`[11] Patent Number:
`
`
`
`4,506,434
`
`
`
`
`
`Ogawa et al.
`
`
`
`‘[45] Date of Patent:
`Mar. 26, 1985
`
`[19]
`
`4,391,650
`
`
`
`
`
`
`
`
`
`................... .. 29/571 X
`7/1983 Pfeifer et al.
`
`
`
`
`
`
`FOREIGN PATENT DOCUMENTS
`
`
`
`
`
`
`
`3023410
`1/1922 Fed. Rep. of Germany.
`1/1977 Japan .............................1s6/661.1
`2174
`
`
`
`
`
`51872 4/1977 Japan ............................... 156/653
`
`
`
`
`
`OTHER PUBLICATIONS
`
`
`IBM Technical Disclosure Bulletin, vol. 23, No. 8, Jan.
`
`
`
`
`
`
`
`1981, New York, D. W. Ormond, pp. 3694-3697.
`
`
`
`
`
`
`IBM Technical Disclosure Bulletin, vol. 21, No. 7, Dec.
`
`
`
`
`
`
`
`1978, New York, H. B. Pogge, pp. 2734—2735.
`
`
`
`
`
`
`IBM Technical Disclosure Bulletin, Abbas et a1., “Sim-
`
`
`
`
`
`
`
`plified Isolation for an Integrated Circuit”, vol. 25, No.
`
`
`
`
`
`
`
`
`12, May 1983, pp. 6611-6614.
`
`
`
`
`
`Primary Examiner——Brian E. Hearn
`
`
`
`Assistant Examiner—David A. Hey
`
`
`
`Attorney, Agent, or Firm—Armstrong, Nikaido,
`
`
`
`
`Marmelstein & Kubovcik
`
`
`ABSTRACT
`
`[57]
`
`
`
`
`
`
`
`
`
`A method for producing semiconductor devices having
`a substrate, element fabrication areas formed in the
`
`
`
`
`
`
`
`substrate and isolation areas surrounding the element
`
`
`
`
`
`
`
`fabrication areas. The method comprises forming a
`
`
`
`
`
`
`thermal strain absorbing layer on the top surface of the
`
`
`
`
`
`
`
`
`element fabrication areas, forming at least one groove in
`
`
`
`
`
`
`
`an area which is to become the isolation areas, inlaying
`
`
`
`
`
`
`
`
`
`an insulator in the at least one groove, and annealing the
`
`
`
`
`
`
`
`
`
`insulator to make the density thereof uniform.
`
`
`
`
`
`
`
`9 Claims, 21 Drawing Figures
`
`
`
`
`
`
`
`
`[75]
`
`
`[51]
`
`
`[56]
`
`
`
`[54] METHOD FOR PRODUCTION OF
`
`
`
`
`SEMICONDUCTOR DEVICES
`
`
`Inventors: Tetsuya Ogawa, Machida; Nobuo
`
`
`
`
`
`
`
`
`Toyokura, Kawasaki, both of Japan
`
`
`
`
`
`
`Fujitsu Limited, Kawasaki, Japan
`[73] Assignee:
`[21] App]. No.: 414,803
`
`
`
`
`[22] Filed:
`Sep. 3, 1982
`
`
`
`
`
`
`
`
`
`
`_
`[30]
`Foreign Application Priority Data
`sep. 10, 1931 [JP]
`Japan ................................ 56442911
`
`
`
`
`
`
`
`Int. c1.3 ................. .. H01L 21/76; HOIL 21/302;
`
`
`
`
`
`
`
`HOIL 21/20
`
`
`[52] U.S. c1. ...................................... .. 29/571; 29/578;
`
`
`
`
`
`
`29/576 w; 148/1.5; 143/175, 148/187;
`
`
`
`
`156/643; 156/648; 156/662; 357/49
`
`
`
`
`[53] Field of Search ............... .. 29/571, 576 R, 576 13,
`
`
`
`
`
`
`
`29/576 w, 573; 148/174, 175, 187, 1.5; 357/47,
`
`
`
`
`
`
`
`43, 49, 50; 156/643, 648, 653, 661.1, 662
`
`
`
`
`
`
`
`
`References Cited
`
`
`U.S. PATENT DOCUMENTS
`
`
`
`1/1969 Bean et al.
`.. . ... 156/648 X
`3,421,055
`. . . ... . ..
`
`
`
`
`
`
`3/1973 Zoroglu . . .. .
`.. . ... 148/187
`3,719,535
`
`
`
`
`
`8/1978 Bondur et al.
`29/576 W X
`4,104,086
`
`
`
`
`
`3/1980 Khan et al.
`....... 29/S71
`4,192,059
`
`
`
`
`
`
`
`1/1980 Ho et al.
`148/174 X
`4,209,349
`
`
`
`
`
`
`...... ..
`6/1980 Ho et al.
`148/1.5 X
`4,209,350
`
`
`
`
`
`
`2/1981 Anantha et al.
`29/578 X
`4,252,582
`
`
`
`
`
`
`4/1981 Kumar et al.
`29/576 W X
`4,261,763
`.
`
`
`
`
`
`5/1983 Ozawa ............................ .. 29/571 X
`4,385,433
`
`
`
`
`
`
`
`
`
`
`.
