`Patent No. 6,455,138
`
`Filed on behalf of Textron Innovations Inc.
`
`By:
`
`Patrick A. Doody (patriok.doodygchillsburylaw.com)
`Bryan P. Collins (bryan.collinnggillsburylaw.corn)
`Pillsbury Winthrop Shaw Pittman LLP
`1650 Tysons Boulevard
`McLean, VA 22102
`Tel: (703) 770—7900
`Fax: (703) 770-7901
`
`UNITED STATES PATENT AND TRADEMARK OFFICE
`
`BEFORE THE PATENT TRIAL AND APPEAL BOARD
`
`WAVELOCK ADVANCED TECHNOLOGY CO., LTD.
`Petitioner
`
`V.
`
`TEXTRON INNOVATIONS INC.
`
`Patent Owner
`
`Case IPR2013-00149
`
`Patent 6,455,138
`
`TEXTRON INNOVATIONS’ PATENT OWNER RESPONSE
`
`PURSUANT TO 37 C.F.R. §42.120
`
`
`
`TABLE OF CONTENTS
`
`Case IPR2013-00149
`
`Patent No. 6,455,138
`
`Egg
`
`Contents
`
`I.
`
`INTRODUCTION ..................................................................................................................... 1
`
`II. MATERIAL FACTS ................................................................................................................. 2
`
`III. THE ‘138 PATENT AND KUWAHARA ................................................................................ 5
`
`A. The ‘138Patent .............................. 6
`
`B. Kuwahara ............................................................................................................................. 8
`
`IV. THE BOARD SHOULD FIND THAT CLAIMS 1-3, 8, 10, 16—19, 21, 25-33, 35, AND 36
`ARE PATENTABLE IN VIEW OF WAVELOCK’S CHALLENGE ................................... 12
`
`A. Inherency Requires the Inherent Element to Necessarily Result and Cannot be Based on
`Probabilities .................................................... ,................................................................... 14
`
`B'. Wavelock Fails to Carry Its Burden in Proving the Claimed Invention is Inherently Made
`' by Kuwahara’s Examples .................................................................................................. 20
`
`1. Dr. Iezzi impermissibly assumes the copolymer resin of Kuwahara is a liquid .......... 22
`2. Even if the Copolymer Resin of Kuwahara-were a liquid, there is no evidence that the
`liquid could fill the 500 Angstrom sized voids in Kuwahara’s metallized layer ........ 24
`3. There is no evidence that Kuwahara roller coats the copolymer resin on “top” of the
`metallized layer ............................................................................................................ 27
`4. Kuwahara teaches away from the presence of a copolymer resin between the metal
`islands ................................................................................r .......................................... 30
`5. A person having ordinary skill in the art would not know whether the copolymer resin
`would flow around the island metal structures ............................................................ 32
`
`C. Having Failed to Establish that Kuwahara Inherently Anticipates Claim 1, All of the
`Proposed Grounds of Rejection Must Be Withdrawn ....................................................... 33
`
`V. CONCLUSION ....................................................................................................................... 35
`
`ii
`
`
`
`TABLE OF AUTHORITIES
`
`Case IPR2013-00149
`
`Patent No. 6,455,138
`
`Page(s)
`
`Cases
`
`Akamai Techs., Inc. v. Cable & Wireless Internet Serv., Inc ........................................................ 16
`Continental Can Co. USA v. Monsanto Co., 948 F.2d 1264, 1269 (Fed. Cir. 1991) .................... 16
`Electro Med Sys, SA. v. Cooper Life Sci, Inc., 34 F.3d 1048, 1052 (Fed. Cir. 1994) ................. 17
`Ex parte Levy, 17 USPQ2d 1461, 1464 (Ed. Pat. App. & Inter. 1990) ......................................... 16
`Finnigan Corp. v. Int’l Trade Comm’n, 180 F.3d 1354, 1366 (Fed. Cir. 1999) ............................ 17
`Glaxo, Inc. v. Novopbarm Ltd, 52 F.3d 1043, 1047-48 (Fed. Cir. 1995) ..................................... 17
`In re Oelrich, 666 F.2d 578, 581 (C.C.P.A. 1981) ........................................................................ 16
`In re Oleicb, 666 F.2d 578, 581—82(CCPA1981)............- ........................................................... 15
`In re Rijckaert, 9 F.3d 1531, 1534 (Fed. Cir. 1993) ...................................................................... 14
`In re Robertson, 169 F.3d 743, 745 (Fed. Cir. 1999) .................................................................... 15
