the present invention.
`
`
`
`
`FIGS.4a and 46 are cross-sectional views of an inte-
`
`
`
`
`
`
`
`
`
`grated circuit with a local interconnect formed accord-
`
`
`
`
`
`
`ing to an alternate embodiment of the invention.
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`15
`
`
`20
`
`
`25
`
`
`30
`
`
`35
`
`
`
`
`
`
`
`45
`
`50
`
`
`
`35
`
`
`
`
`65
`
`
`
`
`4,957,590
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`4
`
`FIG. 5 is a cross-sectional SEM microphotograph
`
`
`
`
`
`
`illustrating the anisotropy of the etch described herein.
`
`
`
`
`
`
`
`DETAILED DESCRIPTION OF THE
`
`
`
`PREFERRED EMBODIMENTS
`
`
`FIG.1 showsthefirst step utilizing the method of the
`
`
`
`
`
`
`
`
`
`preferred embodiment of the present invention, as di-
`
`
`
`
`
`
`
`rected to an integrated circuit wafer 44. Wafer 44 con-
`
`
`
`
`
`
`
`
`
`tains a semiconducting substrate 10 formed ofsilicon.
`
`
`
`
`
`
`
`
`is
`Field oxide 12, preferably silicon dioxide (SiOz),
`
`
`
`
`
`
`
`
`grownor deposited in selected portions of the surface of
`
`
`
`
`
`
`
`
`
`
`the substrate 10 for isolation of active regions from one
`
`
`
`
`
`
`
`
`
`
`another according to the well known local oxidation
`
`
`
`
`
`
`
`
`(LOCOS)isolation technique; of course, other isolation
`
`
`
`
`
`
`
`techniques suchas trenchisolation mayalternatively be
`
`
`
`
`
`
`
`
`used. The active transistors of the integrated circuit
`
`
`
`
`
`
`
`
`device are formed into the locations of the surface of
`
`
`
`
`
`
`
`
`
`
`substrate 10 not covered with field oxide 12, such loca-
`
`
`
`
`
`
`
`
`
`tions commonly called moat regions. In FIG. 1, a tran-
`
`
`
`
`
`
`
`
`
`sistor 44 is shown having source and drain regions 14
`
`
`
`
`
`
`
`
`
`and 16, respectively, diffused into the moat region be-
`
`
`
`
`
`
`
`
`tween two portionsof field oxide 12. Source and drain
`
`
`
`
`
`
`
`
`
`regions 14 and 16 are generally implanted and subse-
`
`
`
`
`
`
`
`
`quently diffused after the placementofpolysilicon gate
`
`
`
`
`
`
`
`electrode 30 over gate dielectric 24, so that source and
`
`
`
`
`
`
`
`
`
`drain regions 14 and 16 areself-aligned relative to gate
`
`
`
`
`
`
`
`
`
`electrode 30. As described in U.S. Pat. No. 4,356,623,
`
`
`
`
`
`
`
`
`issued Nov. 11, 1982 and assigned to Texas Instruments
`
`
`
`
`
`
`
`
`Incorporated, the incorporation of sidewall oxide fila-
`
`
`
`
`
`
`ments 26 along the side of gate electrode 30 provide for
`
`
`
`
`
`
`
`
`
`
`
`a graded junction, as shown in FIG. 1. FIG. 1 further
`
`
`
`
`
`
`
`
`
`
`
`illustrates a polysilicon layer 42 overlying field oxide 12
`
`
`
`
`
`
`
`
`serving as an interconnect to another portion of the
`
`
`
`
`
`
`
`
`
`integrated circuit, for example extending to another
`
`
`
`
`
`
`
`moat region (not shown) and serving as the gate elec-
`
`
`
`
`
`
`
`
`
`trode for a transistor.