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`TSMC Exhibit 1010
`
`Page 1 of 15
`
`
`
`U.S. Patent Mar. 26, 1985‘
`
`
`
`
`
`
`Sheetl of7
`
`
`
`
`4,506,434
`
`
`
`4
`
`
`
`
`
`
`
`24
`
`
`
`
`
`
`
`
`
`
`
`v,5’Z”’7""¢},,';’;/Z?E
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`Fig.2(b)
`
`W9
`
`
`
`
`
`
`5/1/1141‘ 23
`
`
`
`Page 2 of 15
`
`
`
`U.S. Patent Mar. 26, 1985
`
`Sheet2of7
`
`4,506,434
`
`
`
`Fig.2(d )
`
`::
`2‘
`Fig.2(e)
`D
`7]All22
`
`“K 24
`
`D
`
`Fig.2(f)
`
`24
`
`1/
`
`Page 3 of 15
`
`
`
`U.S. Patent Mar. 26, 1985
`
`Sheet3of7
`
`4,506,434
`
` n
`
`43
`
`
`
`a
`
`D
`
`0
`
`‘
`
`e
`
`0
`
`o
`
`0
`
`44
`
`o
`
`
`
`45
`
`4:
`
`7 ‘
`"
`
`~
`‘
`
`Page 4 of 15
`
`Page 4 of 15
`
`
`
`U.S. Patent Mar. 26, 1985
`
`Sheet4of7
`
`4,506,434
`
`Fig. 4(c)
`
`47
`
`46
`
`47 6
`
`43
`
`Fig.(d)
`
`4
`
`46
`
`47
`
`
`
`4 3
`
`::
`
`Fig.(e)
`
`47
`
`46
`
`Page 5 of 15
`
`Page 5 of 15
`
`
`
`
`
`
`
`U.S. Patent Mar. 26, 1985
`
`
`
`Sheet5of7
`
`
`
`4,506,434
`
`
`
`
`
`57'
`
`56
`
`as
`?\‘.K\\\.\‘\\\‘\\\\
`
`
`
`
`
`
`
`
`4
`
`\ F
`
`5(c)
`
`ig.
`
` %
`
`60
`
`
`
`59
`
`57
`
`
`
`Page 6 of 15
`
`Page 6 of 15
`
`
`
`U.S. PatentJ Mar. 26, 1935
`
`
`
`
`
`
`
`
`6
`
`Sheet6of7
`
` 4,506,434
`
`
`
`
`
`
`Fig.
`
`
`
`
`
`
`
`0
`
`
`
`— 6
`
`8
`
`647
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`77
`75
`
`.
`
`
`
`0
`
`.,
`
`°
`
`0
`
`D
`
`O
`
`.
`
`°
`
`0
`
`o
`
`o
`
`
`..
`
`74
`
`
`
`
`75
`
` WA """"i!lA
`
`
`
`
`
`'I_.'£.II.I.I..I.I.I.4 3:
`7/1/11] /g:|\\‘\\\\\\€
`
`76
`
`
`
`
`
`
`
`
`Page 7 of 15
`
`
`
`U.S. Patent Mar. 26, 19854
`
`
`
`
`
`
`Sheet7of7
`
`
`
`4,506,434
`
`
`
`
`Fig. 8(0)
`
`
`
`4
`
` 4
`
`
`
`
`
`
`
`96
`
`
`
`95
`
`
`
`
`[H
`
`
`
`
`
`I
`
`
`
`
`Fig. 8(b)
`
`
`
`
`
`'1/4mmwl.
`
`
`9‘
`
`Page 8 of 15
`
`
`
`1
`
`METHOD FOR PRODUCTION OF
`
`
`
`SEMICONDUCI‘OR DEVICES
`
`
`
`4,506,434
`
`5
`
`
`
`10
`
`15
`
`
`
`20
`
`
`
`25
`
`30
`
`35
`
`
`
`
`
`45
`
`50
`
`55
`
`BACKGROUND OF THE INVENTION
`
`
`
`
`
`
`
`1. Field of the Invention
`
`
`
`
`
`
`
`The present invention relates to methods for produc-
`tion of semiconductor devices, and more specifically to
`
`
`
`
`
`
`an improvement applicable to methods for production
`
`
`
`
`
`
`of buried insulating layers each of which surrounds a
`
`
`
`
`
`
`
`portion of a semiconductor substrate in which elements
`
`
`
`
`
`
`
`
`
`
`
`
`are fabricated, the buried insulating layers functioning
`to isolate from one another, each element fabricated in
`
`
`
`
`
`
`
`
`a chip.