`MEHL/Biopnile, 192 F.3d at 1365 ................................................................................................. 17
`Metabolite Labs, Inc. v. Lab. Corp. ofAm. Holdings, 370 F.3d 1354, 1367 (Fed. Cir. 2004) ..... 15
`Rosco Inc. v. Mirror Lite C0.,304 F.3d 1373, 1379~81 (Fed. Cir. 2002) ...................................... 18
`Rosco, 304 F.3d at 1380—81 ........................................................................................................... 19
`Scaltech, Inc. v. Retec/Tetra, L.L.C., 178 F.3d 1378, 1384 (Fed. Cir. 1999) ................................ 16
`Teleflex, Inc. v. FicosaN. Am. Corp, 299 F.3d 1313, 1335 (Fed. Cir. 2002) ............................... 18
`Telemac Cellular Corp. v. Topp Telecom, Inc., 247 F.3d 1316, 1328 (Fed. Cir. 2001) ............... 18
`Transclean Corp. v. Bridgewood Servs., Inc., 290 F.3d 1364, 1373 (Fed. Cir. 2002) .................. 16
`Trintec Indus, Inc. v. Top—USA. Corp, 295 F.3d 1292, 1297 (Fed. Cir. 2002) .......................... 17
`
`Rules and Regulations
`37 C.F.R. §42120 ................................................................................................ 1
`37 C.F.R. §42.23 .............................................................................................................................. 2
`
`
`
`Case IPR20l3—00149
`
`Patent No. 6,455,138
`
`I.
`
`INTRODUCTION
`
`Pursuant to 37 CPR. §42. 120, Patent Owner Textron Innovations Inc.
`
`(“TeXtron”) submits this Patent Owner Response (“Response”) in reply to the
`
`Decision to Institute Inter Partes Review dated August 1, 2013 (“Decision”) of
`
`Murano, US. Patent No. 6,455,138 (the “’ 138 patent”). Textron also submits this
`
`Response to the Petition for Inter Partes Review filed February 15, 2013,
`
`(“Petition”) to the extent the Patent Trial and Appeal Board (PTAB) relied on the
`
`Petition in rendering its decision to institute.
`
`The Petitioner, Wavelock Advanced Technology Co., Ltd. (“Wavelock”) has
`
`failed to carry its burden in proving that the only document relied upon to reject the
`
`sole independent claim, Kuwahara, JP 63—286337 (“Kuwahara”) inherently
`
`' anticipates the claims. Specifically, Wavelock has failed to prove that Kuwahara-
`
`necessarily produces a discontinuous layer including discrete islands of metal in an
`
`adhesive. The entire basis for Wavelock’s position is premised on one sentence in
`
`Kuwahara, and one sentence in each of paragraphs 39 and 57 of Dr. Robert Iezzi’s
`
`declaration (the “Declaration”). Wavelock has not produced any evidence other
`
`than unsupported opinion testimony, which is legally insufficient to carry its
`
`burden in proving that the prior art necessarily will produce the claimed invention.
`
`In addition, Dr. Iezii is forced to make assumptions regarding Kuwahara’s
`
`disclosure in rendering his conclusion that islands of Sn deposited in Kuwahara are
`
`
`
`. IPR2013-00149
`Patent No. 6,455,138
`
`,“in the adhesive.” Wavelock Exhibit 1017, 157, pg. 26. Assumptions regarding
`
`the prior art disclosure are wholly inadequate to establish inherent anticipation,
`
`which requires the alleged inherent claim limitation to be the necessary result of
`
`the prior art. A mere probability (which must result when assumptions are made)
`
`precludes inherency as a matter of law. Accordingly, the rejections of allof the
`
`claims at issue in this proceeding based on Kuwahara are legally erroneous.
`
`II. MATERIAL FACTS
`
`Petitioner did not include a statement of material facts. Textron presents the
`
`following material facts pursuant to 37 C.F.R. '§42.231:
`
`l. The ‘138 patent claims all require the presence of a discontinuous
`
`layer including discrete islands of metal in an adhesive (Wavelock
`
`Exhibit 1001, pg. 9);
`
`2. Some of the problems the ‘ 138 patent seeks to minimize or overcome
`
`are delamination of metallized polymer composite, corrosion of the
`
`metal layer, and popping that can occur when solvents are used and
`
`then evaporated during processing of the composite (Id at pg. 5);
`
`1The list is by no means exhaustive, and more material facts may be established
`during this proceeding. The list presented in Patent Owner’s response is merely
`illustrative of the important material facts for the particular issues discussed
`herein.
