`5,091,047
`
`
`
`
`Feb. 25, 1992
`
`
`
`
`Ulllted States Patent
`
`
`Cleeves et al.
`
`
`[19]
`
`,
`US005091047A
`[11] Patent Number:
`
`
`
`
`
`
`[45] Date of Patent:
`
`
`
` .
`
`[54] PLASMA ETCHING USING A BILAYER
`
`
`
`
`
`MASK
`
`
`[75]
`
`
`
`Inventors:
`
`
`
`.
`
`James M. Cleeves, Redwood City;
`
`
`
`
`
`
`
`
`James G. Heard; Zoilo c. H. Tan,
`both Of Cupertino, all of Calif.
`
`
`
`
`
`‘
`.
`-
`-
`
`
`
`
`
`
`[73] A5513"66' Sggmégffémndmm corp" sama
`
`
`
`
`
`
`
`
`
`
`
`[21] Appl‘ No" 733,473
`
`
`
`
`
`[22] Filed:
`Jul. 22, 1991
`
`’
`Related US. Application Data
`
`
`
`
`
`
`
`
`
`
`
`
`Division of Ser No 210‘ 2“ Jun‘ 17 1988 Pat No
`5,045,150
`'
`'
`’
`’
`'
`'
`’
`'
`
`
`
`
`
`
`
`
`
`
`
`’
`
`
`
`[62]
`
`
`
`[51]
`
`
`
`
`
`
`
`
`Int. Cl.5 ...................... .. B44C 1/22; c03C 15/00;
`
`
`
`
`C03C 25/06; C23F'1/00
`
`
`
`
`
`[52] US. Cl. .................................. .. 156/643; 156/646;
`156/653; 156/656; 156/657; 156/659.1;
`
`
`
`
`l56/661.1; 156/904; 204/ 192.37
`
`
`
`
`[58] Field of Search ............. .. 156/643, 646, 653, 656,
`
`
`
`
`
`
`
`
`156/657, 659.1, 661.1, 904; 204/192.32, 192.37;
`
`
`
`
`
`
`252/79.l; 427/38, 39
`
`
`
`[56]
`
`
`
`
`
`
`References Cited
`US, PATENT DOCUMENTS
`
`
`
`5/1978 Hoepfner ..................... 156/661.1X
`4,092,210
`
`
`
`
`
`4,484,978 11/1984 Keyser ................................ 156/643
`
`
`
`
`
`
`
`
`Primary Examiner——-William A. Powell
`
`
`
`
`
`Attorney, Agent, or Firm—Townsend and Townsend
`
`
`ABSTRACT
`[57]
`
`
`
`
`
`
`
`
`A bilayer mask is utilized for etching a primary layer,
`which may be either an aluminum metallization layer or
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`a dielectric layer. The bilayer mask includes both a thin
`resist layer and a metal imaging layer. The thin resist
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`layer provides for high resolutiOn patterning of the
`
`
`
`
`
`
`
`
`metal imaging layer. The metal imaging layer, in turn,
`
`
`
`
`
`
`provides for durability to withstand subsequent plasma
`
`
`
`
`
`etching of the underlying primary layer.
`
`
`
`7 Claims, 1 Drawing Sheet
`
`
`
`
`
`
`“ ‘\ \‘ \‘ \‘ “ \‘ “ \1
`/6
`
`""""""""'4
`
`&\\\\\\\\\\\\\\\\: l4
`
`
`
`
`“'
`
`ll'llllll'I'Illlll.‘
`
`n\\\\\\\\\\\\\\\\\\\‘~
`
`\\\\\\\\\\\\\\\"
`
`Page 1 0f 4
`
`TSMC Exhibit 1034
`
`TSMC v. IP Bridge
`IPR2016-01377
`
`Page 1 of 4
`
`TSMC Exhibit 1034
`TSMC v. IP Bridge
`IPR2016-01377
`
`
`
`
`
`US. Patent
`
`Feb. 25, 1992
`
`
`
`
`
`5,091,047
`
`
`
`“ ‘\ “ \‘ “ “ “ “ \‘u
`'IIIIIIIIIIIIIIIIJ
`
`
`
`&\\\\\\\\\\\\\\\\l
`
`
`
`
`
`
`
`s\\\\\\\\\\\\\\\\\\\‘~
`
`“'
`
`llll’lllll’l’lllll.‘
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`Page 2 0f 4
`
`Page 2 of 4
`
`
`
`
`PLASMA ETCHING USING A BILAYER MASK
`
`
`
`
`
`
`1
`
`5,091,047
`
`This is a division of application Ser. No. 07/210,211
`
`
`
`
`
`filed June 17, 1988, now US. Pat. No. 4,045,150.