`
`
`2. Description of the Prior Art
`
`
`
`
`
`There is now a tendency irfwhich the dimensions of
`
`
`
`
`
`
`each element is decreased in order to satisfy require-
`
`
`
`
`
`
`ments for a larger quantity of elements fabricated in a
`
`
`
`
`
`
`chip and also for a larger quantity of elements fabri-
`
`
`
`
`
`
`
`
`
`cated in the unit area of a chip. Such requirements are
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`included in the requirements effective to satisfy the
`ultimate purposes for development of LSI’s and further
`
`
`
`
`
`
`
`of VLSI’s. Insofar as the processes for isolating each
`
`
`
`
`
`
`
`
`element fabricated in one chip from one another are
`
`
`
`
`
`
`
`
`
`concerned, a process which is called local oxidation of
`
`
`
`
`
`
`silicon is available, and it is well known that this process
`
`
`
`
`
`
`
`
`has various advantages in the aspects of easy production
`
`
`
`
`
`
`
`of durable wiring which is free from potential discontin-
`
`
`
`
`
`
`
`
`uation thereof and the potential employment of self-
`
`
`
`
`
`
`
`alignment and the like. However, this local oxidation
`
`
`
`
`
`
`
`
`process has drawbacks. The first is the problem of bird’s
`
`
`
`
`
`
`
`
`beak. Referring to FIG. 1, local oxidation of the top
`
`
`
`
`
`
`
`
`surface of a silicon (Si) substrate 11, having a lirriited
`
`
`
`
`
`
`
`area covered by a silicon nitride (Si3N4) layer mask 12,
`
`
`
`
`
`
`
`is accompanied by lateral growth of a silicon dioxide
`
`
`
`
`
`
`(SiO2) layer 13. This lateral growth produces a silicon
`
`
`
`
`
`
`
`
`dioxide (SiO2) layer having a bird’s beak shape which
`
`
`
`
`
`
`
`
`40
`extends under the silicon nitride (Si3N4) layer 12. The
`
`
`
`
`
`
`
`
`
`lateral length A of this bird’s beakcauses a degradation
`
`
`
`
`
`
`of dimensional accuracy. The second is the problem of
`
`
`
`
`
`
`
`strain which is produced in the portion B of the silicon
`
`
`
`
`
`
`
`substrate 11. The portion B directly contacts the layer
`
`
`
`
`
`
`
`
`13 of silicon dioxide (SiOz) which is converted from
`
`
`
`
`
`
`
`
`silicon (Si) during the oxidation process which inevita-
`
`
`
`
`
`
`
`
`bly causes expansion in volume of the nitride. This
`
`
`
`
`
`
`
`strain, appearing in the silicon (Si) layer B, can cause
`
`
`
`
`
`
`
`
`unsatisfactory characteristics in elements fabricated in
`
`
`
`
`
`the silicon (Si) layer. The third is the problem of white
`
`
`
`
`
`
`
`
`
`ribbon. Since it is not easy to completely remove the
`
`
`
`
`
`
`
`
`silicon nitride (Si3N4) layer 12, numerous minute parti-
`
`
`
`
`
`
`
`
`cles of the nitride remain on the surface of the silicon
`
`
`
`
`
`
`
`
`
`(Si) substrate 11 in the form of scattered stains. These
`
`
`
`
`
`
`
`
`residual nitride particles function as a type of mask
`
`
`
`
`
`
`
`
`during oxidation processes carried out in later steps.
`
`
`
`
`
`
`
`The above process results in a local oxidation process
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`which is not necessarily satisfactory for the production
`of a semiconductor device having minute patterns. To
`
`
`
`
`
`
`
`overcome the foregoing drawbacks, a method wherein
`
`
`
`
`
`
`each element is isolated from one another by buried
`
`
`
`
`
`
`
`insulating layers which are grown to fill grooves pro-
`
`
`
`
`
`
`
`
`duced along the surface of a silicon (Si) substrate to
`
`
`
`
`
`
`
`
`
`surround each element, has been developed and is pres-
`
`
`
`
`
`
`
`
`ently being used. Unfortunately, however,
`this im-
`
`
`
`
`
`
`
`proved method has other drawbacks described below,
`
`
`
`
`
`
`
`with reference to the drawings.
`
`
`
`
`
`
`2
`
`
`
`
`
`
`
`
`this
`Depending on the etching process employed,
`improved prior art method is classified into two inde-
`
`
`
`
`
`
`
`
`
`
`pendent categories.
`The first is the case wherein a dry etching process is
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`employed. Referring to FIG. 2(a), the first step is to
`employ a chemical vapor deposition process for the
`
`
`
`
`
`
`
`purpose of growing an insulating layer 22 on a silicon
`
`
`
`
`
`
`
`
`
`
`
`
`
`(Si) substrate 21 which is provided with grooves 23
`surrounding mesa shaped portions 24 in which elements
`
`
`
`
`
`
`are to be fabricated, before a photoresist layer 25 is
`
`
`
`
`
`
`
`
`coated on the uneven surface of the insulating layer 22.