`
`
`
`IPR2013—00149
`
`Patent No. 6,455,138
`
`3. Kuwahara, JP Laid-Open Application 63-286337 published
`
`November 24, 1988 (“Kuwahara” ~— Wavelock Exhibit 1006 and 1007
`
`(English translation»2 discloses ornamental molded articles useful for
`
`the outer casing of electronic appliances such as television sets and
`
`VTRs, in which the molded articles include a metallized layer formed
`
`in discrete islands that are separated from one another to have
`
`insulating properties and not cause electrical shocks (Wavelock
`
`Exhibit 1007, pg. 2);
`
`4. Kuwahara makes use of low melting point metals such as Sn, Pb, Zn,
`
`Bi, and the like (Id at pg. 4), where the melting point of tin is 232°C
`
`and the melting point of indium is 157°C (Declaration of Dr. Iezzi,
`
`Wavelock Exhibit 1017 at 1182, pg. 38);
`
`5. Kuwahara discloses in Examples 1 and 2 that the distance between the
`
`metal islands is 500 Angstroms (Wavelock Exhibit 1007, at pg. 5);
`
`6. 500 Angstroms is an order of magnitude smaller than the resolution of
`
`a light microscope, as shown in “A Cellular World, PH709 The
`
`Biology of Public Health, printed from http://sph.bu.edu/otlt/MPH—
`
`2 Citations to Kuwahara are citations to the English translation found in Wavelock
`‘ Exhibit 1007.
`
`
`
`IPR2013-00149
`
`Patent No. 6,455,138
`
`Modules/P'H/P'H709 A Cellular_World/PH709 A Cellular World printhtml —
`
`(Textron Exhibit 1001 at pg. 19);
`
`7. Kuwahara disclosesZ:
`
`In example 1 and example 2, a deposited Sn layer was provided in an
`island structure shown below on one surface of a 12 um thick
`
`elongated piece of a polyethylene terephthalate film by performing
`
`vacuum deposition under evaporation conditions shown below with a
`
`semi—continuous vacuum deposition apparatus; a vinyl chloride-vinyl
`
`acetate copolymer resin was applied to the deposited Sn layer of the
`examples to a thickness of 2 um with a roller coater, then heated with
`
`a 200 um thick polyvinylchloride film and laminated under pressure.
`
`The thus obtained products were slit to 10mm width, and the slit
`
`products, with the polyvinylchloride film inwards and the
`
`polyethylene terephthalate film outwards, were adhered to a
`
`polyvinylchloride resin while being molded, so as to obtain molded
`
`I articles having metal luster and insulating properties.
`
`Wavelock Exhibit 1007 at pg. 5.
`
`8. Dr. Iezzi states that the vinyl chloride-vinyl acetate copolymer resin
`
`used in Kuwahara’s examples is an adhesive, and that since “the
`
`adhesive is applied on top of the discontinuous metal layer in a liquid
`
`state, the adhesive would inherently flow around the island metal
`
`structures so that islands of metal would be in the adhesive.”
`
`(Wavelock Exhibit 17 at 1139, pg. 17, emphasis added).
`
`
`
`IPR2013-00149
`
`Patent No. 6,455,138
`
`9. Dr. Iezzi further states that “[v]inyl chloride-vinyl acetate copolymer
`
`resin was a common adhesive used to adhere a metallized film to a
`
`vinyl chloride film and other plastic films.” Id at 1157, pg. 26;
`
`10.Dr.-‘Iezzi concludes that “[o]ne of ordinary skill in the art would have
`
`also understood that since the adhesive (vinyl chloride—vinyl acetate
`
`copolymer resin) is applied by a coater to the Sn islands deposited on
`
`the PET film, the Sn islands are in the adhesive.” Id at 1157, pg. 27;
`
`1 1.Even if Dr. Iezzi’s assumption were accurate that the vinyl chloride-
`
`vinyl acetate copolymer resin of Kuwahara is a liquid, there is no
`
`evidence or proof (and the documents of record suggest the opposite)
`
`that this liquid would necessarily fill the spaces between the metal .