`
`
`
`
`
`
`
`
`
`BACKGROUND OF THE INVENTION
`
`
`
`1. Field of the Invention
`
`
`
`
`The present invention relates generally to the field of
`
`
`
`
`
`
`
`semiconductor fabrication, and more particularly to a
`
`
`
`
`
`
`
`
`
`
`
`
`
`method for plasma etching using a bilayer mask in order
`to define very small geometries on a semiconductor
`
`
`
`
`
`
`
`substrate.
`
`
`
`
`
`
`2. Description of the Background Art
`As the drive to increase device density continues, it
`
`
`
`
`
`
`becomes increasingly necessary to be able to define
`
`
`
`
`
`
`
`
`very small geometries on the surface of a semiconduc-
`
`
`
`
`
`
`tor substrate. To form such small geometries, it is highly
`
`
`
`
`
`
`
`. desirable to use very thin resist layers which provide for
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`precise replication of the projected masking pattern.
`
`
`
`
`
`
`
`
`Image resolution and definition are lost as‘the thickness
`
`
`
`
`
`of the photoresist layer increases.
`
`
`
`
`
`
`
`
`The ability to utilize very thin photoresist layers,
`however, is limited by the need to provide a resist layer
`
`
`
`
`
`
`
`25
`which is sufficiently thick to withstand the etching of
`
`
`
`
`
`
`
`
`
`
`
`
`
`the underlying layer which is being patterned through
`the resist mask. In particular, plasma etching often re-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`quires a relatively thick resist layer since it is a relatively
`
`
`
`
`
`
`
`
`lengthy process and many etchant gases directly attack
`the resist material. For that reason, the resist layers used
`
`
`
`
`
`
`
`
`
`
`as masks in plasma etching processes are often too thick
`
`
`
`
`
`
`
`
`
`to allow for submicron geometries, as is frequently
`
`
`
`
`
`
`
`
`desired.
`
`For the above reasons, it would be desirable to pro-
`
`
`
`
`
`
`
`vide methods which would combine the advantages of
`
`
`
`
`
`
`
`a thin resist layer, i.e., high image resolution, definition,
`
`
`
`
`
`
`
`
`
`and control, with the ability to withstand the relatively
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`harsh conditions associated with plasma etching.
`SUMMARY OF THE INVENTION
`
`
`
`
`
`
`
`
`
`
`The present invention provides for high resolution
`plasma etching of a primary layer on a semiconductor
`
`
`
`
`
`
`
`
`
`
`
`
`substrate and is particularly suitable for forming submi-
`cron geometries. The present invention utilizes a bilayer
`
`
`
`
`
`
`
`mask, including a metal image layer formed over the
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`primary layer and a very thin resist layer formed di-
`rectly over the metal image layer. The thin resist layer
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`is patterned by conventional
`techniques, where the
`thinness of the layer allows for a very high resolution
`
`
`
`
`
`
`
`
`and definition of the desired pattern. The resist mask is
`
`
`
`
`
`
`
`
`then used to etch the metal image layer under condi-
`
`
`
`
`
`
`
`
`
`tions which are highly selective for the metal over the
`
`
`
`
`
`
`
`
`
`
`resist. The metal image layer mask is then used to pat-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`tern the primary layer under more rigorous plasma etch
`conditions.
`
`In a first exemplary embodiment, the primary layer is
`
`
`
`
`
`
`
`aluminum and the metal image layer is chromium. The
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`chromium layer is patterned using the resist mask and a
`conventional wet chromium etchant, such as ceric am-
`
`
`
`
`
`
`monium sulfate-based etchants. The resulting chromium
`
`
`
`
`
`
`mask is then used to pattern the underlying aluminum
`
`
`
`
`
`
`
`
`
`
`
`
`
`layer, typically with a chlorine plasma etch.