`
`
`
`
`In this embodimentof the invention, source and drain
`
`
`
`
`
`
`
`
`
`regions 14 and 16, and gate electrodes 30 and 42, are
`
`
`
`
`
`
`
`
`
`
`
`clad with a refractory metal silicide such as titanium
`
`
`
`
`
`
`
`
`
`silicide. This cladding is performed by depositing a
`
`
`
`
`
`
`
`
`layer of the refractory metal, and subsequently heating
`
`
`
`
`
`
`
`
`the wafer 44 so that the metal directly reacts with the
`
`
`
`
`
`
`
`
`
`
`
`underlying silicon to form thesilicide, as described in
`
`
`
`
`
`
`
`
`
`U.S. Pat. No. 4,384,301, issued on May 17, 1983 and
`
`
`
`
`
`
`
`
`
`
`assigned to Texas Instruments Incorporated. An exam-
`
`
`
`
`
`
`ple of the conditions for such direct reaction is heating
`
`
`
`
`
`
`
`
`
`
`the wafer 44 in a nitrogen and argon ambient at a tem-
`
`
`
`
`
`
`
`
`
`
`perature on the order of 675° C. Other methods of
`
`
`
`
`
`
`
`
`
`
`achieving the direct reaction may alternatively be used,
`
`
`
`
`
`
`
`
`for example, by use of a single-wafer Rapid Thermal
`
`
`
`
`
`
`
`
`Processor (RTP) where the wafer 44 is rapidly heated
`
`
`
`
`
`
`
`
`
`to the appropriate temperature for a sufficient amount
`
`
`
`
`
`
`
`
`of time to perform the direct reaction described above.
`
`
`
`
`
`
`
`
`
`It has been determined by physical analysis that the
`
`
`
`
`
`
`
`
`
`titanium silicide formed in this manner may notbestoi-
`
`
`
`
`
`
`
`
`
`chiometrically, or chemically, pure titanium silicide, but
`
`
`
`
`
`
`that measurable amounts of other materials such as
`
`
`
`
`
`
`
`silicon oxide and other oxides are also present in the
`
`
`
`
`
`
`
`
`
`film.
`,
`
`As described in said U.S. Pat. No. 4,675,073, where
`
`
`
`
`
`
`
`
`
`titanium is used as the refractory metal, as a result of the
`
`
`
`
`
`
`
`
`
`
`
`direct reaction process a layer of a conductive titanium
`
`
`
`
`
`
`
`compound covers the surface of the wafer 44,including
`
`
`
`
`
`
`
`
`
`the silicide regions. Referring to FIG. 1, source region
`
`
`
`
`
`
`
`
`
`14, drain region 16, and gate electrodes 28 and 42 are
`
`
`
`
`
`
`
`
`
`
`
`shownclad with titanium silicide film 20, 22, 28 and 40,
`
`
`
`
`
`
`
`
`
`
`
`respectively. A layer 43 of residual material containing,
`
`
`
`
`
`
`
`
`for example, titanium nitride if the direct reaction is
`
`
`
`
`
`
`
`
`
`
`Page 5 of 10
`
`Page 5 of 10
`
`
`
`4,957,590
`
`.
`5
`
`performed in a nitrogen atmosphere, remains over the
`
`
`
`
`
`
`
`surface; if a layer of oxide (not shown) is provided over
`
`
`
`
`
`
`
`
`
`the top of the titanium metal layer prior to the direct
`
`
`
`
`
`
`
`
`
`
`reaction, as described in U.S. Pat. No. 4,690,730 issued
`
`
`
`
`
`
`
`
`Sept. 1, 1987 and assigned to Texas Instruments Incor-
`
`
`
`
`
`
`
`
`porated, layer 43 may contain titanium oxide. When
`
`
`
`
`
`
`
`formed in the nitrogen atmosphere, in the event that
`
`
`
`
`
`
`
`
`oxygen is present (at contamination-level concentra-
`
`
`
`
`
`tion) in the titanium metal or in the atmosphere, or from
`
`
`
`
`
`
`
`
`
`
`the underlying silicon dioxide, layer 43 mayalso include
`
`
`
`
`
`
`
`
`titanium oxide, for example in the form of titanium
`
`
`
`
`
`
`
`
`oxynitride (TiO,Ny).