`
`islands, especially when Kuwahara provides no characteristics of the
`
`resin (e.g., monomer percentages, molecular weight, viscosity, etc).
`
`III.
`
`THE ‘138 PATENT AND KUWAHARA
`
`Patent Owner presents a brief summary of the ‘138 patent and the only prior .
`
`art cited in the Decision (Kuwahara) as disclosing the features of the only
`
`independent claim of the ‘138 patent. The differences between the ‘138 patent and
`
`Kuwahara will reveal why the allegations, assumptions, and conclusions advanced
`
`by Petitioner Wavelock fail to prove, as a matter of necessity, that Kuwahara
`
`inherently discloses all of the features of the ‘ 138 patent claims.
`
`
`
`IPR2013-00149
`
`Patent No. 6,455,138
`
`A.
`
`The ‘138 Patent
`
`The ‘138 patent discloses a metallized composite comprising a first
`
`thermoplastic layer, a discontinuous intermediate layer comprising discrete islands
`
`of metal in an adhesive, and a second thermoplastic layer. Wavelock Exhibit 1001,
`
`' pg. 1. Figure 1 illustrates an embodiment of such a metallized composite.
`
`IO
`
`\'8
`
`
`
`Wavelock Exhibit 1001, pg. 2. The ‘138 patent describes this embodiment as
`
`follows:
`
`In one embodiment, shown in FIG. 1, metallized composite 10
`
`includes first thermoplastic layer 12. Discontinuous layer 14 is on first
`
`thermoplastic layer 12 and includes first side 16 and second side 18.
`
`- Discontinuous layer includes discrete islands of metal 20 and adhesive
`
`22. Second thermoplastic layer 24 is on discontinuous layer 14,
`
`
`
`IPR2013—00149
`
`. Patent No. 6,455,138
`
`whereby discontinuous layer 14 is between the first and second
`
`thermoplastic layers.
`
`Wavelock Exhibit 1001, pg. 6, col. 4, 11. 1-8.
`
`Some of the problems the ‘138 patent seeks to minimize or overcome are
`
`delamination of metallized composite, corrosion of the metal layer, and popping
`
`that can occur when solvents are used and then evaporated during processing of the
`
`composite material (Id at pg. 5, col. 1, 11. 10-63). Thus, the metallized composite
`
`includes discrete islands of metal in an adhesive to prevent and/or minimize
`
`corrosion of the metal layer, and to preventand/or minimize delamination between
`
`the metal layer and the thermoplastic layers on either side (10’).
`
`Claim 1 of the ‘138 patent, the only independent claim, recites:
`
`l. A metallized composite, comprising:
`
`a) a first thermoplastic layer;
`
`b) a discontinuous layer on said first layer, said discontinuous layer
`
`including discrete islands of metal in an adhesive; and
`
`c) a second thermoplastic layer, said discontinuous layer being
`
`between said first and second thermoplastic layers.
`
`Wavelock Exhibit 1001, pg. 9.
`
`
`
`IPR2013—00149
`
`Patent No. 6,455,138
`
`B.
`
`Kuwahara
`
`Kuwahara discloses ornamental molded articles useful for the outer casing
`
`of electronic appliances such as television sets and VTRs, in which the molded
`
`articles include a metallized layer formed in discrete islands that are separated
`
`from one another so that they have insulating properties and do not cause electrical
`
`shocks (Wavelock Exhibit 1007, pg. 2). The purpose of Kuwahara’s film is to
`
`prevent shocks when used on electronic appliances, and consequently, Kuwahara
`
`avoids any potential contact between adjacent metal islands. Id at pg. 4.
`
`Kuwahara discloses that if the distance between the islands is less than 100 A, then
`
`a tunneling current flows so that the insulating characteristic degrades. Id.
`
`Kuwahara makes use of low melting point metals such as Sn, Pb, Zn, Bi, and
`
`the like (Id at pg; 4), where the melting point of tin is 23 2°C and the melting point
`
`of indium is 157°C (Declaration of Dr. Iezzi, Wavelock Exhibit 1017 at 1182, pg.