`In a second exemplary embodiment,
`the primary
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`layer is an organic or inorganic dielectric and the metal
`image layer is aluminum. The aluminum is wet or dry
`
`
`
`
`
`
`
`etched using the thin layer resist as a mask, and the
`
`
`
`
`
`
`
`
`
`
`patterned aluminum layer in turn acts as a mask for
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`plasma etching the dielectric. A fluorine plasma etch is
`
`
`
`
`
`65
`
`Page 3 0f 4
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`5
`
`10
`
`
`
`15
`
`20
`
`
`
`
`
`30
`
`35
`
`
`
`
`
`45
`
`
`
`50
`
`55
`
`
`
`
`
`
`2
`
`typically used with inorganic dielectric layers, such as
`
`
`
`
`
`
`
`silicon oxide and silicon nitride, while an oxygen plasma
`
`
`
`
`
`
`
`
`may be used with organic polymeric dielectrics.
`
`
`
`
`
`
`BRIEF DESCRIPTION OF THE DRAWINGS
`
`
`
`
`FIG. 1 illustrates a conventional semiconductor sub-
`
`
`
`
`
`
`
`
`
`
`
`
`
`strate having a primary layer, a metal image layer, and
`a resist layer formed successively over its surface.
`
`
`
`
`
`
`
`FIG. 2 illustrates the structure of FIG. 1, wherein the
`
`
`
`
`
`
`
`
`
`
`
`resist layer has been patterned.
`FIG. 3 illustrates the structure of FIG. 2, wherein the
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`metal image layer has been patterned using the resist
`layer as a mask.
`
`
`FIG. 4 illustrates the structure of FIG. 3, wherein the
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`primary layer has been patterned using the metal image
`layer as a mask.
`
`
`DESCRIPTION OF THE PREFERRED
`
`
`EMBODIMENTS
`
`
`
`
`
`
`Referring generally to FIGS. 1—4, specific methods
`
`
`
`
`
`will be described for fabricating semiconductor devices
`
`
`
`
`
`
`according to the method of the present invention.
`Semiconductor devices are fabricated on silicon
`
`
`
`
`
`
`wafer substrates 10 (a portion of one being illustrated in
`
`
`
`
`
`
`FIGS. 14). Usually, the wafer will include a variety of
`
`
`
`
`
`
`
`
`features (not illustrated) formed on its upper surface,
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`including transistors, resistors, capacitors, and the like.
`
`
`
`
`
`
`According to the present invention, a primary layer
`12, which is either an aluminum layer or a dielectric
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`layer, will be formed over the substrate 10 using con-
`
`
`
`
`
`
`ventional techniques. The primary layer 12 is patterned
`
`
`
`
`
`
`
`using a bilayer mask including a metal imaging layer 14
`and a resist layer 16, which is specifically intended to
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`provide for high resolution plasma etching of the pri-
`mary layer.
`
`
`In a first embodiment of the invention, the primary
`
`
`
`
`
`
`
`
`
`
`
`layer 12 is an aluminum layer formed by conventional
`
`
`
`
`techniques, such as sputter deposition or evaporation.
`Usually, the aluminum layer 12 will be a metallization
`
`
`
`
`
`
`
`
`
`
`
`
`layer intended for interconnecting the various features
`formed on the substrate 10.
`
`
`
`
`When the primary layer 12 is aluminum, the metal
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`imaging layer will be chromium, typically applied by
`
`
`
`
`
`
`sputter deposition or evaporation. The chromium layer
`14 must be sufficiently thick to withstand the subse-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`quent plasma etching of the primary layer 12, as de-
`
`
`
`
`
`
`
`scribed hereinafter. Thicknesses in the range from 100
`
`
`
`
`
`
`
`
`
`to 1009 A, more usually in the range from about 500 to
`1000 A, are suitable.