`
`
`
`
`
`
`
`
`As a result, the top surface of the photoresist layer 25
`
`
`
`
`
`
`
`
`becomes flat. Referring to FIG. 2(b), the second step is
`
`
`
`
`
`
`
`
`to employ a dry etching process which has a single
`
`
`
`
`
`
`
`
`etching rate regardless of the quality of the material to
`
`
`
`
`
`
`
`be etched, to the substrate 21 covered by the insulating
`
`
`
`
`
`
`
`layer 22 and by the photoresist layer 25. As a result, the
`
`
`
`
`
`
`
`
`insulating layer 22 remains only in the groove 23, and
`
`
`
`
`
`
`
`
`the top surface of the silicon (Si) substrate 21 becomes
`
`
`
`
`
`
`
`
`uncovered. During this process, however,
`the ion
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`beams employed for the dry etching process readily
`produce damaged areas C along the top surface of the
`
`
`
`
`
`
`
`
`mesa shaped portion 24 of the silicon (Si) substrate 21 in
`
`
`
`
`
`
`
`which elements are to be fabricated. These damaged
`
`
`
`
`
`
`
`
`areas can cause unsatisfactory characteristics for ele-
`
`
`
`
`
`
`
`ments fabricated in the substrate 21. It is quite natural
`
`
`
`
`
`
`
`that the silicon (Si) substrate must be exposed to a plu-
`
`
`
`
`
`
`
`
`rality of high temperature processes such as oxidation
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`and annealing for repairing the damage caused by appli-
`cation of ion implantation processes and the like, during
`
`
`
`
`
`
`
`
`later processes for production of elements therein. Re-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`ferring to FIG. 2(c), since the foregoing high tempera-
`ture processes are involved with non-uniform variation
`
`
`
`
`
`
`
`of density of the insulating layer 22, this variation causes
`
`
`
`
`
`
`
`
`
`strains E1 and/or E2 to occur at the corners of the mesa
`
`
`
`
`
`
`
`shaped portion 24 of the substrate 21 surrounded by the
`
`
`
`
`
`
`buried insulating layer 22. These strains are also param-
`
`
`
`
`
`
`
`
`
`eters for causing unsatisfactory characteristics for ele-
`
`
`
`
`
`
`
`ments fabricated in the substrate 21.
`
`
`
`
`
`The second is the case wherein a wet etching process
`
`
`
`
`
`
`
`
`is employed. Referring to FIG. 2(d), the first step is to -
`
`
`
`
`
`
`
`
`
`employ a dry etching process to remove the photoresist
`
`
`
`
`
`
`layer 25 from the areas on which elements are to be
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`fabricated, leaving the photoresist layer 25 only along
`the grooves. Referring to FIG. 2(e), the second step is
`
`
`
`
`
`
`
`
`to employ a wet etching process to remove the insulat-
`
`
`
`
`
`
`
`
`ing layer 22 from the areas on which elements are to be
`
`
`
`
`
`
`
`
`fabricated, leaving the insulating layer 22 only in the
`
`
`
`
`
`
`
`
`grooves 23. Since the grooves 23 have sharp corners at
`
`
`
`
`
`
`
`
`the bottom and top edges, the density of the insulating
`
`
`
`
`
`
`
`
`
`layer 22 is not entirely uniform and the density thereof
`
`
`
`
`
`
`
`
`is less along the broken lines shown in each of FIGS.
`
`
`
`
`
`
`
`
`
`2(a), 2(b), 2(d) and 2(e) than in the other regions. Since
`
`
`
`
`
`
`
`
`
`
`a material having a lower density has a larger etching
`
`
`
`
`
`
`
`
`rate, recesses D are produced along the edges of the
`
`
`
`
`
`
`
`insulating layers 22 which are buried in the silicon (Si)
`
`
`
`
`
`
`
`
`substrate 21. As a result, the surface of a chip is not flat,
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`causing the possibility of discontinuity and/or‘dimen-
`sional errors for wires which are placed along the sili-
`
`
`
`
`
`
`
`
`
`
`con (Si) substrate 21.
`
`
`
`
`To prevent occurrence of the foregoing recesses D
`
`
`
`
`
`
`along the edges of the insulating layer 22, an annealing
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`process is ordinarily employed after the completion of
`
`
`
`
`
`
`
`
`the insulating layer 22. Albeit this annealing process is
`effective to unify or make uniform the density of the
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`insulating layer 22 even in the portions along the broken
`lines shown in FIG. 2, differences in the amount of the
`
`
`
`
`
`
`
`coefficient of expansion between the material of the
`
`
`
`
`
`
`
`
`
`
`
`
`
`65
`
`Page 9 of 15
`
`Page 9 of 15
`
`
`
`4,506,434
`
`3
`
`substrate and the material of the insulating layer causes
`
`
`
`
`
`
`
`
`stresses to occur along the interfaces of both materials,
`
`
`
`
`
`
`
`since the stresses are concentrated along the edges. As a
`
`
`
`
`
`
`
`
`result, strains E1and/or E2 occur along the edges of the
`
`
`
`
`
`
`
`
`element fabrication areas of the substrate 21 surrounded
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`by the buried insulating layer 22 in FIG. 2(f). These
`
`
`
`
`
`
`
`strains are also parameters for causing unsatisfactory
`characteristics for elements fabricated in the substrate
`
`
`
`
`
`
`21.