`
`38). Kuwahara discloses in Examples 1 and 2 the distance between the metal
`
`islands as 500 Angstroms (Wavelock Exhibit 1007 at pg. 5). 500 Angstroms is
`
`extremely small, and would not even be visible under a conventional light
`
`microscope, as shown and described in “A Cellular World, PH709 The Biology of
`
`Public Health, printed from http://sph.bu.edu/otlt/MPl-.I~
`
`
`Modules/PH/PH709_A Cellular World/PH709 A CellulariWorld_prillt.htm_l — (Textron Exhibit
`
`1002 at pg. 19). A figure from page 19 of this document is reproduced below:
`
`
`
`IPR2013—00149
`
`Patent No. 6,455,138
`
`353513351 BLIES
`
`warms
`
`Mafia).
`MQL EC l 1 ES
`
`MGLECFLES
`
`arrays
`
`fig;
`39'“
`
`isaazaghbll
`
`maximum at
`mm m Harman
`
`mamas
`
`gflIfiw .
`flitWTIfifi'
`:93“qu
`{3?
`
`
`
`Egg
`
`tail
`
`tag-.8.
`
`W93.
`
`WA
`
`ram
`
`To appreciate how small 500 Angstroms is, one would have to carve up a
`
`one millimeter segment into 20,000 equally-spaced segments, and just one of those
`
`segments represents 500 Angstroms. The following hyphen is about one
`
`millimeter long ( - ), which. means 500 Angstroms would be l/20,000th the size of
`
`the hyphen. The figure above shows that macro-molecules like polymers, are
`
`hundreds of Angstroms in size, which likely depends on the molecular weight and
`
`number of repeating units. It is highly likely, and at the very least possible, that the
`
`
`
`IPR2013—00149
`
`Patent No. 6,455,13 8
`
`copolymer resin used by Kuwahara is larger than the 500 Angstrom space between
`
`the metal islands and would not fit in the space unless modified.3
`
`Kuwahara’s example discloses, in examples 1 and 2:
`
`In example 1 and example 2, a deposited Sn layer was provided in an
`
`island structure shown below on One surface of a 12 um thick
`
`elongated piece of a polyethylene terephthalate film by performing
`
`vacuum deposition under evaporation conditions shown below with a
`
`semi-continuous vacuum deposition apparatus; a vinyl chloride—vinyl
`
`acetate copolymer resin was applied to the deposited Sn layer of the
`
`examples to a thickness of 2 um with a roller coater, then heated with
`
`a 200 um thick polyvinylchloride film and laminated under pressure.
`The thus obtained products were slit to 10mm width, and the slit
`
`products, with the polyvinylchloride film inwards and the
`polyethylene terephthalate film outwards, were adhered to a
`
`polyvinylchloride resin while being molded, so as to obtain molded
`
`articles having metal luster and insulating properties.
`
`Wavelock Exhibit 1007 at pg. 5. The most likely result from carrying out this
`
`example is not the illustration provided in Dr. Iezzi’s Declaration and relied upon
`
`in the Decision, but rather the film would have the following structure.
`
`3 One will never know the true answer, however, because Kuwahara does not
`disclose the molecular weight of the copolymer resin, and Wavelock has
`provided no evidence that the copolymer resin could fit in such a small space.
`
`10
`
`
`
`IPR2013—00149
`
`Patent No 6 ,455,138
`
`
`H“
`2pm W/
`
`
`Copolymer
`
`Sn islands
`
`0.4 pm
`
`
`
`Ri\\\\\\\
`\\\\\\\\\\\\\\\\\ } pET
`12pm
`
`Sn islands 500 A
`
`It is possible to interpret Kuwahara’s example as disclosing roll coating the
`
`copolymer resin in a highly viscous State in which the resin is applied “to” the
`
`upper surface of the metallized layer while the layer is upside down, which is
`
`conventional in roll coating (see illustration below) 4:
`
`
`
`The metallized layer of Kuwahara
`would be on the bottom and the
`
`resin would be applied to the
`bottom of the layer.
`
`
`
`Kuwahara then discloses heating the film, apparently to cure or set the adhesive
`
`and if an solvent were used,5 to eva orate the solvent, and laminatin the film
`y
`P
`g
`
`4 See Textron Exhibit 1002, “About Roll Coaters,” excerpted from the Schaefer
`Company website: htt
`://www.schaeferco.com/about rollcoatershtml.
`
`
`
`5 Kuwahara does not disclose applying the copolymer resin dissolved in a solvent.
`Rather, this would have to be an assumption made based on Kuwahara’s
`disclosure.
`It is equally plausible that the copolymer resin is a solid, and is
`
`11
`
`
`
`IPR201 3-00149
`
`Patent No. 6,455,138
`
`with a 200 um thick PVC film. Kuwahara again does not disclose the temperature
`
`at which the materials are heated, or the lamination pressure.