`
`
`
`In an alternate embodiment, the primary layer 12 is a
`
`
`
`
`
`
`
`
`
`
`
`
`dielectric layer,
`including both inorganic dielectrics
`
`
`
`
`
`
`
`
`
`such as silicon oxide and silicon nitride as well as or-
`
`
`
`
`
`
`ganic dielectrics, such as polyimides. The dielectric
`
`
`
`
`
`
`
`layer 12 is formed by conventional techniques. In the
`case of inorganic dielectrics, such techniques include
`
`
`
`
`
`
`
`thermal oxidation (for silicon oxides) and chemical
`
`
`
`
`
`
`
`vapor deposition (CVD). In the use of organic dielec-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`trics, a liquid resin may be applied by conventional
`
`
`spin-on techniques.
`
`
`
`
`
`
`
`
`For dielectric primary layers 12, the metal imaging
`
`
`
`
`
`
`
`layer 14 will be aluminum. Again, the aluminum layer
`14 will be sufficiently thick to act as a mask during
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`subsequent plasma etching of the primary dielectric
`layer 12. Thicknesses in the range from about 100 to
`
`
`
`
`
`
`
`
`1000 A, more usually in the range from about 200 to 500
`
`
`
`
`
`
`
`
`
`A, are suitable.
`
`
`
`The nature of the resist layer 16 is not dependent on
`
`
`
`
`
`
`
`the nature of the primary layer 12, but must be able to
`
`
`
`
`
`
`
`
`
`
`Page 3 of 4
`
`
`
`5,091,047
`
`
`3
`
`
`
`
`
`
`
`
`protect the underlying metal imaging layer 14. Suitable
`resist materials include photoresists, electron beam re-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`sists, and x-ray resists. The thickness of the resist layer
`
`
`
`
`
`
`
`
`will depend both on the desired image resolution and on
`
`
`
`
`
`
`
`the need to cover irregular surface topographies. With
`
`
`
`
`
`
`
`
`
`planarized surfaces, resists as thin as 0.2 pm may be
`
`
`
`
`
`
`
`employed, providing for etched geometries of 0.5 pm
`and below. In the case of irregular surface topogra-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`phies, resist layers having a thickness in the range from
`
`
`
`
`
`
`
`
`about 1 to 2 pm may find use. The resists are applied by
`
`
`
`
`
`
`conventional spin-on techniques to the desired thick-
`ness, and cured.
`
`
`
`Referring now to FIG. 2, the resist layer 16 is pat—
`
`
`
`
`
`
`
`
`terned by conventional techniques, such as light expo-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`sure for photoresists, electron beam exposure for elec-
`tron beam resist, and x-ray exposure for x-ray resists.
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`After exposure, the resists are developed to provide a
`
`
`
`
`
`
`
`desired mask for subsequent etching of the underlying
`‘
`metal imaging layer 14.
`_
`
`
`
`
`
`
`Once the resist layer 16 has been patterned, it is used
`
`
`
`
`
`
`
`
`as a mask for etching the metal image layer 14, as illus-
`
`
`
`
`
`
`
`
`
`trated in FIG. 3. The chromium metal imaging layer 14
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`may be etched using conventional wet etchants, such as
`ceric ammonium sulfate-based etchants, at room tem-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`perature. The aluminum metal imaging layer 14 may be
`wet etched using a phosphoric/nitric acid mixture, or
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`may be dry etched using a chlorine plasma, such as
`CCI3, CC14, HCl, C12, or BCI3.
`
`
`
`
`
`
`
`
`
`
`
`
`
`After patterning, the metal imaging layer 14 is used as
`
`
`
`
`
`
`
`
`
`
`
`a mask for plasma etching the primary layer 12. In the
`case of an aluminum primary layer 12, a chlorine plasma
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`i employed as described above. In the case of a dielec-
`
`
`
`
`
`
`
`
`
`tric primary layer, the nature of the plasma will depend
`on the nature of the dielectric. In the case of organic
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`dielectrics, such as polyimides, an oxygen plasma is
`suitable. In the case of inorganic dielectrics, such as
`
`
`
`
`
`
`
`
`silicon dioxide and silicon nitride, fluorine plasmas such
`
`
`
`
`
`
`
`
`as CF4, CHF3, and the like, will find use.