`
`
`
`
`4
`
`duction of a semiconductor device in accordance with
`
`
`
`
`
`
`
`
`
`
`
`
`the present invention. Since a thermal strain absorbing
`layer 32 is interleaved between the top surface of a
`
`
`
`
`
`
`
`
`semiconductor substrate 31 and an insulator layer 33
`
`
`
`
`
`
`
`except for the area which is to become a buried insulat-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`ing layer, strains E1 occur along the edges of the ther-
`mal strain absorbing layer 32 rather than along the top
`
`
`
`
`
`
`
`
`
`edges of the element fabrication areas of the semicon-
`
`
`
`
`
`
`
`ductor substrate 31, during an annealing process which
`
`
`
`
`
`
`
`is carried out to make uniform the density of the insulat-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`ing layer 33. During a dry etching process which is
`carried out to remove a portion of the insulating layer
`
`
`
`
`
`
`
`33, damaged areas G are produced in the thermal strain
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`absorbing layer 32 rather than in the semiconductor
`substrate 31. As a result, the portions of the semicon-
`
`
`
`
`
`
`
`
`
`ductor substrate 31 in which elements are to be pro-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`duced are protected from potential strains and damage,
`thereby enabling the characteristics of the elements to
`
`
`
`
`
`
`
`be enhanced. Since the strains E1 do not occur in the
`
`
`
`
`
`
`
`
`
`semiconductor substrate 31 and since the magnitude of
`
`
`
`
`
`
`stress which may cause strains E2 is limited, the amount
`
`
`
`
`
`
`
`
`of strains E2 which occurs along the bottom edges of
`
`
`
`
`
`
`
`
`
`the element fabrication areas 34 of the semiconductor
`
`
`
`
`
`
`
`substrate surrounded by the buried insulating layers is
`
`
`
`
`
`
`also decreased.
`
`
`The requirements for the thermal strain absorbing
`
`
`
`
`
`
`
`layer are (a) that the material will have to be chemically
`
`
`
`
`
`
`
`
`
`stable under an annealing temperature of approximately
`
`
`
`
`
`900“ C. or higher and (b) that the material readily ab-
`
`
`
`
`
`
`
`
`
`
`
`sorbs strains. Exemplary materials satisfying these re-
`
`
`
`
`
`
`
`
`
`
`
`
`
`quirements are polycrystalline silicon (Si), molybdenum
`silicide (MoSi2), tungsten silicide (WSi2), titanium sili-
`
`
`
`
`
`
`
`cide (TiSi2) and tantalum silicide (TaSi2).
`
`
`
`
`
`
`
`Silicon dioxide (SiO2), silicon nitride (Si3N4) and
`
`
`
`
`
`
`aluminum oxide (A1203) can be selected as the material
`
`
`
`
`
`
`of the buried insulating layer.
`
`
`
`
`
`Not only silicon (Si) but also any of the compound
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`semiconductors including galium-arsenic (GaAs), indi-
`um-phosphorus (InP) et al can be selected as the mate-
`
`
`
`
`
`
`rial of the semiconductor substrate.
`
`
`
`
`
`To achieve the foregoing second object, a method for
`
`
`
`
`
`
`
`production of a semiconductor device in accordance
`
`
`
`
`
`with the other embodiment of the present invention
`
`
`
`
`
`
`
`comprises, in addition to the steps specified above for
`
`
`
`
`
`
`
`the method for production of a semiconductor device in
`
`
`
`
`
`accordance with the present invention, a step to pro-
`
`
`
`
`
`
`
`
`duce a conductive layer on the thermal strain absorbing
`
`
`
`
`
`
`
`layer and on the buried insulating layer and a step to
`
`
`
`
`
`
`
`
`
`pattern the conductive layer to a shape corresponding
`
`
`
`
`
`
`to the gate electrode and some of the conductive wires.
`
`
`
`
`
`
`
`
`
`Materials selected as a material for the conductive
`
`
`
`
`
`
`
`layer are molybdenum silicide (MoSi2), tungsten silicide
`
`
`
`
`
`
`
`(WSi2),
`titanium silicide
`(TiSi2),
`tantalum silicide
`
`
`
`
`
`
`(TaSi2) and polycrystalline silicon (Si).
`
`
`
`
`
`BRIEF DESCRIPTION OF THE DRAWINGS
`
`
`
`
`The present invention, together with its various fea-
`
`
`
`
`
`
`
`tures and advantages, can be readily understood from
`
`
`
`
`
`
`
`the following more detailed description presented in
`
`
`
`
`
`
`
`
`
`
`
`conjunction with the following drawings.
`FIG. 1 is a cross-sectional view of a silicon (Si) sub-
`
`
`
`
`
`
`strate showing the position after the completion of a
`
`
`
`
`
`
`
`
`prior art local oxidation process.