`
`
`Layer 43 will have a thickness on the order of 100 nm
`
`
`
`
`
`
`
`
`
`
`
`over field oxide 12, and will be thinner (e.g., on the
`
`
`
`
`
`
`
`
`
`
`
`order of 40 nm thick) in the locations oversilicide film
`
`
`
`
`
`
`
`
`
`
`
`20, 22, 28 and 40 cladding the underlying silicon or
`
`
`
`
`
`
`
`
`
`
`polysilicon. If desired, the thickness of layer 43 may be
`
`
`
`
`
`
`
`
`
`
`increased by a second deposition of titanium metal after
`
`
`
`
`
`
`
`
`the initial direct reaction, followed by a second direct
`
`
`
`
`
`
`
`
`reaction in a nitrogen atmosphere, as described in U.S.
`
`
`
`
`
`
`
`
`
`Pat. No. 4,676,866 issued June 30, 1987 and assigned to
`
`
`
`
`
`
`
`
`
`
`Texas Instruments Incorporated.
`
`
`
`It should further be noted that the instant invention is
`
`
`
`
`
`
`
`
`
`
`also applicable to other structures, as well as to similar
`
`
`
`
`
`
`
`
`
`
`interconnection structures formed in a different manner.
`
`
`
`
`
`
`For example, layer 43 may alternatively be formed by
`
`
`
`
`
`
`
`
`
`way of deposition, for example by chemical vapor de-
`
`
`
`
`
`
`
`
`position or by sputtering of titanium nitride. If layer 43
`
`
`
`
`
`
`
`
`
`is deposited, it should be noted that the structure may
`
`
`
`
`
`
`
`
`
`not necessarily include a silicide cladding on the sur-
`
`
`
`
`
`
`
`
`faces of the source/drain regions 14 and 16, or on the
`
`
`
`
`
`
`
`
`
`
`gate electrode 30. However, for such a structure the
`
`
`
`
`
`
`
`
`etch process described herein is also beneficial for the
`
`
`
`
`
`
`
`
`selective etching of the interconnect layer 43.
`
`
`
`
`
`
`
`Referring to FIG. 2, the next step in the preferred
`
`
`
`
`
`
`
`
`
`
`embodiment of the present invention is illustrated. A
`
`
`
`
`
`
`
`
`layer of masking material is deposited over layer 43, and
`
`
`
`
`
`
`
`
`
`
`is patterned according to conventional techniques to
`
`
`
`
`
`
`
`remain in the locations of the eventual local intercon-
`
`
`
`
`
`
`
`
`nect, as shown by patterned masking material 46 in
`
`
`
`
`
`
`
`
`FIG. 2. The masking material 46 serves to protect the
`
`
`
`
`
`
`
`
`
`covered portion of layer 43 from subsequent etching.
`
`
`
`
`
`
`
`The patterned masking material 46 may be photoresist,
`
`
`
`
`
`
`
`or a hardmask material such assilicon dioxide.
`
`
`
`
`
`
`
`When photoresist serves as the masking material 46,it
`
`
`
`
`
`
`
`is preferable to clean the surface of wafer 44 prior to
`
`
`
`
`
`
`
`
`
`
`beginning the etching process, by use of an Oz based
`
`
`
`
`
`
`
`
`
`resist descum to establish etch rate uniformity, to pre-
`
`
`
`
`
`
`
`
`vent extended etch initiation periods and to eliminate
`
`
`
`
`
`
`
`
`post-etch scumming problemsor incomplete etching of
`
`
`
`
`
`
`
`layer 48. An O2 descum time equal to the removal of
`
`
`
`
`
`
`
`
`
`
`
`approximately 400A ofresist is sufficient. Wafer 44 is
`
`
`
`
`
`
`
`
`
`then hardbakedat 120° C. for approximately 60 minutes
`
`
`
`
`
`
`
`
`
`in an oven and then O2 descummedagain.It is necessary
`
`
`
`
`
`
`
`
`
`
`to redo the descum if more than a three hour delay is
`
`
`
`
`
`
`
`
`
`
`
`
`incurred after the descum before the local interconnect
`
`
`
`
`
`
`
`
`dry etch described below to avoid incomplete etching
`
`
`
`
`
`
`
`
`of the local interconnect. It should also be noted that
`
`
`
`
`
`
`
`
`
`
`the oxygen descum, if performed after hard bake, will
`
`
`
`
`
`
`
`
`
`removethe resist anisotropically.