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`After etching, the substrate will appear as illustrated
`in FIG. 4, with the resist layer 16 having been removed '
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`during' the plasma etch of the primary layer. If desired,
`the metal imaging layer 14 may be removed by conven-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`tional techniques. The chromium imaging layer can be
`
`
`
`
`
`
`
`removed by wet etching with ceric ammonium sulfate—
`based etchants or with an oxygen plasma. An aluminum
`
`
`
`
`
`
`
`
`
`
`
`
`
`metal imaging layer 14 can be removed by wet etching
`using a phosphoric acid/nitric acid mixture at an ele-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`vated temperature, typically about 70° C., or by dry
`etching with a chlorine-based plasma.
`
`
`
`
`
`10
`
`15
`
`20
`
`25
`
`
`
`
`
`30
`
`35
`
`
`
`
`4
`
`
`
`
`
`
`
`
`
`Use of the present invention provides for high resolu-
`
`
`
`
`
`
`
`tion plasma etching of both aluminum metallization
`
`
`
`
`
`
`
`
`layers and organic and inorganic dielectric layers. By
`
`
`
`
`
`
`
`employing a bilayer mask including both a metal imag-
`
`
`
`
`
`
`
`
`
`
`ing layer and a resist layer, very thin resist layers pro-
`
`
`
`
`
`
`
`
`viding for high resolution and definition can be utilized.
`
`
`
`
`
`
`
`
`
`By then using the photoresist to pattern the metal imag—
`
`
`
`
`
`
`
`
`ing layer, a mask combining both the high resolution of
`
`
`
`
`
`
`
`
`a thin photoresist and the durability of a metal
`is
`achieved.
`
`
`
`
`
`
`
`
`Although the foregoing invention has been described
`
`
`
`
`
`
`
`
`
`in some detail by way of illustration and example for
`
`
`
`
`
`purposes of clarity of understanding, it will be obvious
`that certain changes and modifications may be practiced
`
`
`
`
`
`
`
`
`
`
`
`
`
`within the scope of the appended claims.
`What is claimed is:
`
`
`
`
`
`
`
`
`
`l. A method for etching a silicon dioxide dielectric
`layer on a semiconductor substrate, said method com-
`
`
`
`
`
`
`
`prising:
`forming a layer of aluminum having a thickness in the .
`
`
`
`
`
`
`range from about 100 to 1000 A over the dielectric
`
`
`
`
`
`
`
`
`
`layer;
`
`
`
`
`
`
`forming a thin resist layer having a thickness in the
`
`
`
`
`
`
`
`range from about 0.2 to 2 pm over the aluminum
`_
`layer;
`
`
`
`
`
`
`
`photolithographically patterning the resist layer to
`form a first mask;
`
`
`
`
`
`
`
`
`
`
`
`etching the aluminum layer through the first mask to
`form a second mask;
`
`
`
`
`
`
`
`
`
`
`
`plasma etching the dielectric layer through the sec—
`ond mask with a fluorinated hydrocarbon or oxy—
`
`
`
`
`
`
`
`
`
`
`
`
`
`gen plasma, wherein said plasma etching removes
`
`
`
`
`
`
`
`the resist layer from the aluminum layer.
`2. A method as in claim 1, wherein the resist is a
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`photoresist having a thickness in the range from about
`0.2 to 2 pm.
`
`
`3. A method as in claim 1, wherein the resist is an
`
`
`
`
`
`
`
`electron beam resist having a thickness in the range
`
`
`
`
`
`
`from about 0.2 to 2 pm.
`
`
`
`
`4. A method as in claim 1, wherein the resist is an
`
`
`
`
`
`
`
`
`
`x-ray resist having a thickness in the range from about
`
`
`
`
`
`
`
`
`0.2 to 2 pm.
`
`
`5. A method as in claim 1, wherein the aluminum
`
`
`
`
`
`
`
`
`
`
`layer is formed by sputtering or evaporation.
`6. A method as in claim 1, wherein the aluminum
`
`
`
`
`
`
`layer is wet etched.
`
`
`
`7. A method as in claim 1, wherein the aluminum
`
`
`
`
`
`
`
`
`
`layer is dry etched. t
`t
`t
`t
`i
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`45
`
`
`
`
`
`
`
`
`
`
`
`
`
`50
`
`
`
`55
`
`
`
`65
`
`
`
`Page 4 of 4
`
`Page 4 of 4
`
`