`
`Even if a low viscosity Solution of the copolymer resin were applied to the
`
`surface of Kuwahara’s metal islands, and even if they were applied on top of the
`
`metal islands, very little if any could possibly fill in the 500 Angstrom sized
`
`spaces. If Kuwahara’s metal islands were coated with a highly viscous copolymer
`
`resin using conventional roller coating configurations (e. g., with the surface to be
`
`coated upside downrso that the “bottom” would be coated), it is even more unlikely
`
`that any of the resin would fill the 500 Angstrom—sized spaces between the metal
`
`islands. Wavelock therefore has failed to carry its burden in proving that
`
`Kuwahara’s examples would necessarily (i.e., without any probability) produce the
`
`claimed film.
`
`IV. THE BOARD SHOULD FIND THAT CLAIMS 1-3, 8, 10, 16-19, 21, 25-
`33, 35, AND 36 ARE PATENTABLE IN VIEW OF WAVELOCK’S
`CHALLENGE
`
`The only prior art cited against claim 1 in the Decision is Kuwahara, and the
`
`Decision alleges that the examples of Kuwahara inherently produce the claimed
`
`discontinuous layer. The only evidence to support this allegation is unsupported
`
`coated as a solid, or is heated and coated as a highly viscous 100% solid resin
`film.
`
`12
`
`
`
`IPR2013-00149
`
`Patent No. 6,455,138
`
`opinion testimony by Dr. Iezzi that is premised on assumptions that are not
`
`necessarily consistent with Kuwahara’s disclosure. Wavelock has not provided
`
`any other evidence to support inherency - a doctrine that requires the inherent
`
`element (in this case, the formation of a discontinuous layer) to necessarily occur,
`
`where possibilities, assumptions, and probabilities are inadequate.
`
`The entire basis upon which Wavelock’s anticipation rejection is premised
`
`stems from one sentence in Kuwahara, and one sentence in Dr. Iezzi’s declaration.
`
`The sentence of Kuwahara states “a vinyl chloride—Vinyl acetate copolymer resin
`
`was applied to the deposited Sn layer of the examples to a thickness of 2 mm with a
`roller coater, then heated with a 200 um thick polyvinylchloride film and laminated
`
`under pressure.” Dr. Iezzi stretches this disclosure and assumes that the copolymer
`
`resin first is a liquid, then that the liquid was applied to the top of the layer
`
`(insinuating a configuration in which the resin is vertically on top of the metallized
`
`layer), and then that the liquid would inherently flow around the island metal
`
`structures so that islands of metal would be in the adhesive. No other evidence
`
`exists.
`
`The evidence is inadequate to establish inherency, especially when it is
`
`premised on assumptions and a belief as to what might result. Inherency requires
`
`necessity —~ probabilities are insufficient. The most reasonable interpretation of
`
`13
`
`
`
`IPR2013—00149
`
`Patent No. 6,455,138
`
`Kuwahara is that no resin (or very little if any) would flow around the island metal
`
`structures since roller coating typically applies a highly viscous adhesive to an
`
`upside down film, which then is heated to form a thin film of adhesive. Rather,
`certain conditions would have to exist for even some small portion ofthe resin to
`
`flow around the metal islands — conditions that are neither disclosed nor suggested
`
`in Kuwahara. Even if a person having ordinary skill in the art “could” modify the
`
`coating and laminating conditions to force some resin into the 500 Angstrom
`
`spaces between the metal islands, there is no evidence of record to establish what
`
`those conditions might be, nor does Kuwahara disclose any reason to do so. In
`
`' fact, Kuwahara requires no contact between the metal islands, and the presence of
`
`a-material between each metal island might permit tunneling current flow, which
`
`Kuwahara expressly avoids (Wavelock Exhibit 1007, pg. 4).6
`
`A.
`
`Inherency Requires the Inherent Element to Necessarily Result
`and Cannot be Based on Probabilities
`
`The fact that a certain result or characteristic may occur or be present in the
`
`prior art is not sufficient to establish the inherency of that result or characteristic.
`
`In re Rijckaert,9 F.3d 1531, 1534 (Fed. Cir. 1993) (reversed rejection because
`
`6 This is especially true if a solvent were used to dissolve the resin, since residual
`solvent would remain in the spaces. As is the case with most solvents like water
`and alcohols, that solvent would likely permit electricity to flow between the
`metal islands. This would completely destroy the entire purpose of Kuwahara.