`
`
`
`
`
`FIGS. 2(a), 2(b), 2(c), 2(d), 2(e) and 20‘) are cross-sec-
`
`
`
`
`
`
`
`
`
`
`tional views of silicon (Si) substrates, each of which
`
`
`
`
`
`
`
`
`shows the state after the completion of each of the
`
`
`
`
`
`
`
`
`
`
`major steps of a method for production of a buried
`
`
`
`
`
`
`
`
`
`
`
`
`SUMMARY OF THE INVENTION
`
`
`
`An object of the present invention is to provide a
`
`
`
`
`
`
`
`
`method for producing a semiconductor device having a
`
`
`
`
`
`plurality of elements each of which is isolated from one
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`another by buried insulating layers, wherein an im-
`
`
`
`
`
`
`provement is made (a) to prevent strains E1 which may
`otherwise occur along the top edges of the element
`
`
`
`
`
`
`
`
`
`fabrication areas of the semiconductor substrate sur-
`
`
`
`
`
`
`
`rounded by buried insulating layers which function to
`
`
`
`
`
`
`isolate each element from one another, from occurring
`
`
`
`
`
`
`
`
`during an axmealing process which is carried out to
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`unify the density of the insulating layer, (b) to decrease
`the amount of strains E2 which occur along the bottom
`
`
`
`
`
`
`
`
`edges of the element fabrication areas of the semicon-
`
`
`
`
`
`
`
`
`
`
`
`
`
`ductor substrate surrounded by buried insulating layers
`which function to isolate each element from one an-
`
`
`
`
`
`
`
`other during the annealing process which is carried out
`
`
`
`
`
`
`
`
`to unify the density of the insulating layer and (c) to
`
`
`
`
`
`
`
`
`
`
`
`prevent damaged areas C which may otherwise be pro-
`
`
`
`
`
`
`
`duced along the element fabrication areas of a semicon-
`
`
`
`
`
`
`
`
`
`
`
`
`
`ductor substrate surrounded by buried insulating layers,
`
`
`
`
`
`
`
`from being produced during a dry etching process
`which is carried out to remove a part of the insulating
`
`
`
`
`
`
`
`layer which is grown on the semiconductor substrate
`
`
`
`
`
`
`leaving the other part of the insulating layer in grooves
`
`
`
`
`
`
`
`
`surrounding the element fabrication areas of the semi-
`
`
`
`
`
`
`
`conductor substrate, the remaining part of the insulating
`
`
`
`
`
`
`
`layer being the buried insulating layer which functions
`
`
`
`
`
`
`
`
`as an isolation region.
`
`
`
`The other object of the present invention is to pro-
`
`
`
`
`
`
`
`
`vide a method for production of a semiconductor de-
`
`
`
`
`
`vice having a plurality of elements each of which has
`
`
`
`
`
`
`
`
`satisfactory quality due to lack of damage in the element
`
`
`
`
`
`
`
`fabrication areas of the semiconductor substrate sur-
`
`
`
`
`
`
`
`rounded by buried insulating layers which function to
`
`
`
`
`
`
`isolate each element from one another, wherein an im-
`
`
`
`
`
`
`
`provement is made to simplify the steps for production
`
`
`
`
`
`
`
`of wiring.
`
`
`To achieve the foregoing first object, a method for
`
`
`
`
`
`
`
`
`production of a semiconductor device in accordance
`
`
`
`
`
`with the present invention comprises a step of growing
`
`
`
`
`
`
`
`a thermal strain absorbing layer on at least a portion of
`
`
`
`
`
`
`
`the top surface of a semiconductor substrate, the por-
`
`
`
`
`
`
`
`
`tion being an area which is not an area which becomes
`
`
`
`
`
`
`
`
`an isolation area, a step of producing at least one groove
`
`
`
`
`
`
`
`
`along said area which becomes an isolation area, a step
`
`
`
`
`
`
`
`
`of inlaying an insulator in said at least one groove, and
`
`
`
`
`
`
`
`
`a step of annealing said insulator.
`
`
`
`
`
`The concept of the present invention is to interleave
`
`
`
`
`
`
`
`a thermal strain absorbing layer between the top surface
`
`
`
`
`
`
`
`
`
`of a semiconductor substrate and an insulating layer, of
`
`
`
`
`
`
`which a part is to become a buried insulating layer, for
`
`
`
`
`
`
`
`
`the purpose of allowing the thermal strain absorbing
`
`
`
`
`
`
`
`layer to absorb strains which may otherwise occur due
`
`
`
`
`
`
`
`
`to an annealing process and to prevent damage which
`
`
`
`
`
`
`
`may otherwise be produced by irradiation of ion beams.
`
`
`
`
`
`
`FIG. 3 shows the cross-sectional view of a semicon-
`
`
`
`
`
`
`ductor device produced employing a method for pro-
`
`
`
`
`
`
`
`
`10
`
`
`
`15
`
`20
`
`
`
`25
`
`
`
`30
`
`35
`
`45
`
`
`
`
`
`50
`
`55
`
`60
`
`65
`
`
`
`Page 10 of 15
`
`Page 10 of 15
`
`
`
`4,506,434
`
`5
`
`l0
`
`15
`
`
`
`25
`
`30
`
`
`
`20
`
`5
`
`
`
`
`
`
`
`insulating layer which functions as isolation, according
`to the prior art.
`
`
`
`
`FIG. 3 is a cross-sectional view of a semiconductor
`
`
`
`
`
`
`
`
`
`device produced employing a method for production of
`a semiconductor device in accordance with the present
`
`
`
`
`
`
`
`invention.
`
`
`
`
`
`
`
`
`
`
`FIGS. 4(a), 4(b), 4(c), 4(d) and 4(2) are cross-sectional
`views of silicon (Si) substrates, each of which shows the
`
`
`
`
`
`
`
`state after the completion of each of the major steps of
`
`
`
`
`
`
`
`
`a method for production of a semiconductor device in
`
`
`
`
`
`accordance with one embodiment of the present inven-
`
`
`
`
`
`
`
`tion.