`
`
`
`
`After patterning masking material 46, wafer 44 is
`
`
`
`
`
`
`
`placed in any appropriate plasma etching device such as
`
`
`
`
`
`
`
`
`plasma modeetcher, a reactive ion etcher or a micro-
`
`
`
`
`
`
`
`
`waveafter glow, which are well known in the art. In
`
`
`
`
`
`
`
`
`
`
`the preferred embodiment, a plasma mode etcher, not
`
`
`
`
`
`
`
`shown, utilized. The plasma mode etcher comprises a
`
`
`
`
`
`
`
`symmetrical parallel plate reactor, for example with the
`
`
`
`
`
`
`
`substrate grounded. The powered top plate comprises
`
`
`
`
`
`
`
`
`6
`
`graphite or titanium, and the bottom plate may com-
`
`
`
`
`
`
`
`
`prise bare aluminum. The plates are spaced approxi-
`
`
`
`
`
`
`
`mately one centimeter apart, and approximately 200
`
`
`
`
`
`
`
`watts of poweris applied. Radio frequency (RF) energy
`
`
`
`
`
`
`
`
`
`is transmitted between the parallel plates by an RF
`
`
`
`
`
`
`
`
`
`generator. The powered electrode also serves as a gas
`
`
`
`
`
`
`
`
`
`dispersal source similar to a shower head. According to
`
`
`
`
`
`
`
`
`the invention, a chlorine bearing agent such as carbon
`
`
`
`
`
`
`
`
`
`tetrachloride (CCl4) is used as the dry etch reactant in
`
`
`
`
`
`
`
`
`
`
`the plasma mode etcher. Wafer 44 is placed on the
`
`
`
`
`
`
`
`
`
`
`groundedplate which is spaced apart from the powered
`
`
`
`
`
`
`
`
`
`plate by approximately one centimeter. The preferred
`
`
`
`
`
`
`
`substrate temperature is on the order of 50° C.
`
`
`
`
`
`
`
`
`
`Carbontetrachloride is a particularly useful chlorine-
`
`
`
`
`
`
`bearing agent for this etch because it can exhibit low
`
`
`
`
`
`
`
`
`
`
`etch rates of photoresist and silicon dioxide. Carbon
`
`
`
`
`
`
`
`
`tetrachloride also has a carbon center which will serve
`
`
`
`
`
`
`
`
`
`to “poison” the titanium silicide first layers 20, 22, 28
`
`
`
`
`
`
`
`
`
`
`and 40 once layer 43 of the titanium compoundlying
`
`
`
`
`
`
`
`
`
`
`over them has been etched. This poisoning, or surface
`
`
`
`
`
`
`
`
`
`passivation, is due to carbon, probably in the form of a
`
`
`
`
`
`
`
`
`
`
`partially dissociated carbon tetrachloride molecule
`
`
`
`
`
`(such as CCl, where x=1, 2 or 3) reacting with either
`
`
`
`
`
`
`
`
`
`
`
`the titanium orthesilicon in the titaniumsilicide film 20,
`
`
`
`
`
`
`
`
`
`
`
`22, 28 and 40 to form silicon carbide or titanium carbide.
`
`
`
`
`
`
`
`
`
`
`
`Since silicon carbide and titanium carbide are both non-
`
`
`
`
`
`
`
`
`volatile, the reactive sites on the titanium silicide first
`
`
`
`
`
`
`
`
`
`layers 20, 22, 28 and 40 are effectively “tied up”, con-
`
`
`
`
`
`
`
`
`
`
`sumed or covered, thus preventing reaction of layers 20,
`
`
`
`
`
`
`
`
`22, 28 and 40 with the other reactive speciesin the etch,
`
`
`
`
`
`
`
`
`
`
`
`
`namely chlorine. If not passivated, the chiorine in the
`
`
`
`
`
`
`
`
`
`etch is capable of volatilization and etching ofthe tita-
`
`
`
`
`
`
`
`
`
`nium or the silicon in silicide film 20, 22, 28 and 40.
`
`
`
`
`
`
`
`
`
`
`
`
`Moreover, the surface passivation from the chlorocar-
`
`
`
`
`
`
`bon reagents can be of such a magnitude that a polymer
`
`
`
`
`
`
`
`
`film is formed, so that the surface passivation is on a
`
`
`
`
`
`
`
`
`
`
`macroscopic scale rather than a molecular scale.