`
`14
`
`
`
`IPR2013—00149
`
`Patent No. 6,455,138
`
`inherency was based on what would result due to optimization of conditions, not
`
`what was necessarily present in the prior art); In re OeIrz'ch, 666 F.2d 578, 581-82
`
`(CCPA 1981). “To establish inherency, the extrinsic evidence ‘must make clear
`
`that the missing descriptive matter is necessarily present in the thing described in
`
`the reference, and that it would be so recognized by persons of ordinary skill.
`
`Inherency, however, may not be established by probabilities or possibilities. The
`
`mere fact that a certain thing may result from a given set of circumstances is not
`
`sufficient.’ ”In re Robertson, 169 F.3d 743, 745 (Fed. Cir. 1999) (citations omitted)
`
`(The claims were drawn to a disposable diaper having three fastening elements.
`
`The reference disclosed two fastening elements that could perform the same
`
`function as the three fastening elements in the claims. The court construed the
`
`claims to require three separate elements and held that the reference did not
`
`disclose a separate third fastening element, either expressly or inherently).
`
`Moreover, “[a]n invitation to investigate is not an inherent disclosure” where a
`
`prior art reference “discloses no more than a broad genus of potential applications
`
`of its discoveries.” Metabolite Labs, Inc. v. Lab. Corp. ofAm. Holdings, 370 F.3d
`
`1354, 1367 (Fed. Cir. 2004).
`
`“In relying upon the theory of inherency, the examiner must provide a basis
`
`in fact and/or technical reasoning to reasonably support the determination that the
`
`allegedly inherent characteristic necessarily flows from the teachings of the applied
`
`15
`
`
`
`prior art.” Ex parte Levy, 17 USPQ2d 1461, 1464 (Ed. Pat. App. & Inter. 1990).
`
`The Federal Circuit explained the standard for determining inherency as follows:
`
`IPR2013-00149
`
`Patent No. 6,455,138
`
`Inherency, however, may not be established by probabilities or
`possibilities. The mere fact that a certain thing may result from a
`given set of circumstances is not sufficient. If, however, the disclosure
`is sufficient to show that the natural result flowing from the operation
`as taught would result in the performance of the questioned function,
`it seems to be well settled that the disclosure should be regarded as
`sufficient.
`
`Continental Can Co. USA v. Monsanto Co., 948 F.2d 1264, 1269 (Fed. Cir. 1991)
`
`(quoting In re Oelrich, 666 F.2d 578, 581 (C.C.P.A. 1981); accord Akamai Techs,
`
`Inc. v. Cable & Wireless Internet Serv, Inc., 344 F.3d 1186, 1192 (Fed. Cir. 2003)
`
`("A claim limitation is inherent in the prior art if it is necessarily present in the
`
`prior art, not merely probably or possibly present"); Transclean Corp. v.
`
`.Bridgewooa’ Servs., Inc, 290 F.3d 1364, 1373 (Fed. Cir. 2002) ("Because
`
`anticipation by inherent disclosure is appropriate only when the reference discloses
`
`prior art that must necessarily include the unstated limitation, the Japanese patent
`
`cannot inherently anticipate the claims of the '080 patent") (emphasis in original);
`
`Scaltecli, Inc. v. Retec/Tetra, L.L.C., 178 F.3d 1378, 1384 (Fed. Cir. 1999)
`
`("Inherency may not be established by probabilities or possibilities. The mere fact
`
`that a certain thing may result from a given set of circumstances is not sufficient to
`
`. establish inherency. However, if the natural result flowing from the operation of
`
`the process offered for sale would necessarily result in achievement of each of the
`
`16
`
`
`
`IPR2013—00149
`
`Patent No. 6,455,138
`
`claim limitations, the claimed invention was offered for sale"), appeal after
`
`remand, 269 F.3d 1321, 1330-31 (Fed. Cir. 2001); Finnigan Corp. v. Int’l Trade
`
`Comm ’n, 180 F.3d 1354, 1366 (Fed. Cir. 1999) (reversing finding of anticipation .
`
`because testimony demonstrated that it was only a possibility that claimed
`
`nonresonance ejection was disclosed in reference and stating "The mere possibility
`
`that Figure 2 might be understood by one of skill in the art to disclose
`
`nonresonance ejection is insufficient to show'that it is inherently disclosed
`
`therein").