`
`FIGS. 5(a), 5(b) and S(c) are cross-sectional views of
`
`
`
`
`
`
`
`
`silicon (Si) substrates, each of which shows the state
`
`
`
`
`
`
`
`
`
`after the completion of each of the major steps of a
`
`
`
`
`
`
`
`
`
`
`method for production of a semiconductor device in
`
`
`
`
`
`
`accordance with another embodiment of the present
`
`
`
`
`
`
`invention.
`
`FIG. 6 is a cross-sectional view of a complementary
`
`
`
`
`MOS (C-MOS) semiconductor device produced em-
`
`
`
`
`
`
`ploying a method of production in accordance with a
`
`
`
`
`
`third embodiment of the present invention.
`
`
`
`
`
`FIGS. 7(a) and 7(b) are cross-sectional views, of
`
`
`
`
`
`
`
`
`which the former and the latter respectively show an
`
`
`
`
`
`
`
`
`intermediate state of and the state after the completion
`
`
`
`
`
`
`
`
`of a process for production of a 1-transistor and 1-
`
`
`
`
`
`
`
`capacitor type dynamic random access memory cell in
`
`
`
`
`
`
`
`accordance with a fourth embodiment of the present
`
`
`
`
`
`
`invention.
`
`FIGS. 8(a) and 8(b) are cross-sectional views, of
`
`
`
`
`
`
`
`
`which the former and the latter respectively show an
`
`
`
`
`
`
`
`
`intermediate state of and a state after the completion of
`
`
`
`
`
`
`
`a process for production of a bipolar type integrated
`
`
`
`
`
`
`
`
`circuit device in accordance with a fifth embodiment of
`
`
`
`
`
`
`35
`the present invention.
`
`
`
`DETAILED DESCRIPTION OF THE
`
`
`
`PREFERRED EMBODIMENTS
`
`
`In the following description, one of each embodiment
`
`
`
`
`
`
`
`in accordance with the present invention will be pres- 40
`
`
`
`
`
`
`
`
`ented, on the assumption that FET’s are produced in a
`
`
`
`
`
`
`silicon substrate, such FET’s being isolated from one
`
`
`
`
`
`
`
`
`another by buried insulating layers each of which sur-
`
`
`
`
`
`
`
`rounds each of the FET-s.
`
`
`
`
`The first embodiment is a method for production of a 45
`
`
`
`
`
`semiconductor device having a plurality of FET’s, each
`
`
`
`
`
`
`of which is fabricated in an element fabrication area of
`
`
`
`
`
`
`a silicon (Si) substrate surrounded by a buried insulating
`
`
`
`
`
`
`
`layer, wherein an improvement is realized in which a
`
`
`
`
`
`
`
`
`
`
`
`thermal strain absorbing layer of polycrystalline silicon
`(Si) is interleaved between the substrate and the insulat-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`ing layer such that the polycrystalline silicon (Si) layer
`absorbs potential strains and damage which may other-
`
`
`
`
`
`
`
`
`wise occur in the silicon (Si) substrate. This embodi-
`
`
`
`
`
`
`
`
`ment will be presented, referring to FIGS. 4(a), 4(b),
`
`
`
`
`
`
`
`
`
`4(c), 4(d) and 4(e).
`
`
`
`
`Referring to FIG. 4(a), the top surface of a silicon (Si)
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`substrate 41 is oxidized to produce a silicpn dioxide
`(SiO2) layer 42 having a thickness of 500 A, before a
`
`
`
`
`
`
`
`
`60
`
`
`
`
`
`
`polycrystalline silicon (Si) layer 43 having a thickness of
`1,000 A is grown on the silicon dioxide (SiO2) layer 42.
`
`
`
`
`
`
`
`
`The function of the silicon dioxide (SiO2) layer 42 is to
`
`
`
`
`
`
`
`
`make it easy to remove the polycrystalline silicon (Si)
`
`
`
`
`
`
`
`layer 43 in a later step. In other words, it functions to
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`solve the difficulty in removing the polycrystalline
`silicon (Si) layer 43 when it is produced directly on the
`
`
`
`
`
`
`
`
`silicon (Si) substrate 41, which is, of course, a material
`
`
`
`
`
`
`
`
`identical to the layer. The function of the polycrystal-
`
`
`
`
`
`
`
`
`
`6
`
`line silicon (Si) layer 43 is to absorb, strain and damage.
`
`
`
`
`
`
`
`
`
`Therefore, this layer 43 can be replaced by a molybde-
`
`
`
`
`
`
`num silicide (MoSi2) layer, a tungsten silicide (WSi2)
`
`
`
`
`
`
`
`layer, a titanium silicide (TiSi2) layer, a tantalum silicide
`
`
`
`
`
`
`
`(TaSi2) layer or the like, insofar as the annealing tem-
`
`
`
`
`
`
`
`
`perature range is 900° through l,l0O° C. This is because
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`these materials are stable from the chemical viewpoint
`in the foregoing temperature range and readily absorb
`
`
`
`
`
`
`
`
`strains. A photoresist layer 44 is produced on the sur-
`
`
`
`
`
`
`face of polycrystalline silicon (Si) layer 43, before a
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`patterning process is applied to the photoresist layer 44
`for the purpose of producing grooves along the area
`
`
`
`
`
`
`
`
`corresponding to the area in which a buried insulating
`
`
`
`
`
`
`layer is produced. A thickness of the layer 43 is thicker
`
`
`
`
`
`
`than 500 A for absorb.