`
`
`
`
`
`
`Conversely, the reactive carbon containing species
`
`
`
`
`
`
`will react with the nitrogen componentofthe titanium
`
`
`
`
`
`
`
`
`
`nitride in layer 43 to form CN or CN2,each of whichis
`
`
`
`
`
`
`
`
`
`
`
`
`
`volatile. If oxygen is present in layer 43, the reactive
`
`
`
`
`
`
`
`
`
`
`carbon containing species will react with the oxygen to
`
`
`
`
`
`
`
`
`
`form carbon monoxide, also volatile. The residual
`
`
`
`
`
`
`
`atomic chlorine radicals will react with the titanium
`
`
`
`
`
`
`
`
`componentin the titanium nitride of layer 43 to form
`
`
`
`
`
`
`
`
`
`
`titanium chloride (TiCl, where x= 1-4), which is also
`
`
`
`
`
`
`
`
`
`volatile. Thus, the titanium nitride of layer 43 whichis
`
`
`
`
`
`
`
`
`
`
`not protected by patterned masking material 46 will be
`
`
`
`
`
`
`
`
`
`etched, while leaving the titanium silicide first layers 20,
`
`
`
`
`
`
`
`
`
`22 28 and 40, field oxide 12, and patterned masking
`
`
`
`
`
`
`
`
`
`
`material 46.
`
`
`This mechanism, where the carbon from the carbon
`
`
`
`
`
`
`
`
`tetrachloride builds a residue on the material which is
`
`
`
`
`
`
`
`
`
`not to be substantially etched, but which reacts with
`
`
`
`
`
`
`
`
`
`nitrogen in the titanium nitride film to form volatile
`
`
`
`
`
`
`
`
`
`cyanogen (and with oxygen to form volatile carbon
`
`
`
`
`
`
`
`
`monoxide), can apply to other underlying layers having
`
`
`
`
`
`
`
`
`the same property as the titanium silicide. These other
`
`
`
`
`
`
`
`
`
`underlying layers can be either insulating or conduc-
`
`
`
`
`
`
`
`tive. Examples of conductive material which are be-
`
`
`
`
`
`
`
`lieved to have the property of being unable to volatilize
`
`
`
`
`
`
`
`
`
`the carbon, and which therefore will have a residue
`
`
`
`
`
`
`
`
`buildup thereupon when the titanium nitride is etched
`
`
`
`
`
`
`
`with the carbon tetrachloride etch described above,
`
`
`
`
`
`
`include silicon, cobalt silicide, tungsten, molybdenum,
`
`
`
`
`
`among others.
`
`
`In order to initiate the plasma, it is necessary to de-
`
`
`
`
`
`
`
`
`
`
`tach electrons from the chlorocarbon anions present in
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`20
`
`25
`
`
`
`
`
`30
`
`
`
`35
`
`
`
`
`
`45
`
`
`
`50
`
`55
`
`
`
`
`
`
`
`65
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`Page6 of 10
`
`Page 6 of 10
`
`
`
`7
`
`the plasma gas. Because neutral chlorocarbon species
`
`
`
`
`
`
`
`have high cross-sections for electron attachment, the
`
`
`
`
`
`
`
`reaction chamber tends to become depleted of free
`
`
`
`
`
`
`
`
`electrons, which are crucial to the ignition of the plasma
`
`
`
`
`
`
`
`
`
`
`by the mechanism of electron-impact ionization of other
`
`
`
`
`
`
`
`
`atomic and molecular species. Such electron-impact
`
`
`
`
`
`
`ionization is generally required to ignite the plasma
`
`
`
`
`
`
`
`
`once the avalanche condition is reached. As is well
`
`
`
`
`
`
`
`
`
`knownin the art, the electron is an important charged
`
`
`
`
`
`
`
`
`
`
`species in plasma ignition since its low massallowsit to
`
`
`
`
`
`
`
`
`
`
`
`be sufficiently energized by an RFelectric field to ion-
`
`
`
`
`
`
`
`
`
`ize a neutral species.
`
`
`
`
`A useful method according to the invention for gen-
`
`
`
`
`
`
`
`