`
`Thus, "[o]ccasional results are not inherent-""37 A challenger can use
`
`evidence extrinsic to the prior—art reference to show that the missing item is
`
`7 MEHL/Biophz'le, 192 F.3d at 1365; accord Trintec Indus, Inc. v. Top-USA.
`Corp., 295 F.3d 1292, 1297 (Fed. Cir, 2002) (vacating summary judgment of
`anticipation by inherency since record evidence did not show prior art inherently
`"created" the image in a computer, as required by the claim, but may have
`"created“ the image manually and then provided it to the computer for further
`processing, and stating "It is irrelevant that a skilled artisan might possibly use the
`computer to create the final desired image from the'color separations. Inherency
`does not embrace probabilities or possibilities"); Glaxo, Inc. v. Novoplzarm Ltd,
`52 F.3d 1043, 1047—48 (Fed. Cir. 1995) (stating that claimed invention was not
`anticipated by inherency in example of reference where it was shown that the
`allegedly inherent compound was not produced every time when following the
`teachings of the reference even though validity challenger‘s expert performed prior
`art example thirteen times and obtained claimed material); Electra Med. Sys, SA.
`v. Cooper Life Sci, Inc, 34 F.3d 1048, 1052 (Fed. Cir. 1994) ("The mere fact that
`a certain thing may result from a given set of circumstances is insufficient to prove
`anticipation").
`
`17
`
`
`
`lPR2013-00149
`
`Patent No. 6,455,138
`
`necessarily present.8 The challenger may not, however, use extrinsic evidence to
`
`supply missing material that is not inherent from the information expressly
`
`disclosed.9 For example, in Rosco Inc. 12. Mirror Lite C0,,304 F.3d 1373, 1379-81
`
`(Fed. Cir. 2002) the challenger argued that its design patent on a mirror inherently
`
`anticipated a utility patent on a mirror that required a varying radius of curvature.
`
`The challenger argued that if it made its mirror in the shape. shown in the design
`
`patent and used a certain thermoforming process to make the mirror, a varying
`
`radius of curvature would inevitably result. The design patent, however, provided 4
`
`no disclosure of any process to make the mirror, and the thermoforming process
`
`was not the only way to make the mirror. Hence, it was not inevitable that one of
`
`skill in the art would use the thermoforming process to make the mirror. On this
`
`basis, the Federal Circuit reversed a district court's finding of anticipation by
`
`inherency because the disclosure in the design patent did not ShOW that a mirror
`
`with the required radius of curvature would necessarily result from using the
`
`8 Telemac Cellular Corp. v. Topp Telecom, Inc., 247 F.3d 1316, 1328 (Fed. Cir.
`2001) ("[R]ecourse to extrinsic evidence is proper to determine whether a feature,
`while not explicitly discussed, is necessarily present in a reference. The evidence
`must make clear that the missing feature is necessarily present, and that it would be
`' so recognized by persons of skill in the relevant art").
`9 Teleflex, Inc. v. Ficosa N. Am. Corp, 299 F.3d 1313, 1335 (Fed. Cir. 2002) ("As
`we have repeatedly stated, anticipation requires that each limitation of a claim must
`be found in a single reference. Although we have permitted the use .of additional
`references to confirm the contents of the allegedly anticipating reference, we have
`made clear that anticipation does not permit an additional reference to supply a
`missing claim limitation").
`
`18
`
`
`
`IPR2013-00149
`
`Patent No. 6,455,138
`
`disclosure ofjust the design patent.10 Accordingly, While the doctrine of inherency
`
`permits accounting for a prior—art reference's implicit disclosures in an anticipation
`
`analysis, it does not permit filling in missing elements just because one of skill in
`
`the art might know of the missing material from some other source.
`
`The Finnigan and Rosco cases are relevant to the facts of the present case,
`
`although both Finnigcm and Rosco presented closer examples of inherency than the
`
`present evidence. At least in Finnigan and Rosco, the evidence supported a
`
`possibility. No such evidence exists here. Rather, the only evidence is
`
`unsupported opinion testimony that is premised on assumptions that the resin is a
`
`liquid, that it was applied on top of the layer (suggesting a vertical configuration),
`
`I
`
`and the bare allegation that the “adhesive would inherently flow around the island
`
`metal structures.” Wavelock Exhibit 101