`
`
`
`
`
`
`
`
`
`
`the patterned photoresist
`Referring to FIG. 4(b),
`layer 44 functions as a mask during a parallel plate type
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`reactive ion etching process applied to the substrate for
`
`
`
`
`
`
`
`the purpose of partly removing the polycrystalline sili-
`con (Si) layer 43, the silicon (Si) substrate 41 for the
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`ultimate purpose to produce grooves 45 having the
`depth of 6,500 A in the silicon (Si) substrate 41. A car-
`
`
`
`
`
`
`
`bon fluoride (CF4) gas containing oxygen (02) by 5% is
`
`
`
`
`
`
`
`employed as the reactive gas and an etching rate of 200
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`A/min. is realized at a pressure of 5 X 10-3 Torr. After
`the photoresist layer 44 is entirely removed, a low pres-
`
`
`
`
`
`
`
`sure chemical vapor deposition process is employed to
`
`
`
`
`
`
`
`
`
`
`
`
`
`grow a silicon dioxide (SiO2) layer 47 having a thick-
`ness of 8,000 A which entirely covers the top surface of
`
`
`
`
`
`
`
`
`the substrate 41. Thereafter, the substrate is subjected to ,
`
`
`
`
`
`
`
`an annealing process for 20 minutes in the nitrogen (N2)
`
`
`
`
`
`
`
`
`gas at a temperature of l,000° C. for the purpose of
`
`
`
`
`
`
`
`
`unifying or making uniform the density of the silicon
`
`
`
`
`
`
`
`
`
`dioxide (SiO2) layer 47. Albeit strains may occur in the
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`polycrystalline silicon (Si) layer 43 during this process,
`the entire portion of the silicon (Si) substrate 41 is main-
`
`
`
`
`
`
`
`
`tained free from strains. In other words, potential strains
`
`
`
`
`
`
`
`
`which might otherwise occur along the edges of the
`
`
`
`
`
`
`
`
`element fabrication area 46 of the silicon (Si) substrate
`
`
`
`
`
`
`
`41 surrounded by the buried insulating layer 47, are
`
`
`
`
`
`
`
`
`
`absorbed by the polycrystalline silicon (Si) layer 43.
`
`
`
`
`
`
`
`
`The top surface of the silicon dioxide (SiO2) layer 47 is
`
`
`
`
`
`
`
`coated by a photoresist layer 48 of e.g. AZl350J pro-
`
`
`
`
`
`
`duced and marketed by Shipley Company Inc. of the
`
`
`
`
`
`
`
`
`U.S.A. and the top surface of the photoresist layer 48
`
`
`
`
`
`
`
`
`becomes flat.
`
`
`Referring to FIG. 4(c), a dry etching process is ap-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`plied to the substrate until the top surface of the poly-
`crystalline silicon (Si) layer 43 is exposed. An argon
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`(Ar) gas at a pressure of 7n>< 10-4 Torr. is employed and
`an etching rate of 500 A/min.
`is realized. Although
`
`
`
`
`
`
`
`
`damage may occur in the polycrystalline silicon (Si)
`
`
`
`
`
`
`
`layer 43, during this process, the entire silicon (Si) sub-
`
`
`
`
`
`
`
`
`
`
`strate 41 is protected from damage. This means that
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`potential damages which might be otherwise be pro-
`duced along the edges of the element fabrication area 46
`
`
`
`
`
`
`
`
`of the silicon (Si) substrate 41 surrounded by the buried
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`insulating layer 47, are absorbed by the polycrystalline
`silicon (Si) layer 43.
`
`
`
`
`Referring to FIG. 4(d), a dry etching process is ap-
`
`
`
`
`
`
`
`plied to the substrate to remove only the upper portion
`
`
`
`
`
`
`
`
`of the silicon dioxide (SiO2) layer 47 by a depth corre-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`sponding to the thickness of the polycrystalline silicon
`(Si) layer 43. A trifluoromethane (CHF3) gas at a pres-
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`sure of 0.05 Torr. is employed and an etching rate of 800
`A/min. is realized.
`—
`
`
`
`Referring to FIG. 4(e), a plasma etching process em-
`
`
`
`
`
`
`ploying a carbon fluoride (CF4) gas containing 5% of
`
`
`
`
`
`
`
`
`
`
`
`50
`
`55
`
`
`
`65
`
`Page 11 of 15
`
`Page 11 of 15
`
`
`
`4,506,434
`
`
`7
`oxygen (02) at a pressure of 1 (one) Torr. is applied to
`
`
`
`
`
`
`thesubstrate to remove the polycrystalline silicon (Si)
`
`
`
`
`
`
`layer 43 at an etching rate of 500 A/min. Thereafter, a
`
`
`
`
`
`
`
`
`
`
`
`
`
`hydrogen fluoride (HF) solution is brought into contact
`with the surface of the substrate to remove the silicon
`
`
`
`
`
`
`
`
`dioxide (SiO2) layer 42 and the top portion of the silicon
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`
`dioxide (SiO2) layer 47, thereby exposing the top sur-
`face of the silicon (Si) substrate 41. As a result, a portion
`
`
`
`
`
`
`
`
`of the sili